Anti-cracking treatment method for salix integra

A treatment method and technology for the prevention of willow wormwood, applied in the direction of wood treatment, wood treatment details, reed/straw treatment, etc., can solve the problems of easy cracking of willow twig branches, affecting the performance and aesthetics of tallow willow products, affecting processing efficiency, etc., so as to shorten the processing time. time, the effect of improving weaving efficiency and yield, and improving commerciality

Inactive Publication Date: 2018-11-23
ANHUI HUAYU CRAFTS GRP
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to changes in temperature or humidity during weaving, willow branches are prone to cracking, which affects the performance and aesthetics of willow products. The existing treatment agents used to treat willow anti-cracking usually take 2-3 days to process, which affects processing efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An anti-cracking treatment method for Chinese wolfberry, comprising the following contents:

[0017] (1) Peel the bark willow, wash and disinfect it, and then soak it in an aqueous solution of sodium azide with a mass concentration of 0.9%. After soaking for 25 minutes, air-dry it in hot air at a temperature of 60°C until the surface becomes dry;

[0018] (2) Coat the willow willow after the above treatment with a treatment agent. After the coating is completed, in a warehouse with a temperature of 35°C and a humidity of 68%, the temperature is 55°C and the microwave power is 700w. After 25 minutes of treatment, the can be woven;

[0019] The treatment agent includes the following raw materials in parts by weight: 15 parts of polyvinyl acetate emulsion, 4 parts of amino silicone oil, 1.5 parts of hexamethyldisilazane, 0.7 part of p-toluenesulfonic acid, mercapto-containing siloxane coupling agent 2.5 parts, 12 parts of alcohol esters, 2 parts of isooctyl acrylate, and ...

Embodiment 2

[0027] An anti-cracking treatment method for Chinese wolfberry, comprising the following contents:

[0028] (1) Peel the bark willow, wash and disinfect it, and then soak it in an aqueous solution of sodium azide with a mass concentration of 0.6%. After soaking for 30 minutes, air-dry it in hot air at a temperature of 55°C until there is no water on the surface;

[0029] (2) Coat the willow willow after the above treatment with a treatment agent. After the coating is completed, in a warehouse with a temperature of 36°C and a humidity of 70%, the temperature is 60°C, and the microwave power is 600w. After 20 minutes of treatment, the can be woven;

[0030] The treatment agent includes the following raw materials in parts by weight: 18 parts of polyvinyl acetate emulsion, 5 parts of amino silicone oil, 2 parts of hexamethyldisilazane, 0.6 part of p-toluenesulfonic acid, mercapto-containing siloxane coupling agent 3 parts, 16 parts of alcohol ester twelve, 1 part of isooctyl acr...

Embodiment 3

[0038] An anti-cracking treatment method for Chinese wolfberry, comprising the following contents:

[0039] (1) Peel the bark willow, wash and disinfect it, and then soak it in an aqueous solution of sodium azide with a mass concentration of 1.2%. After soaking for 20 minutes, air-dry it in hot air at a temperature of 65°C until the surface becomes dry;

[0040] (2) Coat the willow bark after the above treatment with a treatment agent. After the coating is completed, treat it in a warehouse with a temperature of 34-36°C and a humidity of 65-70% at a temperature of 50°C and a microwave power of 800w. Weaving can be done after 30 minutes;

[0041] The treatment agent includes the following raw materials in parts by weight: 12 parts of polyvinyl acetate emulsion, 3 parts of amino silicone oil, 1 part of hexamethyldisilazane, 0.8 part of p-toluenesulfonic acid, mercapto-containing siloxane coupling agent 2 parts, 12 parts of alcohol ester twelve, 3 parts of isooctyl acrylate, 0.8...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of processing of salix integra, and particularly relates to an anti-cracking treatment method for salix integra. The anti-cracking treatment method comprises the following steps of peeling the salix integra, cleaning, and disinfecting; soaking by a sodium azide water solution with mass concentration of 0.6 to 1.2%, soaking for 20 to 30min, and drying byhot air at the temperature of 55 to 65 DEG C until the surface is free from water; coating the treated salix integra by a treatment agent, treating for 20 to 30min at the temperature of 50 to 60 DEGC and microwave power of 600 to 800w in a warehouse with temperature of 34 to 36 DEG C and humidity of 65 to 70%, and then weaving. Compared with the prior art, the anti-cracking treatment method hasthe advantages that the treatment method is scientific and reasonable, the treatment time is effectively shortened to one day or less, the cracking or deformation of the salix integra is effectively avoided, the weaving efficiency and finished rate are improved, and the commercial property of the salix integra product is improved.

Description

technical field [0001] The invention belongs to the technical field of bark willow processing, and in particular relates to a treatment method for bark willow to prevent cracking. Background technique [0002] Willow is one of the traditional Chinese handicrafts, rich in raw material resources and with a long history. Willow products are beautiful in appearance, low in price, green and environmentally friendly, and have good artistry and practicality. They are widely used in daily life, home decoration and art appreciation, etc., and are welcomed by consumers at home and abroad. The market prospect is good. Willow is a willow One of the main raw materials for making. [0003] Due to changes in temperature or humidity during weaving, willow branches are prone to cracking, which affects the performance and aesthetics of willow products. The existing treatment agents used to treat willow anti-cracking usually take 2-3 days to process, which affects processing efficiency. Con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/02B27K3/12B27K3/52B27K5/00B27K9/00
Inventor 王东营
Owner ANHUI HUAYU CRAFTS GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap