Preparation method of nano ceramic powder with lubrication function

A nano-ceramic powder, functional technology, applied in the field of nano-materials, achieves the effect of strong practicability, simple process and easy-to-obtain raw materials

Inactive Publication Date: 2018-02-02
佛山慧创正元新材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For inorganic nano-ceramic materials, due to factors such as their specific gravity and compatibility with organic materials, their dispersion is somewhat special, and there is no detailed report on the dispersion of nano-ceramic powder materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Mix 2 parts of alumina, 1 part of calcium borate, 2 parts of carbon powder, 5 parts of carbon fiber, 1 part of titanium carbide, and 5 parts of polyethylene glycol into a high-temperature roller smelting furnace for pressurized roller smelting. The temperature is 1050°C, the pressure is 8MPa, and the reaction is continued for 3 hours. Then, 5 parts of lubricant and 3 parts of phenylethyl alcohol oleate are added, and the stirring is continued for 50 minutes. Insulation, wherein the lubricant is composed of: 7 parts of silicate, 2 parts of phosphate, 1 part of castor oil, 5 parts of glycerol, 1 part of lithium hydroxide, and 1 part of boron nitride;

[0022] (2) Inject the high-temperature mixed solution of step (1) into a screw-type stirring paddle, and carry out cooling and stirring on the above-mentioned mixed solution. The stirring speed is controlled at 500 rpm, and stirring is performed while cooling. Stirring at ℃ for 30 minutes to prepare a semi-solid slurry;...

Embodiment 2

[0027] (1) Mix 3 parts of alumina, 2 parts of calcium borate, 4 parts of carbon powder, 10 parts of carbon fiber, 2 parts of titanium carbide, and 7 parts of polyethylene glycol into a high-temperature roller smelting furnace for pressurized roller smelting. The temperature is 1050°C, the pressure is 8MPa, and the reaction is continued for 3 hours. Then, 5 parts of lubricant and 3 parts of lauryl phenylacetate are added, and the stirring is continued for 50 minutes. Insulation, wherein the lubricant is composed of: 7 parts of silicate, 2 parts of phosphate, 1 part of castor oil, 5 parts of glycerol, 1 part of lithium hydroxide, and 1 part of boron nitride;

[0028] (2) Inject the high-temperature mixed solution of step (1) into the screw-type stirring paddle, lower the temperature and stir the above-mentioned mixed solution, control the stirring speed at 700 rpm, stir while cooling down, and when the temperature reaches 670° C. Stirring at ℃ for 30 minutes to prepare a semi-so...

Embodiment 3

[0033] (1) 5 parts of alumina, 3 parts of calcium borate, 5 parts of carbon powder, 15 parts of carbon fiber, 2 parts of titanium carbide, and 9 parts of polyethylene glycol are mixed and injected into a high-temperature roller smelting furnace for pressurized roller smelting. The temperature is 1050°C, the pressure is 8MPa, and the reaction is continued for 3 hours. Then, 5 parts of lubricant and 3 parts of maleic acid alcohol ester are added, and the stirring is continued for 50 minutes. Keep warm above ℃, and the lubricant composition is: 7 parts of silicate, 2 parts of phosphate, 1 part of castor oil, 5 parts of glycerol, 1 part of lithium hydroxide, and 1 part of boron nitride;

[0034] (2) Inject the high-temperature mixed solution of step (1) into the screw-type stirring paddle, and carry out cooling and stirring on the above-mentioned mixed solution. Stirring at ℃ for 30 minutes to prepare a semi-solid slurry;

[0035] (3) inject the semi-solid slurry in the step (2) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of nano ceramic powder with a lubrication function, ceramic slurry is prepared by pressurizing high temperature roll milling, a specific lubricant and a specific defoaming agent are added, and the nano ceramic powder with the lubrication function can be obtained by screw stirring paddle natural cooling, centrifugal spray drying, sieving, heat treatment,screening and other a series of process for optimization. The nano ceramic powder with the lubrication function effect has good wear resistance, small friction, good lubrication, and good applicationprospect.

Description

technical field [0001] The invention relates to the technical field of nanometer materials, in particular to a preparation method of nanometer ceramic powder with lubricating function. Background technique [0002] High-performance structural ceramics have many excellent properties such as high temperature resistance, wear resistance, corrosion resistance, high strength, and oxidation resistance. They are ideal materials for manufacturing high-temperature lubricating and wear-resistant components. From the perspective of future development, high-temperature structural ceramics are low-density structural materials that can work for a long time above 1000°C and have high strength and corrosion resistance. At present, due to the inherent brittleness of ceramic materials and the decline in mechanical properties of materials caused by tribological design, their wider application in the field of high-temperature lubrication is largely limited. However, the scale of matter after n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/80C04B35/83C04B35/10
CPCC04B35/803C04B35/10C04B35/83C04B2235/3203C04B2235/3409C04B2235/3843C04B2235/386C04B2235/483C04B2235/96C04B2235/963
Inventor 邵光伟
Owner 佛山慧创正元新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap