Preparation method of carbon nanometer tube film

A carbon nanotube thin film and mixed solution technology, applied in the field of materials, can solve the problems of uneven distribution, low output, thick pipe diameter, etc., and achieve the effects of good uniformity, high output, and less impurities and defects

Inactive Publication Date: 2017-09-22
沙冰娟
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Carbon nanotubes prepared by existing processes usually have technical problems of low yield, low purity, thick tube diameter and uneven distribution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The preparation method of carbon nanotube film, comprising steps:

[0020] (1), stir ferrocene, 0.8wt% thiophene and oxygen-containing hydrocarbon dehydrated ethanol to prepare a mixed solution with a concentration of 0.04g / ml;

[0021] (2), the mixed solution is coated on the surface of the N-type silicon substrate;

[0022] (3), add the mixed solution into the resistance furnace, and under argon protective gas, heat up to 1250 ℃;

[0023] (4), pass into the hydrogen with flow rate of 450sccm, keep warm for 8 minutes, and form the carbon nanotube film on the surface of the N-type silicon substrate;

[0024] (5), stop feeding hydrogen, cool the furnace, and take out the sample.

[0025] In this example, the carbon nanotube thin film prepared on the surface of the substrate has high yield and good quality, and the carbon nanotubes have high purity, are in the form of a network structure, have a tube diameter of about 18 nm, and have good uniformity, and there are fewer...

Embodiment 2

[0027] The preparation method of carbon nanotube film, comprising steps:

[0028] (1), stirring cobalt, 0.6wt% thiophene and oxygen-containing hydrocarbon dehydrated ethanol to prepare a mixed solution with a concentration of 0.035-0.05g / ml;

[0029] (2), the mixed solution is coated on the surface of the P-type silicon substrate;

[0030] (3), add the mixed solution into the resistance furnace, and under nitrogen protective gas, heat up to 1100 ℃;

[0031] (4), pass into the hydrogen with flow rate of 500sccm, keep warm for 6 minutes, and form the carbon nanotube film on the surface of the p-type silicon substrate;

[0032] (5), stop feeding hydrogen, cool the furnace, and take out the sample.

[0033] In this example, the carbon nanotube thin film prepared on the surface of the substrate has high yield and good quality, and the carbon nanotubes have high purity, are in the form of a network structure, have a tube diameter of about 18 nm, and have good uniformity, and there...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a carbon nanometer tube film. The method comprises the following steps of (1) uniformly stirring catalysts, thiophene and oxygen-containing hydrocarbon absolute ethyl alcohol; preparing a mixed solution with the concentration being 0.035 to 0.05g/ml; (2) coating the surface of a substrate with the mixed solution; (3) adding the mixed solution into a resistance furnace; under the protection gas condition, raising the temperature to 1100 to 1350 DEG C; (4) introducing hydrogen gas with the flow rate being 400 to 500 sccm; performing heat insulation for 6 to 8 minutes; forming a carbon nanometer tube film onto the surface of the substrate; (5) stopping the introduction of the hydrogen gas; cooling the furnace; taking out a sample. The preparation method has the advantages that the carbon nanometer tube film prepared on the surface of the substrate has high yield and high quality; the purity of the carbon nanometer tube is high; a reticular structure is formed; the pipe diameter distribution is about 18nm; the uniformity is good; impurities and defects in the product are few.

Description

technical field [0001] The present application relates to the technical field of materials, in particular to a preparation method of a carbon nanotube film. Background technique [0002] The discovery of carbon nanotubes has led people to open the door to the nano world. Due to its special structure and excellent mechanical, thermal and electrical properties, it has a very wide range of application prospects in materials science, nanoelectronics, biology, etc. extensive scientific research. The vertically aligned carbon nanotube arrays are more conducive to the exertion of certain properties due to their advantages such as high orientation and consistent aspect ratio. [0003] The carbon nanotubes prepared by the existing process usually have the technical problems of low yield, low purity, thick diameter and uneven distribution. SUMMARY OF THE INVENTION [0004] The purpose of the present invention is to provide a preparation method of a carbon nanotube film to overcome...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/16
CPCC01B2202/30C01B2202/36
Inventor 沙冰娟
Owner 沙冰娟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap