Composition containing heterocyclic organic matter and polyalcohol composite PVC heat stabilizer and preparation method thereof

A technology of heterocyclic organic compounds and heat stabilizers, which is applied in the field of PVC heat stabilizers, can solve the problems of poor long-term thermal stability, achieve good thermal stability, simple preparation process, and increase the effect of long-term thermal stability

Inactive Publication Date: 2019-04-30
HUBEI UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the above problems, aiming to provide a kind of shortcoming that can overcome the "zinc burning" phenomenon and poor long-term thermal stability of traditional calcium-zinc heat stabilizers, and has the advantages of environmental protection, non-toxicity, high efficiency, etc., and at the same time, the compound system can Produce synergistic effect, improve the thermal stability of PVC, improve the thermal stability of PVC, the composition containing heterocyclic organic matter and polyhydric alcohol composite PVC heat stabilizer and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition containing heterocyclic organic matter and polyalcohol composite PVC heat stabilizer and preparation method thereof
  • Composition containing heterocyclic organic matter and polyalcohol composite PVC heat stabilizer and preparation method thereof
  • Composition containing heterocyclic organic matter and polyalcohol composite PVC heat stabilizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The preparation method of the present invention is to put PVC, composite heat stabilizer, and calcium carbonate into a high-speed mixer and mix them evenly; carry out mixing on a double-roll mill at 170 ° C, fully mix and plasticize for 5 minutes, and then take off the sheet, and the thickness of the next sheet is 1mm, then performance test.

[0024] The speed of the high-speed mixer used: 1440rpm, the temperature: 60-80°C, and the mixing time: 5min.

[0025] The performance test adopts the static thermal aging method: cut the mixed PVC sample into 4cm×2cm samples, put them in an oven at 180°C, take out a sample every 5 minutes, take pictures, record and compare the addition of different types of stabilizers The discoloration of PVC samples with aging time.

[0026] Performance test Congo red discoloration method: According to GB / T2917.1-2002, cut the prepared PVC sample into a granular sample with a size of 2mm×2mm×1mm, put it into a test tube, and the height of the s...

specific Embodiment approach

[0032] Table 1 PVC composite heat stabilizer comparative example and embodiment

[0033]

[0034]

Embodiment 1

[0036] 1) Weigh 1000g PVC (SG-5), 150g superfine light calcium carbonate, 5g zinc stearate, 3g 4-amino-1,5-dimethyl-2-phenyl-3-pyrazolone , 5 g of sorbitol, and 16 g of polyethylene wax were plasticized on an open mill at 170° C. for 5 minutes and then released into sheets with a thickness of 1 mm.

[0037] 2) Mix the homogeneously mixed mixture in step 1) on a double-roll mill at 170°C, fully mix and plasticize for 5 minutes, and then release the sheet, the thickness of which is 1mm;

[0038] 3) Performance test: use the static heat aging method to test the discoloration of the sample with aging time, or use the Congo red discoloration method to test the thermal stability time of the sample.

[0039] Static heat aging results see figure 1 , Congo red discoloration time is shown in Table 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heterocyclic organic matter and polyhydric alcohol composite PVC (polyvinyl chloride) heat stabilizing agent and a preparation method thereof. A composite thermal stabilizing agent is prepared from the following ingredients in parts by mass through being metered by 100 mass parts of PVC: 15 parts of calcium carbonate, 0.5 to 0.9 part of zinc stearate, 0.1 to 0.5 part of pyrazolone type heat stabilizers, 0.1 to 0.5 part of polyols and 1.6 parts of lubricating agents. According to the preparation method, the PVC, the composite heat stabilizers, the composite heat stabilizers, the calcium carbonate and the lubricating agents are put into a high-speed mixing machine to be uniformly mixed; blending is performed on a 170 DEG C double-roller mill mixer; after the sufficient mixing and plasticization for 5 min, sheet cutting is performed, and the sheet thickness is 1mm; then, a static state heat aging method and a Congo red color change method are used for performing performance test. The pyrazolone type thermal stabilizing agents are used for replacing active chlorine atoms; the generation capability of the conjugated polyene sequence is blocked; the zinc burning phenomenon can be delayed by using polylol; the stability is high. The preparation method has the advantages that the preparation process is simple; the environment is protected; no toxicity exists; the efficiency is high, and the like.

Description

technical field [0001] The invention relates to the technical field of PVC heat stabilizers, in particular to a composition containing heterocyclic organic matter and polyol composite PVC heat stabilizers and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is an important general-purpose thermoplastic, which is widely used in many fields due to its superior performance and low price. However, due to the defective structure on the PVC molecular chain, such as allyl chloride group, end group, oxygen-containing group, head-to-head structure, etc., it is easy to degrade during the heating process, resulting in serious discoloration and mechanical damage to the surface of PVC material. Performance deterioration, so it is necessary to suppress the thermal degradation of PVC by adding a suitable heat stabilizer. PVC heat stabilizers generally replace the active chlorine atoms on the PVC chain to prevent further HCl removal reaction, or absorb t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L23/06C08K13/02C08K3/26C08K5/098C08K5/353C08K5/053C08K5/092
CPCC08K3/26C08K5/053C08K5/092C08K5/098C08K5/353C08K13/02C08L27/06C08L2201/08C08L23/06C08K2003/265
Inventor 严海彪吕奇
Owner HUBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com