Polypropylene composite material and preparation method thereof

A composite material and polypropylene technology, applied in the field of polypropylene composite material and its preparation, can solve the problems of long preparation period, difficult mass production, complicated preparation process, etc. The effect of friction fluctuation reduction

Active Publication Date: 2018-06-22
WUHAN JINFA TECH CO LTD +1
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN105315418A mentions a preparation method of tungsten dioxide modified phenolic resin, tungsten dioxide improves the corrosion resistance and wear resistance of phenolic resin, but this method is difficult to measure due to the complicated preparation process and long preparation cycle production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene composite material and preparation method thereof
  • Polypropylene composite material and preparation method thereof
  • Polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] An embodiment of the polypropylene composite material of the present invention, the components of the polypropylene composite material in this embodiment are shown in Table 1.

[0030] The preparation method of polypropylene composite material described in this embodiment is:

[0031] (1) take each component by proportioning;

[0032] (2) Put tungsten disulfide nanorods, compatibilizers, polypropylene accounting for 30%-50% of the total polypropylene weight and processing aids accounting for 20%-40% of the total processing aid weight into the internal mixer for compaction Refining, then adopting the single-screw extruder extruding granulation that the length-to-diameter ratio of the extrusion screw is 20:1, obtains tungsten disulfide nanorod masterbatch;

[0033] (3) The remaining polypropylene, the tungsten disulfide nanorod masterbatch of step (2) gained, toughening agent, mineral filler, coloring agent and remaining processing aid are dropped into premixer successiv...

Embodiment 2～5

[0035] The components of the polypropylene composite materials described in Examples 2-5 are shown in Table 1, and the preparation methods of the polypropylene composite materials described in Examples 2-5 are the same as those in Example 1.

[0036] The polypropylene composite material described in Examples 1 to 5 is injection-molded into ISO mechanical splines and long plates of 200 × 5 × 2mm by injection molding machine, and then its tensile strength, flexural strength, notched impact strength, abrasion resistance and scratch resistance are measured. , surface Rockwell hardness and surface friction coefficient and other properties. The test results are shown in Table 1.

[0037] Among them, the test methods for each performance index are:

[0038] Tensile strength test standard is based on ISO 527-2, test conditions: temperature 23°C, tensile rate 50mm / min;

[0039] Bending strength test standard is based on ISO 178, test conditions: temperature 23°C, bending rate 2mm / min...

Embodiment 6

[0048] The content of tungsten disulfide nanorods in the polypropylene composite material of the present invention affects the performance of the polypropylene composite material. In order to investigate the influence of the content of tungsten disulfide nanorods on the performance of the polypropylene composite material, the applicant prepared according to the method of Example 1 The polypropylene composite materials of the test group and the control group were tested according to the performance test methods of the polypropylene composite materials described in the above-mentioned Examples 1-5, and the properties of the polypropylene composite materials of the test group and the control group in this embodiment were tested.

[0049] In this example, the components and properties of the polypropylene composite materials of the test group and the control group are shown in Table 2.

[0050] Table 2

[0051]

[0052] In the above Table 2, the polypropylene is PP EP548R, a co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to a polypropylene composite material and a preparation method thereof, and belongs to the technical field of a modified material. The polypropylene composite material is prepared from the following ingredients in parts by weight: 65 to 80 parts of polypropylene, 2 to 12 parts of tungsten disulfide nanometer rods and 1 to 8 parts of compatilizers. The specific content of tungsten disulfide nanometer rods are added into polypropylene substrates under the cooperated dispersion effect of the specific content of compatilizers, so that mutual friction is generated between WS2materials in the prepared polypropylene composite material; layered sliding is generated; the WS2 becomes thin and small through friction; small fragments fill the defects in the abrasion process, sothat the friction undulation is further reduced; the friction stability is enhanced. Therefore the anti-scratching performance and the intensity of the obtained polypropylene composite material are obviously improved.

Description

technical field [0001] The invention relates to a polypropylene composite material and a preparation method thereof, belonging to the technical field of modified materials. Background technique [0002] Polypropylene is widely used in industries such as automobiles, home appliances, packaging, and pipes because of its light weight and low price. However, due to its low surface hardness, large friction coefficient, low strength, low hardness, low surface polarity, and easy scratches. The use is subject to many restrictions, and people began to modify polypropylene according to the needs of use to meet the use in different fields. [0003] The currently used method is to add elastomer materials to the polypropylene matrix to improve the impact strength, and to improve the tensile strength, bending strength and bending modulus by introducing 10-40% talcum powder, mica powder, wollastonite, kaolin and other fillers. The amount of scratch resistance is improved by introducing sc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L53/00C08L23/14C08L51/06C08L23/08C08K13/04C08K7/00C08K3/30C08K5/134C08K3/04C08K3/36C08K3/26C08K3/34C08J3/22
CPCC08J3/226C08J2323/12C08J2323/14C08J2353/00C08J2423/12C08J2423/14C08J2453/00C08K2003/265C08K2003/3009C08K2201/011C08L23/12C08L23/14C08L53/00C08L2205/03C08L51/06C08L23/0815C08K13/04C08K7/00C08K3/30C08K5/1345C08K3/04C08K3/34C08K3/26C08K5/526C08K3/36
Inventor 丁鹏余启生周英辉袁刚黄朝亮万文平陆新
Owner WUHAN JINFA TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap