A technology of interpenetrating network and polymer, which is applied in the field of preparation of organic amphoteric copolymerized polymer interpenetrating network gel, which can solve the problems of low stability of interpenetrating network gel, carcinogenesis of monomer acrylamide, and the influence of gel toxicity , achieving good environmental and economic benefits, simple preparation method, and improved stability

Inactive Publication Date: 2017-05-31
SICHUAN NORMAL UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the main problem in the preparation method of organic amphoteric copolymerized polymer interpenetrating network gel is that the monomer acrylamide is a highly toxic drug that is "carcinogenic, distorting, and mutagenic", and the cross-linking agent N, N methylenebisacrylamide The toxicity is high, and there is an adverse toxic effect on the gel; the stability of the interpenetrating network gel formed by a single cross-linking agent is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Example 1: 124.5g methacryloyloxyethyltrimethylammonium chloride, 110.5g methacrylateoxyethyl trimellitic anhydride, 90.1g caffeic acid and 758.5ml deionized water were added to a sealable reaction with a volume of 2L Stir and mix evenly in the container, the weight concentration of the aqueous solution is 30%; vacuumize to a relative vacuum of -0.03MPa, then feed nitrogen to restore the reactor to normal pressure, add 9.8g of dimethacrylic acid with a number average molecular weight of 3000 An aqueous solution prepared from polyethylene glycol ester and 36.7ml of deionized water, the weight concentration of the aqueous solution is 21%; then the temperature is raised to 37°C, and 1.25g of potassium persulfate, 0.38g of sodium bisulfite and 27.9ml of deionized water are added to prepare The aqueous solution, the weight concentration of the aqueous solution is 5.5%, at a constant temperature of 37 ° C, the pH value is controlled to 4.5, and the stirring reaction is continu...

Embodiment 2

[0009]Example 2: 228.3g of methacryloyloxyethyltrimethylammonium chloride, 414.4g of methacrylateoxyethyl trimellitic anhydride, 180.2g of caffeic acid and 548.5ml of deionized water are added to a volume of 1.5L to seal the reaction Stir and mix evenly in the container, the weight concentration of the aqueous solution is 60%; evacuate to a relative vacuum of -0.07MPa, then feed nitrogen to restore the reactor to normal pressure, add 82.3g of dimethacrylic acid with a number average molecular weight of 19000 An aqueous solution prepared from polyethylene glycol ester and 128.7ml of deionized water, the weight concentration of the aqueous solution is 39%; then the temperature is raised to 48°C, and 6.17g of potassium persulfate, 6.17g of sodium bisulfite and 72.8ml of deionized water are added to prepare The aqueous solution, the weight concentration of the aqueous solution is 14.5%, at a constant temperature of 48 ° C, the pH value is controlled at 9.5, and the stirring reactio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of organic amphoteric copolymerized macromolecular interpenetrating network gel. According to the method, methacryloyloxyethyl trimethyl ammonium chloride, trimellitic anhydride oxyethyl methacrylate and caffeic acid are used as comonomers; polyethylene glycol dimethacrylate is used as a cross-linking agent; potassium persulfate-sodium hydrogen sulfite is used as an initiator; a copolymerization reaction is carried out in deionized water to obtain organic amphoteric copolymerized macromolecular first network gel; the first network gel is swelled in an aqueous solution confected by sorbic acid, D-mannose, trimellitic anhydride oxypropyl methacrylate, ethylene glycol dimethacrylate and deionized water; monomers and a cross-linking agent in the aqueous solution generate copolymerization and esterification reactions under the action of potassium persulfate and pyridoxol hydrochloride; the organic amphoteric copolymerized macromolecular interpenetrating network gel is finally obtained.

Description

technical field [0001] The invention relates to a preparation method of an organic amphoteric copolymer interpenetrating network gel. Background technique [0002] Gel is a special dispersion system. Polymer molecules or colloidal particles are connected to form a three-dimensional space network structure, which can absorb a large amount of water swelling and is insoluble in water. It can maintain a certain shape in water and has both solid and liquid properties. nature. Macroscopically, polymer gel has a certain shape, which will be deformed when a certain external force is applied, and will return to its original shape after removing the external force, with solid viscoelasticity; microscopically, polymer gel has a three-dimensional network structure and is insoluble in water, three-dimensional Network molecules can be stretched in water and have liquid properties. The gel with softness, high water content and rubber viscoelasticity has been widely used in many fields su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F285/00C08F222/14C08F8/14C08F290/06C08F220/34
CPCC08F285/00C08F8/14C08F290/062C08F2800/20C08F2810/20C08F222/14C08F220/34
Inventor朱明魏嘉江燕妮
OwnerSICHUAN NORMAL UNIVERSITY