Method for detecting phosphate ions based on dual-emission europium metal-organic framework materials
A metal-organic framework and phosphate ion technology, which is applied in the direction of luminescent materials, analytical materials, material excitation analysis, etc., can solve the problems of expensive, ineffective analysis and detection, lengthy sample pretreatment, etc., and achieve low detection limit, good Application value, visible effect of detection process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] Synthesis and Characterization of Dual-Emitting Lanthanide Europium Metal-Organic Frameworks
[0041] 20.04 mg, 0.05 mmol / L of Eu(Ac) 3 ·4H 2 A mixture of O and 8.7 mg, 0.05 mmol / L of terphenyl-3,4ʹʹ,5-tricarboxylic acid was stirred in a mixed solution of 2 mL of deionized water and 4 mL of DMF for 0.5 h, and then 5 μL of 2 mol / L was added. HNO 3 . Subsequently, the obtained solution was transferred to a stainless steel autoclave with a polytetrafluoroethylene liner, heated at 120 °C for 48 hours, and cooled to 25 °C after 20 hours to obtain colorless bulk crystals. Ionized water and ether were washed several times. based on ligand H 3 Yield of L: 39%. The theoretical value (%) of elemental analysis of C45H35Eu2NO16 is: C 47.01, H 3.07, N 1.22; the measured value (%) is: C 47.31, H 3.29, N 1.38; it shows that the elemental composition is basically consistent with the theoretical value.
[0042] The structure and properties of the metal-organic framework prepared ...
Embodiment 2
[0050] A method for detecting phosphate ions based on dual-emitting europium metal-organic framework materials:
[0051] (1) The prepared dual-emission europium metal-organic framework material was uniformly dispersed in an aqueous solution to prepare a suspension solution with a concentration of 85 mg / L as the detection system, and 250 nm was used as the excitation wavelength. Fluorescence emission peak;
[0052] (2) Add the solution to be tested into the detection system and mix it evenly, let it stand still to ensure the interaction between the analyte and the material, and examine the changes of the fluorescence emission intensity at 368 nm and 614 nm respectively; the anion refers to the : Phosphate ion;
[0053] The general chemical formula of the dual-emitting europium metal-organic framework material used is: [Eu 2 (L) 2 (H 2 O) 2 (DMF) 2 ], L is terphenyl-3,4ʹʹ,5-tricarboxylic acid, as ligand, Eu 3+ As a metal center, the crystal structure belongs to monoclinic...
Embodiment 3
[0056] Determination of UV Absorption Spectrum and Fluorescence Emission Spectrum of Metal-Organic Framework Materials Used
[0057] The metal-organic framework material prepared in the above-mentioned Example 1 was dispersed in an aqueous solution, and the ultraviolet-visible absorption spectrum and fluorescence emission spectrum of the material were tested, as shown in the appendix. image 3 shows a broad absorption peak at 320 nm in the UV-Vis absorption spectrum of metal-organic framework materials, which is attributed to jump. Under excitation light, the metal-organic frameworks exhibited ligand- and Eu-based structures at 368 nm and 592-698 nm. 3+ Sharp feature emission. In the spectral emission band in the range 592-698 nm, the emission maximum is located at 614 nm and is assigned to 5 D 0 → 7 F 2 The electronic transition of , the side peaks are located at 592 nm ( 5 D 0 → 7 F 1 ), 650 nm ( 5 D 0 → 7 F 3 ) and 698 nm ( 5 D 0 → 7 F 4 ) at. To develop...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com