Fragrance self-restoration extrusion stage PP (polypropylene) composite material and preparation method thereof

A composite material and polypropylene technology, which is applied in the field of self-healing extrusion-grade polypropylene composite materials, can solve problems such as burnt smell of extrusion-grade polypropylene materials, and achieve the effect of improving the acceptability and reducing the amount of addition.

Pending Publication Date: 2017-05-17
CHONGQNG PRET NEW MATERIAL +4
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a scented, self-healing polypropylene composite ma

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fragrance self-restoration extrusion stage PP (polypropylene) composite material and preparation method thereof
  • Fragrance self-restoration extrusion stage PP (polypropylene) composite material and preparation method thereof
  • Fragrance self-restoration extrusion stage PP (polypropylene) composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～ Embodiment 5

[0027] Weigh the components shown in Table 1 by weight percentage: polypropylene, elastomer, talcum powder, fluoropolymer composition, antioxidant, jasmine flavoring agent. The polypropylene, elastomer, and fluoropolymer compositions were first mixed in a high mixer for 3 minutes, then added with talcum powder, jasmine flavoring agent, and antioxidant, and mixed for another 2 minutes, and the speed of the high mixer was 1500 rpm The premix was melted and extruded by a twin-screw extruder, and vacuum granulated to obtain a flavor-type, self-repairing extrusion-grade polypropylene composite material. The specific data are listed in Table 1.

Embodiment 6

[0029] Weigh the components shown in Table 1 by weight percentage: polypropylene, elastomer, talcum powder, fluoropolymer combination

Embodiment 7

[0031] Take the components shown in Table 1 by weight percentage: polypropylene, elastomer, talcum powder, fluoropolymer composition, antioxidant, sweet-scented osmanthus flavor flavoring agent, preparation method is the same as embodiment 1, performance test data is listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fragrance self-restoration extrusion stage PP (polypropylene) composite material and a preparation method thereof. The fragrance self-restoration extrusion stage PP composite material is prepared from the following ingredients in percentage by weight: 43 to 96.9 percent of PP, 2 to 20 percent of elastomers, 0 to 30 percent of talcum powder, 1 to 5 percent of fluoropolymer compositions, 0.001 to 0.005 percent of flavouring agents and 0.1 to 2 percent of antioxidants. The fragrance self-restoration extrusion stage polypropylene composite material has the advantages that in the extrusion molding process of the extrusion stage PP, flux is extruded at a high speed, and receives the high-temperature shearing friction effect of an opening mold, so that the degradation of the PP material can be intensified, so that the emission performance of smell and the like of the product becomes worse; few fragrance agents are added, and are non-toxic and harmless, so that no loss is caused on the original mechanical property of the material and the emission performance such as smell, condensing and VOC; the fragrance can shield the unpleasant smell of plastic smell, charring smell and the like of the high polymer material per se and the material high-temperature degradation; the pleasant fragrance is given out, so that the product acceptability is improved.

Description

technical field [0001] The invention relates to a self-repairing extrusion-grade polypropylene composite material, especially a scented, self-repairing extrusion-grade polypropylene composite material; the invention also provides a scented, self-repairing extrusion grade polypropylene composite material; Preparation method of grade polypropylene composite material. Background technique [0002] Polypropylene hydrocarbon materials are the most widely used materials for interior and exterior parts of automobiles, especially polypropylene materials, which have high strength and good comprehensive performance. With the development of the automobile industry, the amount of polypropylene used in automobiles has grown rapidly in the past few years. Especially in recent years, major OEMs have increasingly stringent requirements on the emission performance of automotive interior materials, among which the smell is particularly prominent, and the smell is the most intuitive and the mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L53/00C08L23/08C08L27/18C08K13/02C08K3/34C08K5/372C08K5/00B29C47/92B29C48/92
CPCC08L53/00B29C48/92B29C2948/92514B29C2948/92704C08K2201/003C08L2205/035C08L23/0815C08L27/18C08K13/02C08K3/34C08K5/372C08K5/00
Inventor 徐美玲蔡青张鹰张祥福周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap