PE film having excellent barrier performance and being antibacterial and preparation method of same

A technology with excellent barrier performance, applied in the field of PE film and its preparation, can solve the problems of PE film barrier, restrict the development of PE film, poor antibacterial effect, etc., achieve good antibacterial performance, important market value and social value, reduce the amount of permeation Effect

Inactive Publication Date: 2018-05-15
GUANGDONG DEXIN TECH INCUBATOR CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the field of packaging materials in the pharmaceutical, food and other industries, although PE films are widely used, because PE films cannot provide a good barrier to oxygen and water vapor, and the antibacterial effect is poor, the development of PE films is restricted. PE film with good antibacterial performance has important market value and social value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A PE film with excellent barrier performance and antibacterial properties is made of the following raw materials in parts by weight: 90 parts of low-density polyethylene, 15 parts of metallocene linear low-density polyethylene, 23 parts of maleamide grafted polyethylene, polyethylene 18 parts of pyrrolidone, 1 part of monoglyceride stearate, 2 parts of polyglyceryl fatty acid ester, 1.3 parts of antioxidant, 1.0 part of fungicide, 0.4 part of oleic acid amide, 0.6 part of calcium naphthenate, modified diatomaceous earth 0.9 servings.

[0025] Wherein, the antioxidant is composed of antioxidant 164 and antioxidant TNP, and the weight ratio of antioxidant 164 and antioxidant TNP in the antioxidant is 5:3. The bactericide is composed of silver amino acid and potassium sorbate, and the weight ratio of silver amino acid and potassium sorbate in the bactericide is 1:2. The modified diatomite is prepared by the following method: weigh diatomite, put it into 10% citric acid so...

Embodiment 2

[0033] A PE film with excellent barrier performance and antibacterial properties is made of the following raw materials in parts by weight: 92 parts of low-density polyethylene, 16 parts of metallocene linear low-density polyethylene, 24 parts of maleamide grafted polyethylene, polyethylene 21 parts of pyrrolidone, 1.7 parts of monoglyceride stearate, 4 parts of polyglycerol fatty acid ester, 1.4 parts of antioxidant, 1.1 parts of fungicide, 0.7 part of oleic acid amide, 0.9 part of calcium naphthenate, modified diatomaceous earth 1.0 servings.

[0034] Wherein, the antioxidant is composed of antioxidant 164 and antioxidant TNP, and the weight ratio of antioxidant 164 and antioxidant TNP in the antioxidant is 5:3. The bactericide is composed of silver amino acid and potassium sorbate, and the weight ratio of silver amino acid and potassium sorbate in the bactericide is 1:2. The modified diatomite is prepared by the following method: weigh diatomite, put it into 10% citric aci...

Embodiment 3

[0042] A PE film with excellent barrier performance and antibacterial properties is made of the following raw materials in parts by weight: 95 parts of low-density polyethylene, 17 parts of metallocene linear low-density polyethylene, 24 parts of maleamide grafted polyethylene, polyethylene 20 parts of pyrrolidone, 1.3 parts of monoglyceride stearate, 3.6 parts of polyglycerol fatty acid ester, 1.5 parts of antioxidant, 1.2 parts of fungicide, 0.6 part of oleic acid amide, 0.8 part of calcium naphthenate, modified diatomaceous earth 1.1 parts.

[0043]Wherein, the antioxidant is composed of antioxidant 164 and antioxidant TNP, and the weight ratio of antioxidant 164 and antioxidant TNP in the antioxidant is 5:3. The bactericide is composed of silver amino acid and potassium sorbate, and the weight ratio of silver amino acid and potassium sorbate in the bactericide is 1:2. The modified diatomite is prepared by the following method: weigh diatomite, put it into 10% citric acid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PE film having excellent barrier performance and being antibacterial, which is prepared from, by weight, 90-100 parts of low density polyethylene, 15-20 parts of metallocenelinear low density polyethylene, 23-26 parts of maleic amide grafted polyethylene, 18-22 parts of polyvinylpyrrolidone, 1-2 parts of glycerol monostearate, 2-5 parts of polyglycerol fatty acid ester,1.3-1.7 parts of an antioxidant, 1.0-1.5 parts of a sterilizing agent, 0.4-0.8 parts of oleamide, 0.6-1.0 part of calcium naphthenate, and 0.9-1.3 parts of modified diatomite. The invention also discloses a preparation method of the PE film having excellent barrier performance and being antibacterial. The PE film has excellent barrier performance and antibacterial performance, can be widely applied to package materials in the fields of medicines, foods and the like. The invention can promote development of the PE films.

Description

technical field [0001] The invention relates to the technical field of packaging materials, in particular to a PE film with excellent barrier performance and antibacterial properties and a preparation method thereof. Background technique [0002] Polyethylene (referred to as PE) is a thermoplastic resin obtained by polymerization of ethylene. In industry, it also includes copolymers of ethylene and a small amount of α-olefins. Polyethylene is odorless, non-toxic, feels like wax, has excellent low temperature resistance (the lowest operating temperature can reach -100 ° C ~ -70 ° C), good chemical stability, and can withstand most acid and alkali erosion (not resistant to oxidation) nature of the acid). It is insoluble in common solvents at room temperature, has low water absorption and excellent electrical insulation, so it is widely used in various industries. Polyethylene film is the most widely used polymer material in the world today. PE protective film is based on s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L51/06C08L39/06C08K13/06C08K9/04C08K3/34C08K5/17C08K5/098C08J5/18
CPCC08J5/18C08J2323/06C08J2423/08C08J2439/06C08J2451/06C08K3/34C08K5/098C08K5/175C08K9/04C08K13/06
Inventor 吴道民吴道祥冯奋
Owner GUANGDONG DEXIN TECH INCUBATOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products