A paint finish polisher for new energy vehicles
A new energy vehicle and polishing agent technology, which is applied in the field of car beauty, can solve the problems of non-corrosion resistance, easy physical scratches and fading of the protective film, and achieve good anti-corrosion performance, long storage time and stable performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] A paint polishing agent for new energy vehicles, comprising the following components in parts by weight: 8 parts of microcrystalline wax, 7 parts of lauryl wax, 20 parts of ethylene glycol, 3 parts of sodium dodecylbenzenesulfonate, dimethyl 6 parts of base silicone oil, 4 parts of montmorillonite, 45 parts of water.
[0024] The preparation method of the above-mentioned paint polishing agent for new energy vehicles is carried out according to the following steps:
[0025] (1) According to the parts by weight, take 8 parts of microcrystalline wax and 7 parts of lauryl wax, mix and melt at 90°C;
[0026] (2) Take 20 parts of ethylene glycol, add it to the molten liquid prepared in step (1), and stir evenly;
[0027] (3) Take 3 parts of sodium dodecylbenzenesulfonate, 6 parts of simethicone, and 4 parts of montmorillonite, add them to the mixed solution prepared in step (2), and stir evenly;
[0028] (4) Cool down to room temperature, add 45 parts of water, stir evenly,...
Embodiment 2
[0030] A paint polishing agent for new energy vehicles, comprising the following components in parts by weight: 5 parts of microcrystalline wax, 5 parts of lauryl wax, 10 parts of liquid paraffin, 1 part of polyoxyethylene lauryl ether, and 3 parts of simethicone 3 parts, 3 parts of iron oxide, 30 parts of water.
[0031] The preparation method of the above-mentioned paint polishing agent for new energy vehicles is carried out according to the following steps:
[0032] (1) According to the parts by weight, take 5 parts of microcrystalline wax and 5 parts of lauryl wax, mix and melt at 80°C;
[0033] (2) Take 10 parts of liquid paraffin, add it to the molten liquid prepared in step (1), and stir evenly;
[0034] (3) Take 1 part of polyoxyethylene lauryl ether, 3 parts of simethicone, and 3 parts of iron oxide, add them to the mixed liquid prepared in step (2), and stir evenly;
[0035] (4) Cool down to room temperature, add 30 parts of water, stir evenly, and prepare.
Embodiment 3
[0037] A paint polishing agent for new energy vehicles, comprising the following components in parts by weight: 10 parts of microcrystalline wax, 10 parts of lauryl wax, 30 parts of ethanol, 5 parts of alkylphenol polyoxyethylene ether, and 8 parts of dimethyl silicone oil Parts, 5 parts of kaolin, 60 parts of water.
[0038] The preparation method of the above-mentioned paint polishing agent for new energy vehicles is carried out according to the following steps:
[0039] (1) According to the parts by weight, take 10 parts of microcrystalline wax and 10 parts of laurel wax, mix and melt at 100°C;
[0040] (2) Take 30 parts of ethanol, add it to the molten liquid prepared in step (1), and stir evenly;
[0041] (3) Take 5 parts of alkylphenol polyoxyethylene ether, 8 parts of simethicone, and 5 parts of kaolin, add them to the mixed solution prepared in step (2), and stir evenly;
[0042] (4) Cool down to room temperature, add 60 parts of water, stir evenly, and prepare.
PUM
Login to View More Abstract
Description