Preparing method of 6181 aluminum alloy panel

A technology of aluminum alloy plates and aluminum alloy ingots, which is applied in the field of aluminum alloys, can solve the problems of reducing the formability of plates, increasing production costs, and reducing production efficiency, and achieves the effects of improving deep drawing performance, increasing production efficiency, and saving energy

Active Publication Date: 2017-05-31
NORTHEASTERN UNIV
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The homogenization treatment temperature of 6181 aluminum alloy ingots generally exceeds 540 ° C, and the holding time exceeds 12 hours, which not only consumes time and energy, but also seriously reduces production efficiency and significantly increases production costs. The excess crystalline phase is spheroidized, coarsened and distributed along the dendrite boundary, which may reduce the formability of subsequent sheets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method of 6181 aluminum alloy panel
  • Preparing method of 6181 aluminum alloy panel
  • Preparing method of 6181 aluminum alloy panel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A preparation method of 6181 aluminum alloy plate, comprising the following steps:

[0034] (1) Ingot preparation: 6181 aluminum alloy ingots were prepared by direct water-cooling semi-continuous casting, with a thickness of 180mm, and the ingredients and their mass percentages were: Si: 0.82%, Mg: 0.99%, Cu≤0.10%, Mn≤ 0.15%, Fe≤0.45%, Zn≤0.20%, Cr≤0.10%, Ti≤0.10%, impurity elements≤0.15%, the balance is Al;

[0035] (2) Heating: After the 6181 aluminum alloy ingot is cut and milled, it is heated to 430 ° C in a circulating air furnace and kept for 4 hours;

[0036] (3) Hot rolling: hot rolling the 6181 aluminum alloy ingot after heat preservation, first rolling 4 passes along the width direction of the slab ingot, and then rolling 15 passes along the length direction of the slab ingot to obtain Hot-rolled plate, the thickness of the hot-rolled plate is 3mm;

[0037] (4) Intermediate annealing: After cutting the hot-rolled sheet to length, heat it to 425°C in a circul...

Embodiment 2

[0058] A preparation method of 6181 aluminum alloy plate, comprising the following steps:

[0059] (1) Ingot preparation: 6181 aluminum alloy ingots were prepared by direct water-cooling semi-continuous casting, with a thickness of 100mm, and the ingredients and their mass percentages were: Si: 0.80%, Mg: 1.00%, Cu≤0.10%, Mn≤ 0.15%, Fe≤0.45%, Zn≤0.20%, Cr≤0.10%, Ti≤0.10%, impurity elements≤0.15%, the balance is Al;

[0060] (2) Heating: After the 6181 aluminum alloy ingot is cut and milled, it is heated to 425 ° C in a circulating air furnace and kept for 6 hours;

[0061] (3) Hot rolling: hot rolling the 6181 aluminum alloy ingot after heat preservation, first rolling 4 passes along the width direction of the slab ingot, and then rolling 11 passes along the length direction of the slab ingot to obtain Hot-rolled plate, the thickness of the hot-rolled plate is 5mm;

[0062] (4) Intermediate annealing: After cutting the hot-rolled sheet to length, heat it to 430°C in a circul...

Embodiment 3

[0070] A preparation method of 6181 aluminum alloy plate, comprising the following steps:

[0071] (1) Ingot preparation: 6181 aluminum alloy ingots were prepared by direct water-cooling semi-continuous casting, with a thickness of 120mm, and the ingredients and their mass percentages were: Si: 0.82%, Mg: 0.99%, Cu≤0.10%, Mn≤ 0.15%, Fe≤0.45%, Zn≤0.20%, Cr≤0.10%, Ti≤0.10%, impurity elements≤0.15%, the balance is Al;

[0072] (2) Heating: After the 6181 aluminum alloy ingot is cut and milled, it is heated to 480 ° C in a circulating air furnace and kept for 4 hours;

[0073] (3) Hot rolling: hot-rolling the 6181 aluminum alloy ingot after heat preservation, first rolling 5 passes along the width direction of the slab ingot, and then rolling 10 passes along the length direction of the slab ingot to obtain Hot-rolled plate, the thickness of the hot-rolled plate is 5mm;

[0074] (4) Intermediate annealing: After cutting the hot-rolled sheet to length, heat it to 440°C in a circul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A preparing method of a 6181 aluminum alloy panel comprises following steps that a 6181 aluminum alloy ingot casting is prepared; the 6181 aluminum alloy ingot casting is heated to 420 DEG C to 480 DEG C, after heat preservation, the casting is subject to hot rolling, and a hot-rolled plate is obtained; the hot-rolled plate is heated to 420 DEG C to 440 DEG C, after heat preservation, furnace cooling to the room temperature is carried out, and through cold rolling, a cold-rolled plate is obtained; through solid-solution treatment, room temperature containing, preageing treatment, and secondary room temperature containing, that is, T4P state, the 6181 aluminum alloy panel is prepared; through the method, casting ingot conventional high-temperature homogenization treatment is reduced, the process flow is shortened, energy is saved, production efficiency is improved, and the cost is greatly reduced; the method can be implemented on an existing aluminum alloy production line, devices and process investment do not need to be added, operation is easy and convenient, remaining crystalline phase particles in the manufactured 6181 aluminum alloy panel are small in size, and are distributed in a dispersion manner, the 6181 aluminum alloy panel punching property is improved, and the property requirement in punching production is completely met while the cost is reduced.

Description

[0001] Technical field: [0002] The invention belongs to the technical field of aluminum alloys, and in particular relates to a preparation method of a 6181 aluminum alloy plate. [0003] Background technique: [0004] Since the car body accounts for about 30% of the weight of the whole vehicle, the use of aluminum alloy instead of steel plate to manufacture the body can reduce the weight of the body by more than 50%, which can significantly reduce the weight of the whole vehicle; under the same impact, the aluminum plate can absorb 50% more impact energy than the steel plate , increasing the safety of the occupants. In addition, the aluminum body basically does not rust during use and has a very high recovery rate. It is an ideal recyclable and environmentally friendly material. Therefore, the urgency and importance of aluminumizing the automobile body are self-evident. The 6181 aluminum alloy sheet that can be strengthened by heat treatment has become an ideal lightweight a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C21/08C22F1/043C22F1/047C22F1/05
CPCC22C21/02C22C21/08C22F1/043C22F1/047C22F1/05