A technology of epoxy resin and toughening agent, applied in the field of epoxy resin toughening agent and toughening agent, to achieve the effect of low cost, high elongation at break and shear strength, and control of reaction operation
Inactive Publication Date: 2017-12-15
王鹏
View PDF1 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The present invention aims to solve the problems of epoxy resin toughening agents in the prior art, and provides an epoxy resin toughening agent, which has better toughening effect, easy control of reaction operation, and relatively low cost
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] A kind of toughening agent for epoxy resin, comprising following raw materials in parts by weight:
[0033] 2,4-toluene diisocyanate 10 parts
[0034] Polyether 210 20 parts
[0035] Polyethylene glycol 10 parts
[0036] 5 parts m-xylylenediamine
[0037] 20 parts of dimethyl sulfoxide
[0038] Tetrahydrofuran 10 parts.
Embodiment 2
[0040] A kind of toughening agent for epoxy resin, comprising following raw materials in parts by weight:
[0041] 2,4-toluene diisocyanate 20 parts
[0042] Polyether 210 25 parts
[0043] Polyethylene glycol 15 parts
[0044] 10 parts m-xylylenediamine
[0045] 30 parts of dimethyl sulfoxide
[0046] 20 parts of tetrahydrofuran.
Embodiment 3
[0048] A kind of toughening agent for epoxy resin, comprising following raw materials in parts by weight:
[0049] 15 parts of 2,4-toluene diisocyanate
[0050] Polyether 210 22.5 parts
[0051] Polyethylene glycol 12.5 parts
[0052] 7.5 parts m-xylylenediamine
[0053] Dimethyl sulfoxide 25 parts
[0054] Tetrahydrofuran 15 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to an epoxy resin toughening agent, which belongs to the technical field of epoxy resins. The toughening agent includes 10-20 parts of 2,4-toluene diisocyanate, 20-25 parts of polyether 210, 10-15 parts of polyethylene glycol, 5-10 parts of m-xylylenediamine, and 20 parts of dimethyl sulfoxide -30 parts, tetrahydrofuran 10-20 parts. The epoxy resin toughening agent has better toughening effect, easy control of reaction operation and relatively low cost.
Description
technical field [0001] The invention relates to a toughening agent, more specifically, the invention relates to an epoxy resin toughening agent, which belongs to the technical field of epoxy resins. Background technique [0002] Epoxy resin has the advantages of high bonding strength, wide bonding surface, low shrinkage, good electrical properties and acid and alkali resistance, and is widely used as adhesives, electrical materials and insulating materials. However, due to the poor toughness, easy cracking and low impact strength of epoxy resin, it is generally toughened and modified when it is used. Amine-terminated polyurethane is an amine-based epoxy resin curing agent containing polyether flexible chain segments synthesized by the reaction of polyurethane prepolymers with common aliphatic or aromatic amines. The amino-terminated polyurethane is used as the toughening agent of the epoxy resin, and through its curing reaction with the epoxy resin, the molecules of the epo...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.