A prestressed steel strand, high temperature resistant technology, applied in textiles, papermaking, textile cables, etc., can solve the problems of brittle steel, difficult to promote in a large area, reduce the bonding stress between steel strands and concrete, and achieve good mechanical properties. performance effect

Active Publication Date: 2021-09-03
TONGJI UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The former method needs to change the existing steel casting process, which is difficult to promote in a large area, and the steel is prone to brittle fracture under low stress; the latter method will reduce the bonding stress between the steel strand and the concrete, and the fireproof coating is easy to Shedding under reciprocating loads such as earthquakes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high temperature resistant prestressed steel strand
  • A high temperature resistant prestressed steel strand
  • A high temperature resistant prestressed steel strand

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0019] A high temperature resistant prestressed steel strand, its structure is as follows figure 1 As shown, including the inner core 1 and the stranded wire 2 wound outside the inner core 1, the inner core 1 is a shape memory alloy inner core with a diameter of 5.25±0.05mm, and the austenite finishing temperature is 200-400°C. In the embodiment, the stranded wire 2 is provided with 6 strands of steel wires with a diameter of 5.07±0.05mm, and the stranded wires made of steel are used, which are spirally wound on the outside of the inner core.

[0020] Shape memory alloy (SMA) has a unique shape memory effect, and SMA will transform from martensite phase to austenite phase and return to the original shape at high temperature. If the traditional prestressed steel wire is stranded with SMA to make a steel strand, and prestress is applied to both ends, the SMA will produce considerable restoring force at high temperature, which can offset the prestress loss of the traditional stee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-temperature-resistant prestressed steel strand, which includes an inner core to wind the twisted wire outside the inner core, the inner core is made of a shape memory alloy material, and the twisted wire is provided with several strands in a spiral shape. Wrapped around the outside of the inner core. Compared with the prior art, the present invention uses an inner core made of SMA material. Under the induction of high temperature, SMA transforms from martensitic phase to austenite phase, returns to the original shape and generates prestress under the constraint, resulting in considerable The restoring force, so as to keep the prestress of the steel strand from being too low, and even increase it.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a high temperature resistant prestressed steel strand. Background technique [0002] According to statistics, it generally takes 2 hours for a building fire to be extinguished from the onset of the fire. At this time, the temperature of the prestressed tendons inside the prestressed concrete structure usually reaches nearly 400°C. Under the action of high temperature, traditional steel strands will not only deteriorate in strength and stiffness, but also cause serious prestress loss due to the high temperature creep of itself and concrete, which not only reduces the bearing capacity of the structure, but also accelerates the cracking and deformation of the structure. Cracking and deformation accelerate the high temperature of the fire to spread to the inside of the components, further aggravating the loss of prestress and structural deformation, thus forming a vicious circle, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D07B1/06D07B5/00
CPCD07B1/0673D07B5/005D07B2401/2035D07B2501/2015D07B5/006
Inventor 李凌志贾英琦刘兆乾包洪印余江滔
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products