A method for making a photoinduced energy storage fluorescent painting
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of photo-induced energy storage and production method, applied in the field of painting, can solve the problems of short storage time of the base material and multiple seasonings, etc., and achieve the effect of being beneficial to storage and improving water resistance.
Active Publication Date: 2020-05-15
麻鑫
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0007] The invention proposes a method for making photo-induced energy storage fluorescent paintings, which solves the problems that the existing fluorescent painting base materials need multiple seasonings and the storage time of the base materials is short
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] Use photo-induced energy storage luminous powder, natural pigments and binders as raw materials to make the base material, and use silk, paper, and cloth as the base for painting; the preparation steps of the base material are as follows:
[0029] (1) Add 20g of bovine bone glue to 70g of water, oscillate ultrasonically at 70°C for 12 hours, and boil to make a glue;
[0030] (2) Add photo-induced energy storage luminous powder and natural pigments to the glue solution obtained in step (1), the mass ratio of the glue solution, photo-induced energy storage luminous powder and natural pigments is 65:10:3, and ultrasonically disperse for 2 min , to get the bottom material.
Embodiment 2
[0032] Use photo-induced energy storage luminous powder, natural pigments and binders as raw materials to make the base material, and use silk, paper, and cloth as the base for painting; the preparation steps of the base material are as follows:
[0033] (1) Add 25g of bovine bone glue to 75g of water, oscillate ultrasonically at 80°C for 11 hours, and boil to make a glue;
[0034] (2) Add photo-induced energy storage luminous powder and natural pigments to the glue solution obtained in step (1), the mass ratio of the glue solution, photo-induced energy storage luminous powder and natural pigments is 70:12:8, and ultrasonically disperse for 4 min , to get the bottom material.
Embodiment 3
[0036] Use photo-induced energy storage luminous powder, natural pigments and binders as raw materials to make the base material, and use silk, paper, and cloth as the base for painting; the preparation steps of the base material are as follows:
[0037] (1) Add 30g of bovine bone glue to 80g of water, oscillate ultrasonically at 85°C for 12 hours, and boil to make a glue;
[0038] (2) Add photo-induced energy storage luminous powder and natural pigments to the glue solution obtained in step (1), the mass ratio of the glue solution, photo-induced energy storage luminous powder and natural pigments is 75:15:15, and ultrasonically disperse for 5 min , to get the bottom material.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides a production method of photo-induced energy-storage fluorescent drawings. Photo-induced energy-storage noctilucent powder, natural pigment and an adhesive are used as raw materials to produce a base material, and spun silk, paper and cloth are used as substrates for drawing, wherein a method for preparing the base material comprises the following steps that 1, an anionic surfactant is dissolved in n-butyl alcohol to form an oil phase solution; 2, cow glue is added into water, and through stirring, a collagen solution is obtained; 3, the photo-induced energy-storage noctilucent powder and the natural pigment are added into the collagen solution in the step 2, and through stirring, a pigment stock solution is obtained; 4, the pigment stock solution obtained in the step3 is added into the oil phase solution, and through ultrasonic concussion, a base material stock solution is obtained; 5, the base material stock solution obtained in the step 4 is subjected to spraydrying to obtain the base material. According to the production method of the photo-induced energy-storage fluorescent drawings, the anionic surfactant is used for preparing the oil phase solution, the prepared pigment stock solution is added into the oil phase solution, through ultrasonic concussion, oil phase molecules are broken, and then the pigment stock solution is evenly dispersed in the oil phase molecules to improve the water resistance of the pigment stock solution.
Description
technical field [0001] The invention relates to the field of painting, in particular to a method for making a photoinduced energy storage fluorescent painting. Background technique [0002] Photoinduced energy storage luminous powder (commonly known as luminous powder) is usually divided into two types: photoluminescent energy storage luminous powder and radioactive luminous powder. Photo-induced energy storage luminous powder is a photo-induced energy storage luminous powder that stores light energy after being irradiated by natural light, daylight, ultraviolet light, etc., and then slowly releases it in the form of fluorescence after stopping the light irradiation. At night or in dark places, the glow can still be seen, lasting for several hours to more than ten hours. [0003] Fluorescent painting, ordinary but not vulgar. It is to paint the adjusted luminous paste (not luminous paint) on the decoration of the city, the nave of the family, the door plaque, the signboard...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).