Adhesive slurry for laying self-adhesive coiled material by wet laying method and preparation method thereof
A technology of self-adhesive coil material and adhesive slurry, applied in the field of adhesive paste and its preparation, can solve the problem that the bonding effect of the adhesive paste is not ideal, the self-adhesive coil material is not firmly bonded to the base layer, and the self-adhesive The problems such as the separation of the coil and the base layer can avoid other reactions or even deterioration, shorten the demoulding time and reduce the cost.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] Embodiment 1: A kind of bonding slurry that wet paving method lays self-adhesive roll material is used, and the raw material that gets following mass parts is made (each part gets 16kg): 45 parts of JS waterproof coatings, 13 parts of plugging king, common 45 parts of Portland cement, 4 parts of methyl acrylate, 8 parts of hydroxypropyl methylcellulose, 2.3 parts of lignin, 3 parts of rubber powder, 6 parts of micronized silica gel, 1.2 parts of polyvinyl alcohol, 0.8 parts of styrene-acrylate 0.9 parts of rosin resin, 4 parts of gypsum, 2.1 parts of water glass, 2.2 parts of diatomaceous earth, 2.2 parts of polyisobutylene, 1.9 parts of alkylbenzene sulfonate, 3.2 parts of sodium nitrite, 5 parts of potassium sulfate, 0.5 parts of calcium sulfate parts, 70 parts of water.
[0041] The preparation method of the adhesive slurry for laying the self-adhesive coil by the above-mentioned wet laying method, the steps are as follows:
[0042] (1) Rosin resin, polyisobutylene,...
Embodiment 2
[0048] Embodiment 2: A kind of bonding slurry that wet paving method is used for laying self-adhesive roll material, the raw material that gets following mass parts is made (each part gets 15kg): 50 parts of JS waterproof coatings, 18 parts of plugging king, common 55 parts of Portland cement, 6 parts of methyl acrylate, 12 parts of hydroxypropyl methylcellulose, 2.8 parts of lignin, 5 parts of rubber powder, 8 parts of micronized silica gel, 1.6 parts of polyvinyl alcohol, 1.2 parts of styrene-acrylate 1.1 parts of rosin resin, 6 parts of gypsum, 2.5 parts of water glass, 2.6 parts of diatomaceous earth, 2.6 parts of polyisobutylene, 2.2 parts of alkylbenzene sulfonate, 3.7 parts of sodium nitrite, 6 parts of potassium sulfate, 0.7 parts of calcium sulfate part, 80 parts of water.
[0049] The preparation method of the adhesive slurry for laying the self-adhesive coil by the above-mentioned wet laying method, the steps are as follows:
[0050] (1) Rosin resin, polyisobutylen...
Embodiment 3
[0055] Embodiment 3: A kind of bonding slurry that wet laying method is used for laying self-adhesive roll material, get the raw material of following mass parts and make (each part gets 25kg): 47 parts of JS waterproof coating, 15 parts of plugging king, common 49 parts of Portland cement, 4.5 parts of methyl acrylate, 9 parts of hydroxypropyl methylcellulose, 2.5 parts of lignin, 3.5 parts of rubber powder, 6.5 parts of micropowder silica gel, 1.3 parts of polyvinyl alcohol, 0.9 parts of styrene-acrylate 0.95 parts of rosin resin, 4.5 parts of gypsum, 2.2 parts of water glass, 2.3 parts of diatomaceous earth, 2.3 parts of polyisobutylene, 2.0 parts of alkylbenzene sulfonate, 3.4 parts of sodium nitrite, 5.3 parts of potassium sulfate, 0.55 parts of calcium sulfate parts, 73 parts of water.
[0056] The preparation method of the adhesive slurry for laying the self-adhesive coil by the above-mentioned wet laying method, the steps are as follows:
[0057] (1) Rosin resin, poly...