A kind of preparation method of blue marble polishing powder

A technology for marble and polishing powder, applied in the field of preparation of blue marble polishing powder, can solve the problems affecting polishing efficiency, polishing powder concentration changes, changes, etc., and achieve the effects of less dosage, less scratches, and easy control of conditions

Inactive Publication Date: 2020-11-27
UNIV OF JINAN
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in the polishing powder, the change of the chemical composition will lead to a change in the adhesion between the polishing film and the marble, and also lead to changes in the temperature and concentration of the polishing powder in the working area, which will eventually affect the polishing efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] (1) AlN-ZrO 2 Preparation of the composite: Into the reactor, add water: 43mL, zirconium oxychloride: 23g, nano-aluminum nitride: 32g, stir and dissolve, add sodium hydroxide: 2g, stir at room temperature for 30min, solid-liquid separation, and After drying at 105±2°C, place it at 550±10°C for 2 hours, and after cooling, crush it by air flow to obtain AlN-ZrO 2 Composite, the particle size is 0.1~5μm;

[0018] (2) Preparation of blue marble polishing powder: In the grinder, add oxalic acid dihydrate: 43g, AlN-ZrO 2 Compound: 20g, copper oxalate: 6g, grind, mix well, add ammonium hydrogen oxalate: 10g, stearic acid: 20g, grind, mix well, then add nonionic surfactant: 1.0g, grind, mix well, that is To obtain blue marble polishing powder, the particle size is between 0.1 and 5 μm.

Embodiment 2

[0020] (1) AlN-ZrO 2 Preparation of the composite: Into the reactor, add water: 40mL, zirconium oxychloride: 26g, nano-aluminum nitride: 30g, stir and dissolve, add sodium hydroxide: 4g, stir at room temperature for 30min, solid-liquid separation, through After drying at 105±2°C, place it at 550±10°C for 2 hours, and after cooling, crush it by air flow to obtain AlN-ZrO 2 Composite, the particle size is 0.1~5μm;

[0021] (2) Preparation of blue marble polishing powder: In the grinder, add oxalic acid dihydrate: 40g, AlN-ZrO 2 Compound: 18g, copper oxalate: 8g, grind, mix well, add ammonium hydrogen oxalate: 12g, stearic acid: 22g, grind, mix well, then add nonionic surfactant: 0.3g, grind, mix well, that is To obtain blue marble polishing powder, the particle size is between 0.1 and 5 μm.

Embodiment 3

[0023] (1) AlN-ZrO 2 Preparation of the composite: Into the reactor, add water: 430mL, zirconium oxychloride: 230g, nano-aluminum nitride: 320g, stir and dissolve, add sodium hydroxide: 20g, stir and react at room temperature for 30min, solid-liquid separation, through After drying at 105±2°C, place it at 550±10°C for 2 hours, and after cooling, crush it by air flow to obtain AlN-ZrO 2 Composite, the particle size is 0.1~5μm;

[0024] (2) Preparation of blue marble polishing powder: In the grinder, add oxalic acid dihydrate: 430g, AlN-ZrO 2 Compound: 200g, copper oxalate: 60g, grind, mix evenly, add ammonium hydrogen oxalate: 100g, stearic acid: 200g, grind, mix evenly, then add non-ionic surfactant: 10g, grind, mix evenly, that is Blue marble polishing powder, the particle size is between 0.1~5μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
hardnessaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing blue marble polishing powder. The method is characterized by comprising the following steps: (1) preparing an AlN-ZrO2 complex, namely adding the following components: 40-60% of water, 20-26% of zirconium oxychloride, 30-36% of nano aluminum nitride and 1-5% of sodium hydroxide, stirring and reacting at a room temperature for 30 minutes, performing solid-liquid separation, drying at the temperature of 105+ / -2 DEG C, roasting at the temperature of 550+ / -10 DEG C for 2 hours, cooling, and performing air jet milling so as to prepare the AlN-ZrO2 complex; and (2) adding the following components into a grinder: 40-45% of oxalate dehydrate, 18-22% of the AlN-ZrO2 complex and 4-8% of cupric oxalate, grinding, uniformly mixing, adding 8-12% of ammonium binoxalate and 18-24% of stearic acid, grinding, uniformly mixing, adding 0.3-1.0%of a nonionic surfactant, uniformly mixing, thereby obtaining the blue marble polishing powder. The polishing powder has the chemical polishing characteristic. Therefore, the polishing powder is excellent in polishing effect, high in glossiness, less in scratch, high in flatness and small in usage amount.

Description

technical field [0001] The invention relates to marble surface treatment technology, in particular to a preparation method of blue marble polishing powder containing abrasives, oxalic acid and auxiliary agents. Background technique [0002] With its natural and simple texture, marble has bright and bright colors, and has the advantages of no deformation, high hardness, good rigidity, strong wear resistance, small temperature deformation, long service life, no scratches, and no magnetization. Therefore, marble is a major category of natural architectural decorative stones, which generally refer to decorative functions and can be processed into architectural stones or handicrafts. Marble is mainly used to be processed into various shapes and plates, and used as walls, floors, platforms, and columns of buildings, and is a precious material for furniture inlays. It is also commonly used as a material for monumental buildings such as monuments, towers, statues, etc. The quality...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/14
CPCC09G1/02C09K3/1436
Inventor 李慧芝卢燕翟殿棠
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com