Method for tanning sheepskin through synergy of organic amine and epoxy resin composition tanning agent

A technology of epoxy resin and composition, applied in leather impregnation, small raw hide/large raw hide/leather/fur treatment, small raw hide/large raw hide/leather skin/fur chemical treatment, etc., to achieve structural stability, reduce tanning time, The effect of promoting penetration

Active Publication Date: 2018-03-23
CHINA LEATHER & FOOTWEAR IND RES INST +1
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for tanning sheep leather with organic amines and epoxy resin tanning agents in order to solve the existing problems of using epoxy resin tanning agents alone or in combination with other tanning agents to tan the resulting leather

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for tanning sheepskin through synergy of organic amine and epoxy resin composition tanning agent
  • Method for tanning sheepskin through synergy of organic amine and epoxy resin composition tanning agent
  • Method for tanning sheepskin through synergy of organic amine and epoxy resin composition tanning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] In this embodiment, the sheepskin after conventional deliming and softening is put into a drum for tanning:

[0045] First, in the melamine bath solution with a liquid ratio of 80% and a concentration of 1.0%, it is treated by turning at 35°C for 60 minutes, then adding an epoxy resin composition tanning agent with a concentration of 10%, turning at 40°C for 1 hour, turning at 50°C for 8 hours, replenishing water, Let it stand overnight, turn it for at least 30 minutes the next day, then control the water and wash it sequentially, use acetic acid solution (acetic acid: water = 1:10 (mass ratio)) to adjust the pH value of the system to 5.5-6.0, then turn it for at least 30 minutes, and take out the drum. Subsequent processing can be carried out as usual.

[0046] Wherein the epoxy resin composition tanning agent used is made up of epoxy resin X and epoxy resin Y with a mass ratio of 5:1, glycerol triglycidyl ether and ethylene glycol diglycidyl ether contained in epoxy r...

Embodiment 2

[0050] In this embodiment, the sheepskin after conventional deliming, softening (degreasing is carried out simultaneously in the softening process, and the pH value is adjusted to 7.5 to 8.0 with baking soda), and pickled is put into a drum for tanning:

[0051] First, in the dicyandiamide bath solution with a liquid ratio of 90% and a concentration of 0.5%, turn it at 40°C for 30 minutes, then add an epoxy resin composition tanning agent with a concentration of 6%, turn it at 38°C for 2 hours, and turn it at 45°C for 10 hours. Replenish the water, let it stand overnight, turn it for at least 30 minutes the next day, then control the water and wash it with water, use formic acid solution (formic acid: water = 1:10 (mass ratio)) to adjust the pH value of the system to 5.5-6.0, turn it for at least 30 minutes, and take out the drum After riding the horse, the subsequent process can be carried out as usual.

[0052] Wherein the epoxy resin composition tanning agent used is to be ...

Embodiment 3

[0056] In this embodiment, the sheepskin after conventional deliming and softening is put into a drum for tanning:

[0057] First, in the amino resin (melamine and formaldehyde polymer, the molar ratio of melamine and formaldehyde is 1:5) bath solution with a liquid ratio of 80% and a concentration of 0.8%, turn it at 30°C for 50 minutes, and then add epoxy resin with a concentration of 12%. Resin composition tanning agent, rotate at 35°C for 1 hour, rotate at 48°C for 10 hours, replenish water, let stand overnight, turn for at least 30 minutes the next day, then control water and wash in turn, use acetic acid solution (acetic acid: water = 1:10 (mass ratio) ) to adjust the pH value of the system to 5.5-6.0, and then rotate for at least 30 minutes, and then proceed to the follow-up process as usual.

[0058] Wherein the epoxy resin composition tanning agent used is made up of epoxy resin X and epoxy resin Y with a mass ratio of 4:1, glycerol triglycidyl ether and ethylene glyc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
temperatureaaaaaaaaaa
viscosityaaaaaaaaaa
temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for tanning sheepskin through synergy of organic amine and an epoxy resin composition tanning agent. The method comprises the steps that softened or acid removing sheepskin is processed by an organic amine bath lotion, and then the epoxy resin composition tanning agent is added for tanning. As the organic amine permeates into skin fibers, the organic amine can cooperate with the epoxy resin composition tanning agent to make amido of the organic amine and amido on skin collagen fibers have a reaction, a net-shaped crosslink structure is formed, and accordingly the damp heat resistance stability of leather is improved, the epoxy resin can serve as the main tanning agent to tan the sheepskin, the tanning performance is improved, the tanned sheepskin leather isclear in grain surface, rich in body, pure white in color and good in yellowing resistance performance, and the storage life of the tanned leather is longer than six months at the room temperature.

Description

technical field [0001] The invention belongs to the technical field of leather tanning technology, and in particular relates to a method for tanning sheepskin with an organic amine in cooperation with a tanning agent of a multi-epoxy epoxy resin composition. Background technique [0002] So far, chrome tanning has been dominant in leather production. The shrinkage temperature of the tanned leather can reach above 100°C, and the comprehensive performance of the finished leather is excellent. However, the trivalent chromium used in tanning can be converted into hexavalent chromium under conditions such as heating or oxidation, while hexavalent chromium is highly toxic and can cause great harm to the ecological environment and human and animal bodies. In recent years, the safety of chrome-tanned leather has been the focus of attention, and the development of chrome-free tanning agents has become a research and development hotspot. [0003] As early as the 1960s, epoxy resin wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C14C3/08C14C3/22C14C9/04
CPCC14C3/08C14C3/22C14C9/04
Inventor 庞晓燕丁志文刘娜郭松
Owner CHINA LEATHER & FOOTWEAR IND RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com