Novel chlorinated polyethylene rubber compound material and method for preparing same

A chlorinated polyethylene and rubber combination technology, applied in the field of chlorinated polyethylene combination new material and its preparation, can solve the problems of high cost, poor flame retardant performance, etc., achieve performance improvement, save dosage, and shorten plasticization time Effect

Active Publication Date: 2018-08-17
HANGZHOU KELI CHEM CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the rubber used for building sealing strips generally uses EPDM rubber. Ethylene-propylene rubber is a commonly used synthetic rubber. It has good we

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel chlorinated polyethylene rubber compound material and method for preparing same
  • Novel chlorinated polyethylene rubber compound material and method for preparing same
  • Novel chlorinated polyethylene rubber compound material and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1

[0025] A chlorinated polyethylene rubber composite new material, which is composed of: 100kg of rubber-type chlorinated polyethylene, 7kg of magnesium hydroxide, 35kg of semi-reinforced 774 carbon black, 60kg of 990 carbon black, 0.5kg of stearic acid, stearic acid Calcium 2kg, kaolin E2 15kg, dioctyl terephthalate 25kg, protective wax 0.5kg, antimony trioxide 4kg, thiadiazole vulcanizing agent ECHO S 8083M-504.5kg.

[0026] The preparation method of chlorinated polyethylene rubber sealing strip is:

[0027] (1) Weigh chlorinated polyethylene rubber and various additives according to the formula;

[0028] (2) Put the auxiliaries except the vulcanizing agent and the weighed chlorinated polyethylene rubber into the internal mixer, and control the rubber mixing temperature by cooling water to be less than or equal to 100 °C. After mixing for 3 minutes, add the vulcanizing agent and then After mixing for about 1.5 minutes, the material is discharged, and 4-5 t...

Example Embodiment

[0030]Example 2

[0031] A chlorinated polyethylene rubber composite new material, which is composed of: 100kg of rubber-type chlorinated polyethylene, 10kg of magnesium hydroxide, 40kg of semi-reinforced 774 carbon black, 70kg of 990 carbon black, 1kg of stearic acid, and 1kg of calcium stearate 3kg, kaolin E2 20kg, dioctyl terephthalate 32kg, protective wax 1kg, antimony trioxide 6kg, thiadiazole vulcanizing agent ECHO S 808 3M-505.5kg.

[0032] The preparation method of the chlorinated polyethylene rubber sealing strip is the same as that in Example 1.

Example Embodiment

[0033] Example 3

[0034] A chlorinated polyethylene rubber composite new material, which is composed of: rubber type chlorinated polyethylene 100kg, magnesium hydroxide 8.5kg, semi-reinforced 774 carbon black 37.5kg, 990 carbon black 65kg, stearic acid 0.75kg, hard Calcium fatty acid 2.5kg, kaolin E2 17.5kg, dioctyl terephthalate 28.5kg, protective wax 0.75kg, antimony trioxide 5kg, thiadiazole vulcanizing agent ECHOS808 3M-50 5kg.

[0035] The preparation method of the chlorinated polyethylene rubber sealing strip is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a novel chlorinated polyethylene rubber compound material, in particular to a novel chlorinated polyethylene rubber compound material for preparing sealing strips and a methodfor preparing the novel chlorinated polyethylene rubber compound material. The novel chlorinated polyethylene rubber compound material comprises, by weight, 100 parts of rubber-based chlorinated polyethylene, 7-10 parts of magnesium hydroxide, 35-40 parts of semi-reinforced 774 carbon black, 60-70 parts of 990 carbon black, 0.5-1 part of stearic acid, 2-3 parts of calcium stearate, 15-20 parts ofkaolin E2, 25-32 parts of dioctyl terephthalate, 4-6 parts of antimony trioxide, 0.5-1 part of protection wax and 4.5-5.5 parts of vulcanizing agents ECHOS 808 3M-50. The novel chlorinated polyethylene rubber compound material and the method have the advantage that the novel chlorinated polyethylene rubber compound material is excellent in ageing resistance, ozone resistance, flame retardance andmechanical property and low in cost and can be used for preparing the flame-retardant building sealing strips. The invention further provides a method for preparing the sealing strips.

Description

technical field [0001] The invention relates to a new composite material of chlorinated polyethylene rubber, more specifically, to a new composite material of chlorinated polyethylene used for preparing sealing strips and a preparation method thereof. Background technique [0002] Chlorinated polyethylene is an important polymer material prepared by chlorine substitution reaction of polyethylene, and can also be regarded as a terpolymer of ethylene, vinyl chloride and 1,2-dichloroethylene. According to its properties and uses, it can be divided into two categories: resin type products (CPE) and rubber type products (CM rubber). The former has higher relative molecular weight, mechanical strength, melting temperature and plasticizing temperature, and is mainly used for general purpose. Resin PVC, ABS, PP, PE and other weather resistance and impact modifiers; the latter has moderate mechanical strength and flexibility, low melt viscosity and plasticizing temperature, and is ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/28C08L91/06C08K13/02C08K5/12C08K5/09C08K3/04C08K3/34C08K5/47
CPCC08L23/286C08L2201/02C08L2201/08C08L91/06C08K13/02C08K5/12C08K5/09C08K3/04C08K3/346C08K5/47
Inventor 李玉平虢湘刿高旭东刘毓红孙锦伟
Owner HANGZHOU KELI CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap