A kind of processing method of high-strength wood
A processing method and high-strength technology, applied in the field of material manufacturing, can solve problems such as obstacles and insufficient wood strength, and achieve the effects of good application prospects, easy implementation, and light volume and weight.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A kind of processing method of high-strength wood, step A, according to mass parts, with dried 100kg wood (the density of wood is 0.35g / cm 3 , the thickness is 5cm) in the reaction kettle, 500kg of water, make the water completely submerge the wood, heat the water to boiling, add 50kg of sodium hydroxide, 40kg of sodium metabisulfite and 10kg of calcium hydroxide after 5min and continue to boil for 10h After completing the reaction, drain the liquid, re-add 500kg of water, boil for 20min, and take out the wood after repeating twice.
[0021] Step B. Put the wood in a hot press, control the temperature at 110-105° C., press at 6 MPa, and press for 18 hours to obtain a high-strength wood.
[0022] Step C, after the wood is processed into the required shape, anticorrosion treatment is carried out by the brushing method.
[0023] The sample number is QW-1.
Embodiment 2
[0025] A kind of processing method of high-strength wood, step A, according to mass parts, with dried 125kg wood (the density of wood is 0.42g / cm 3 , the thickness is 10cm) in the reaction kettle, 750kg of water, make the water completely submerge the wood, heat the water to boiling, add 75kg of sodium hydroxide, 50kg of sodium metabisulfite and 12kg of calcium hydroxide after 8min and continue to boil for 12h ; After completing the reaction, drain the liquid, re-add 750°C of water, boil for 25 minutes, and take out the wood after repeating twice.
[0026] Step B. Put the wood in a hot press, control the temperature at 120-125° C., press at 7.5 MPa, and press for 15 hours to obtain a high-strength wood.
[0027] Step C, after the wood is processed into the required shape, anticorrosion treatment is carried out by diffusion method.
[0028] The sample number is QW-2.
Embodiment 3
[0030] A kind of processing method of high-strength wood, step A, according to mass parts, with dried 150kg wood (the density of wood is 0.45g / cm 3 , thickness is 12cm) in the reaction kettle, 1000kg of water, make the water completely submerge the wood, heat the water to boiling, add 100kg of sodium hydroxide, 60kg of sodium metabisulfite and 15kg of calcium hydroxide after 10min and continue to boil for 14h After completing the reaction, drain the liquid, add 1000kg of water again, boil for 30min, and take out the wood after repeating twice.
[0031] Step B. Put the wood in a hot press, control the temperature at 125-130° C., press at 9 MPa, and press for 12 hours to obtain a high-strength wood.
[0032] Step C, after processing the wood into the desired shape, carry out anti-corrosion treatment with hot and cold bath method.
[0033] The sample number is QW-3.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com