A kind of bio-based aromatic hydrocarbon polyester polyol for controlled release fertilizer and application thereof

A polyester polyol, bio-based technology, applied in the field of controlled-release fertilizers, can solve the problems that the release of controlled-release fertilizers cannot be achieved, the effect of nutrient controlled-release is weakened, etc., and achieve the effect of moderate viscosity and less dosage.

Active Publication Date: 2019-08-09
张家港晟新和新材料有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Once the number of coatings is reduced to 3-5%, the controlled release effect of nutrients will be significantly weakened, and the release will not meet the standards of controlled release fertilizers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bio-based aromatic hydrocarbon polyester polyol for controlled release fertilizer and application thereof
  • A kind of bio-based aromatic hydrocarbon polyester polyol for controlled release fertilizer and application thereof
  • A kind of bio-based aromatic hydrocarbon polyester polyol for controlled release fertilizer and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The present invention will be further described below in combination with embodiments, so that anyone skilled in the art can make and use the present invention. The embodiments in the following description are by way of example only and modifications will be apparent to those skilled in the art. The general principles defined in the following description will apply to other embodiments, alternatives, modifications, equivalent implementations and applications without departing from the spirit and scope of the invention.

[0040] The main raw material of controlled-release fertilizer polyurethane material coating in the following examples is: bio-based aromatic hydrocarbon polyester polyol (the present invention), castor oil (Tongliao, Inner Mongolia), plasticizer epoxy soybean oil (Guangzhou Jiangyan Chemical Technology Co., Ltd. ), crude MDI (Yantai Wanhua Chemical Group), urea.

[0041] 1. The process of controlled-release fertilizer coating embodiment 1 mainly includ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
acid valueaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Login to View More

Abstract

The invention discloses bio-based aromatic hydrocarbon polyester polyol for controlled-release fertilizer. The bio-based aromatic hydrocarbon polyester polyol is characterized by being synthesized according to a method comprising the following steps: sucking fatty acid (1mol), diethylene glycol (2mol), glycerol (2mol) and the like into a reaction kettle in vacuum according to a sequence; adding terephthalic acid (3mol), phthalic anhydride (2mol) and trimethylol propane (2mol) from a solid feeding hole in the reaction kettle; after stirring in the reaction kettle for 1h, displacing air in the reaction kettle once with nitrogen gas; slowly raising the temperature of the reaction kettle to 180 DEG C to 240 DEG C, carrying out esterification reaction to distill water and maintaining the temperature for 4h; when the temperature of the top of an esterification tower is lower than about 95 DEG C and no water is discharged, sampling and testing an acid value; when the acid value is less than 15mgKOH / g, supplementing a catalyst Tio2 / SO4-2 solid super acid which accounts for 0.03 percent of the total amount; continually keeping heat and reacting for 1h; then carrying out vacuum extraction for about 2h and controlling the vacuum degree to be -0.085mPa to -0.095mPa; when the acid value is less than 2mgKOH / g, the reaction is completed; then cooling and filtering and packaging to obtain a bio-based aromatic hydrocarbon polyester polyol finished product.

Description

technical field [0001] The invention belongs to the technical field of controlled-release fertilizers, and in particular relates to a bio-based aromatic polyester polyol for controlled-release fertilizers and an application thereof. Background technique [0002] my country is a big agricultural country and also a big country that uses fertilizers. However, the utilization rate of traditional fertilizers has been low for a long time. In order to achieve the goal of increasing production, there is only excessive application. This not only wastes a lot of resources, but also brings serious damage to the quality of cultivated land and related water bodies. How to improve the utilization rate of fertilizers to achieve the purpose of increasing efficiency, increasing production, reducing weight and reducing pollution is an inevitable requirement for the development of high-efficiency, green and sustainable agriculture, and the emergence of controlled-release fertilizers can just s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/672C08G63/87C08G18/76C08G18/42C08G18/36C05G3/00C05G3/08C05G3/90
CPCC05G3/90C05G5/37C08G18/36C08G18/4219C08G18/7671C08G63/672C08G63/87
Inventor 颜迪冯向华
Owner 张家港晟新和新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com