A technology of polishing powder and terrazzo, which is applied in the direction of polishing compositions containing abrasives, etc., can solve problems such as polishing brightness and changes that affect polishing efficiency, and achieve good polishing effects, easy control of conditions, and good fluidity

Inactive Publication Date: 2017-12-08
UNIV OF JINAN
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in the polishing powder, the change of the chemical composition will lead to the change of the adhesion between the polishing film and the terrazzo, and the change of the concentration of the polishing powder, which will eventually affect the polishing efficiency and the brightness of the polishing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) Cr 2 o 3 –Fe 2 o 3 -SnO 2 Preparation of the complex: Add water: 640 mL, ferric chloride: 80g, stir and dissolve, add chromium trioxide: 180g, tin dioxide: 80g, add sodium hydroxide: 20g, stir at room temperature React for 30 minutes, separate solid and liquid, dry at 100±2°C, and then roast at 500±10°C for 2 hours, after cooling, crush by air flow to obtain Cr 2 o 3 –Fe 2 o 3 -SnO 2 Complex;

[0019] (2) Preparation of terrazzo polishing powder: In the grinder, add Cr 2 o 3 –Fe 2 o 3 -SnO 2 Compound: 120g, oxalic acid dihydrate: 520g, ammonium hydrogen oxalate: 180g, grind, mix well, add rosin powder: 60g, stearic acid: 100g, grind, mix well, nonionic surfactant: 20g, grind, mix Evenly, the terrazzo polishing powder is obtained.

Embodiment 2

[0021] (1) Cr 2 o 3 –Fe 2 o 3 -SnO 2 Preparation of the complex: In the reactor, add water: 300 mL, ferric chloride: 50 g, stir and dissolve, add chromium trioxide: 100 g, tin dioxide: 30 g, add sodium hydroxide: 20 g, stir at room temperature React for 30 minutes, separate solid and liquid, dry at 100±2°C, and then roast at 500±10°C for 2 hours, after cooling, crush by air flow to obtain Cr 2 o 3 –Fe 2 o 3 -SnO 2 Complex;

[0022] (2) Preparation of terrazzo polishing powder: In the grinder, add Cr 2 o 3 –Fe 2 o 3 -SnO 2 Compound: 75g, oxalic acid dihydrate: 275g, ammonium hydrogen oxalate: 85g, grind, mix well, add rosin powder: 20g, stearic acid: 30g, grind, mix well, nonionic surfactant: 15g, grind, mix Evenly, the terrazzo polishing powder is obtained.

Embodiment 3

[0024] (1) Cr 2 o 3 –Fe 2 o 3 -SnO 2 Preparation of the complex: In the reactor, add water: 64 mL, ferric chloride: 8g, stir and dissolve, add chromium trioxide: 18g, tin dioxide: 8g, add sodium hydroxide: 2g, stir at room temperature React for 30 minutes, separate solid and liquid, dry at 100±2°C, and then roast at 500±10°C for 2 hours, after cooling, crush by air flow to obtain Cr 2 o 3 –Fe 2 o 3 -SnO 2 Complex;

[0025] (2) Preparation of terrazzo polishing powder: In the grinder, add Cr 2 o 3 –Fe 2 o 3 -SnO 2Compound: 12g, oxalic acid dihydrate: 52g, ammonium hydrogen oxalate: 18g, grind, mix well, add rosin powder: 6g, stearic acid: 10g, grind, mix well, nonionic surfactant: 2g, grind, mix Evenly, the terrazzo polishing powder is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of polishing powder for polishing a water grindstone. The preparation method is characterized in that a Cr2O3-Fe2O3-SnO2 compound is used as a grinding material, oxalic acid is used as an acidic polishing agent, and additives including a dispersant, a surfactant and the like are added to prepare the polishing powder. The specific preparation method comprises the following steps: in a grinding machine, adding the following components according to the following mass percent concentration: 10 percent to 15 percent of the Cr2O3-Fe2O3-SnO2 compound, 50 percent to 55 percent of oxalic acid dihydrate and 15 percent to 20 percent of ammonium bioxalate; grinding the materials and uniformly mixing; adding 4 percent to 8 percent of rosin powder and 6 percent to 12 percent of stearic acid, and grinding and uniformly mixing; adding 1.0 percent to 3.0 percent of a non-ionic surfactant, wherein the sum of all the components is 100 percent; grinding and uniformly mixing to prepare the water grindstone polishing powder. The polishing powder disclosed by the invention has a good polishing effect, high glossiness, fewer scratches, high flatness and a small dosage; the ammonium bioxalate is added so that the corrosion performance of the oxalic acid can be buffered.

Description

technical field [0001] The invention relates to terrazzo surface treatment technology, in particular to a preparation method of polishing powder for terrazzo polishing. Background technique [0002] Terrazzo (also known as terrazzo) is a product made by mixing gravel, glass, quartz stone and other aggregates into cement binder to make a concrete product, and then grinding and polishing the surface. The terrazzo made of cement binder is called inorganic terrazzo, and the terrazzo made of epoxy binder is also called epoxy terrazzo or organic terrazzo. According to the construction process, terrazzo is divided into on-site pouring terrazzo and prefabricated plate terrazzo floor . Traditional terrazzo has a huge market in China due to its unique advantages such as low cost, optional color mosaic, and convenient construction. There are as many as one billion square meters of terrazzo floors used in various buildings in urban and rural areas across the country. Abrasion-resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09G1/02
CPCC09G1/02
Inventor 李慧芝张为民朱学英
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap