A preparation method of blended fabric suitable for gym mats

A blended fabric and gymnastics technology, applied in the field of textile fabrics, can solve the problems that affect the performance of athletes' technical level, easily breed a large number of bacteria, and do not take antibacterial into account, and achieve low cost, beautiful appearance, and improved antibacterial effect.

Active Publication Date: 2019-03-15
HANDAN COLLEGE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Gymnastics mat is a common protective gear used in gymnastics competitions or training. The structure used more is a single sponge layer. Gymnastics mats made of this structure and material can only meet the basic requirements of the International Gymnastics Federation standards, but these gymnastics All the mats have uniform disadvantages, such as aging and deformation after long-term use, which affects the technical level of the athletes; it is not easy to clean, and after the sweat of the athletes drips into the gymnastics mat, it is easy to breed a large number of bacteria
[0003] Chinese invention patent CN103603205A discloses a coating for gymnastics mat fabrics, which prevents or delays aging by forming a protective film on the outer layer of the fabric. However, this treatment method is not environmentally friendly due to the addition of a large amount of organic materials. , used indoors is harmful to the human body; second, the antibacterial function is not considered, so it is necessary to study a new type of blended fabric suitable for gymnastics mats

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for preparing a blended fabric suitable for gymnastics mats includes the following steps:

[0027] A. Using Polygonum multiflorum vine as the raw material, using the alkaline boiling degumming process to prepare Polygonum multiflorum vine monofilament;

[0028] B. Put the monofilament of Polygonum multiflorum rattan into lime water and soak it for 2.5 hours, and then dry it until the moisture content is 28%;

[0029] C. Freeze the single fiber of Polygonum multiflorum rattan at a low temperature of minus 28°C for 7 hours;

[0030] D. Take out the monofilament of Polygonum multiflorum rattan and put it in a vacuum puffing box, reduce the air pressure from 12MPa to normal pressure within 7s, put it in water, add biological antibacterial agent, and after microwave dispersion, dry it to a moisture content of 8 %;

[0031] E. Use cotton fiber as the outer layer and Polygonum multiflorum rattan single fiber as the core to make core-spun yarn;

[0032] F. The core-spun yarn and...

Embodiment 2

[0040] A method for preparing a blended fabric suitable for gymnastics mats includes the following steps:

[0041] A. Using Polygonum multiflorum vine as the raw material, using the alkaline boiling degumming process to prepare Polygonum multiflorum vine monofilament;

[0042] B. Put the monofilament of Polygonum multiflorum rattan into lime water and soak for 2h, and then dry it to 30% water content;

[0043] C. Freeze the single fiber of Polygonum multiflorum rattan at minus 22℃ for 8h;

[0044] D. Take out the monofilament of Polygonum multiflorum rattan and put it into a vacuum puffing box, reduce the air pressure from 15MPa to normal pressure within 5s, put it in water, add biological antibacterial agent, carry out microwave dispersion, and dry until the moisture content is 9 %;

[0045] E. Use cotton fiber as the outer layer and Polygonum multiflorum rattan single fiber as the core to make core-spun yarn;

[0046] F. The core-spun yarn and polyester fiber are blended, dyed, printe...

Embodiment 3

[0054] A method for preparing a blended fabric suitable for gymnastics mats includes the following steps:

[0055] A. Using Polygonum multiflorum vine as the raw material, using the alkaline boiling degumming process to prepare Polygonum multiflorum vine monofilament;

[0056] B. Put the monofilament of Polygonum multiflorum rattan into lime water to soak for 3 hours, and then dry it until the water content is 20%;

[0057] C. Freeze the single fiber of Polygonum multiflorum rattan at a low temperature below minus 20°C for 8 hours;

[0058] D. Take out the monofilament of Polygonum multiflorum rattan and put it into a vacuum puffing box, reduce the air pressure from 15MPa to normal pressure within 5s, put it in water, add biological antibacterial agent, carry out microwave dispersion, and dry it to a moisture content of 6 %;

[0059] E. Use cotton fiber as the outer layer and Polygonum multiflorum rattan single fiber as the core to make core-spun yarn;

[0060] F. The core-spun yarn and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of blended fabric suitable for an exercise mat. The principal raw material comprises a polygonum multiflorum rattan single fiber, cotton fibers and polyester fibers, wherein the proportion of the polygonum multiflorum rattan single fiber exceeds 2 / 3, the waste can be used, and the prepared fibers have the remarkable anti-bacterial effects. A covering yarn mode is used because the spinning property of the polygonum multiflorum rattan fiber is poorer, the covering yarn is formed by using the cotton fibers for covering and blended with Dacron. Although the content of the cotton fibers and the polyester fibers is not higher than 30% still, the appearance of the blended fabric is beautiful, and even a lot of the cotton fibers on the surface layer is worn after the long-term use, and the polygonum multiflorum rattan single fiber is exposed, the blended fabric still has not the burr feeling. In conclusion, the prepared blended fabric suitable for the exercise mat has the characteristics of low cost, good safety, and good anti-bacterial effect, and is a novel fiber suitable for the requirement of modern sports equipment.

Description

Technical field [0001] The invention relates to the technical field of textile fabrics, in particular to a method for preparing a blended fabric suitable for gymnastics mats. Background technique [0002] Gymnastics mats are commonly used protective gears used in gymnastics competitions or training. Most of the structures used are a single sponge layer. Gymnastics mats made of this structure and materials can only meet the basic requirements of the International Association of Sports Standards, but these gymnastics All mats have uniform disadvantages. For example, they are prone to aging and deformation after a long time of use, which affects the technical level of athletes; it is not easy to clean, and athletes’ sweat is easy to breed a lot of bacteria after dripping into gymnastics mats. [0003] Chinese invention patent CN103603205A discloses a paint for gymnastic mat fabrics. The paint prevents or delays aging by forming a protective film on the outer layer of the fabric. Howev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01C1/02D02G3/04D02G3/36D03D15/00A63B6/00
CPCA63B6/00D01C1/02D02G3/042D02G3/36D03D15/44D03D15/47
Inventor 李星崔志莹卢建辉马淑卿张勇姜忠晓
Owner HANDAN COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products