Graphene-containing consumable material for printing and preparation method thereof

A technology of graphene and consumables, which is applied in the field of graphene-containing printing consumables and its preparation, which can solve problems such as waste of banana stalk resources, achieve the effect of increasing added value and expanding the scope of application

Inactive Publication Date: 2017-12-01
广西丰达三维科技有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The invention provides a graphene-containing printing consumable and a preparation method thereof to solve the problems of waste of existing banana stalk resources and the like

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene-containing consumable material for printing and preparation method thereof
  • Graphene-containing consumable material for printing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] A graphene-containing printing consumables, in parts by weight, including the following raw materials: 98 parts of banana stalks, 28 parts of kaolin, 63 parts of polylactic acid, 24 parts of potassium tripolyphosphate, 1.2 parts of graphene, fatty alcohol polyoxygen 6 parts of ammonium vinyl ether sulfate, 0.5 parts of triethanolamine soap, 4.5 parts of compound agent I, 3.6 parts of compound agent II;

[0072] The composite agent I includes the following raw materials in parts by weight: 1.7 parts of glycidyl methacrylate, 4.6 parts of modified polyacrylate, 2.2 parts of bis(2-ethylhexyl) phthalate, antioxidant 2 parts of agent 1076, 4.3 parts of polyaluminum chloride, 3 parts of ACR foam regulator, 2 parts of aerosol generating agent, 3.2 parts of coupling agent kh-550;

[0073] The composite agent II is in parts by weight and includes the following raw materials: 152 parts of tapioca starch, 18 parts of dimethyl phosphite, N-ethyl-5-methyl-2-(1-methylethyl)cyclohexyl...

Embodiment 2

[0091] A graphene-containing printing consumables, in parts by weight, comprising the following raw materials: 130 parts of banana stalks, 32 parts of kaolin, 70 parts of polylactic acid, 30 parts of potassium tripolyphosphate, 1.6 parts of graphene, fatty alcohol polyoxygen 8 parts of ammonium vinyl ether sulfate, 0.7 parts of triethanolamine soap, 6.5 parts of compound agent I, 5 parts of compound agent II;

[0092] The compounding agent I includes the following raw materials in parts by weight: 2.5 parts of glycidyl methacrylate, 5.4 parts of modified polyacrylate, 3.2 parts of bis(2-ethylhexyl) phthalate, antioxidant 3 parts of agent 1076, 5.3 parts of polyaluminum chloride, 4 parts of ACR foam regulator, 3 parts of aerosol generating agent, 4.5 parts of coupling agent kh-550;

[0093] The composite agent II is in parts by weight and includes the following raw materials: 165 parts of tapioca starch, 20 parts of dimethyl phosphite, N-ethyl-5-methyl-2-(1-methylethyl)cyclohex...

Embodiment 3

[0111] A graphene-containing printing consumables, in parts by weight, including the following raw materials: 156 parts of banana stalks, 36 parts of kaolin, 78 parts of polylactic acid, 35 parts of potassium tripolyphosphate, 2 parts of graphene, fatty alcohol polyoxygen 10 parts of ammonium vinyl ether sulfate, 0.8 parts of triethanolamine soap, 8.7 parts of compound agent I, 6.2 parts of compound agent II;

[0112] The compounding agent I includes the following raw materials in parts by weight: 3.5 parts of glycidyl methacrylate, 6.2 parts of modified polyacrylate, 4 parts of bis(2-ethylhexyl) phthalate, antioxidant 4 parts of agent 1076, 6.3 parts of polyaluminum chloride, 5 parts of ACR foam regulator, 4 parts of aerosol generating agent, 5.6 parts of coupling agent kh-550;

[0113] The composite agent II is in parts by weight and includes the following raw materials: 182 parts of tapioca starch, 22 parts of dimethyl phosphite, N-ethyl-5-methyl-2-(1-methylethyl)cyclohexyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a graphene-containing printing consumable and a preparation method thereof. The printing consumable includes the following raw materials in parts by weight: 130 parts of banana stalks, 32 parts of kaolin, 70 parts of polylactic acid, and tripolyphosphoric acid 30 parts of potassium, 1.6 parts of graphene, 8 parts of fatty alcohol polyoxyethylene ether ammonium sulfate, 0.7 parts of triethanolamine soap, 6.5 parts of compound agent I, and 5 parts of compound agent II. The printing consumables are prepared from banana stalk powder, It is made of modified kaolin, activated graphene energy powder, 3D printing primary material, mixing, extrusion into strips and other steps. The graphene-containing printing consumables of the present invention have high tensile strength and elongation at break, and can be applied to 3D printing.

Description

【Technical field】 [0001] The invention belongs to the technical field of preparation of materials for 3D printing, and in particular relates to a printing consumable containing graphene and a preparation method thereof. 【Background technique】 [0002] 3D printing is a kind of rapid prototyping technology. It is a technology based on digital model files and using bondable materials such as powdered metal or banana stalks to construct objects by layer-by-layer printing. 3D printing is usually realized by using digital technology material printers. It is often used to manufacture models in mold manufacturing, industrial design and other fields, and is gradually used in the direct manufacturing of some products. There are already parts printed using this technology. , the technology has applications in jewelry, footwear, industrial design, architecture, engineering and construction (AEC), automotive, aerospace, dental and medical industries, education, geographic information sys...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L67/04C08K13/06C08K9/04C08K3/34C08K3/04C08K3/32B33Y70/00
CPCC08L97/02B33Y70/00C08K2003/324C08K2201/014C08L2201/06C08L2205/035
Inventor 钟镇鸿
Owner 广西丰达三维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com