Amphiphilic chitosan-macadamia oil nano microcapsules and preparation method and application thereof

A technology of nano-microcapsules and chitosan, which is applied in the direction of micro-capsules, application, capsule delivery, etc., can solve the problems of restricting the application and development of macadamia nut oil, the instability of macadamia nut oil, and poor skin absorption effect, so as to achieve convenient storage Transportation and application, reducing volatility and photothermal instability, delaying the effect of volatilization rate

Active Publication Date: 2018-12-14
AGRI PRODS PROCESSING RES INST CHINESE ACAD OF TROPICAL AGRI SCI +1
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, macadamia nut oil is unstable at normal temperature and pressure, has low antioxidant capacity and is volatile
During storage, transportation and processing, macadamia nut oil is susceptible to oxidation and deterioration due to factors such as light and heat, and macadamia nut oil is directly applied to cosmetics. When the prepared product is applied to the surface of the skin, the skin absorption effect is poor, Fragrance time is short and other problems, the above problems seriously limit the application and development of macadamia nut oil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amphiphilic chitosan-macadamia oil nano microcapsules and preparation method and application thereof
  • Amphiphilic chitosan-macadamia oil nano microcapsules and preparation method and application thereof
  • Amphiphilic chitosan-macadamia oil nano microcapsules and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The preparation of embodiment 1 amphiphilic chitosan

[0043] (1) Get the chitosan that viscosity is not more than 200mPa.s, be configured into the chitosan aqueous solution that mass concentration is 1.0% with the glacial acetic acid aqueous solution of 1.0% with mass concentration; Get stearic acid, be configured with dehydrated alcohol into mass concentration Concentration is the ethanol solution of stearic acid of 2.0%;

[0044] (2) getting 1kg of the above-mentioned mass concentration of 1.0% chitosan aqueous solution and 1kg of the above-mentioned mass concentration of 2.0% stearic acid ethanol solution, mix, stir and add 10g of 1-ethyl-3-(3-di Methylaminopropyl) carbodiimide hydrochloride, at a temperature of 80°C and a stirring speed of 3000rpm, stirring and reacting for 3h, grafting stearic acid into chitosan molecules as a hydrophobic group to obtain hard Stearic acid grafted chitosan with fatty acid hydrophobic group grafting ratio of 5%;

[0045] (3) Step ...

Embodiment 2

[0048] The preparation of embodiment 2 amphiphilic chitosan

[0049] (1) Get the chitosan that viscosity is not more than 200mPa.s, be configured into the chitosan aqueous solution that mass concentration is 3.0% with the glacial acetic acid aqueous solution of 1.0% with mass concentration; Get stearic acid, be configured with dehydrated alcohol into mass concentration Concentration is the ethanol solution of stearic acid of 5.0%;

[0050] (2) getting 1kg of the above-mentioned mass concentration of 3.0% chitosan aqueous solution and 1kg of the above-mentioned mass concentration of 5.0% stearic acid ethanol solution, mix, stir and add 100g of 1-ethyl-3-(3-di Methylaminopropyl) carbodiimide hydrochloride, at a temperature of 80°C and a stirring speed of 1000rpm, stirring and reacting for 5h, grafting stearic acid into the chitosan molecule as a hydrophobic group to obtain hard Stearic acid grafted chitosan with fatty acid hydrophobic group grafting ratio of 20%;

[0051] (3) ...

Embodiment 3

[0052] The preparation of embodiment 3 amphiphilic chitosan

[0053] (1) Get the chitosan that viscosity is not more than 200mPa.s, be configured into the chitosan aqueous solution that mass concentration is 2.0% with the glacial acetic acid aqueous solution of 1.0% with mass concentration; Get stearic acid, be configured with dehydrated alcohol into mass concentration Concentration is the stearic acid ethanol solution of 3.0%;

[0054] (2) get 1kg above-mentioned mass concentration and be that the chitosan aqueous solution of 2.0% and 1kg above-mentioned mass concentration are the stearic acid ethanol solution of 3.0%, mix, add 80g of 1-ethyl-3-(3-di Methylaminopropyl) carbodiimide hydrochloride, at a temperature of 80°C and a stirring speed of 2000rpm, stirring and reacting for 4h, grafting stearic acid into the chitosan molecule as a hydrophobic group to obtain hard Stearic acid grafted chitosan with fatty acid hydrophobic group grafting ratio of 10%;

[0055] (3) Add 140...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
viscosityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an amphiphilic chitosan and its preparation. The amphiphilic chitosan is stearic acid, N-acetyl-L-cysteine grafted chitosan, and has a molecular weight of 10 to 300 kDa. The amphiphilic chitosan of the invention is used as a nano microcapsule embedding wall material, a hydrophobic substance can be embedded to form a water-soluble nano microcapsule solid, or can be used as the embedding wall material of a hydrophilic substance to form water-insoluble nano-capsules. The invention also discloses amphiphilic chitosan-macadamia oil nano microcapsules and a preparation methodand an application thereof. The nano microcapsule is formed by embedding a core material by the wall material, the core material is macadamia oil, and the wall material is the amphiphilic chitosan provided by the invention. The nano-microcapsules provided by the invention have the advantages of high embedding rate, good dispersibility and uniformity, and the macadamia oil has reduced volatility through embedding of the amphiphilic chitosan, and the stability and bioavailability are significantly improved.

Description

technical field [0001] The invention belongs to the technical field of modification of chitosan and preparation of nano-microcapsules, and specifically relates to amphiphilic chitosan and its preparation method, and amphiphilic chitosan-macadamia nut oil nano-microcapsules and its preparation method and application . Background technique [0002] Macadamia nut, also known as macadamia walnut, Queensland fruit, macadamia nut, etc., is a tree nut native to Australia. It has high nutritional value and medicinal value, and is known as the "king of dried fruits". The Chinese patent with the publication number CN103834470A discloses a method for extracting macadamia nut oil using subcritical extraction technology. Using subcritical extraction technology, under a certain pressure and temperature, the dried and crushed macadamia nuts are extracted multiple times to obtain high-quality oil. Quality Macadamia Nut Oil. In addition, macadamia nut oil can also be obtained by cold press...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K36/185A61K9/50A61K47/36A61K8/92A61K8/73A61K8/11A23L33/12A23P10/30A61P3/06A61P3/10A61P9/12A61Q19/02A61Q19/10
CPCA61K8/11A61K8/736A61K8/922A61K9/0095A61K9/5036A61K36/185A61Q19/02A61Q19/10A23L29/30A23L33/12A23P10/30A61P3/06A61P3/10A61P9/12
Inventor 杨子明李普旺李思东吕明哲陶金龙周闯王超何祖宇陈日志王慧
Owner AGRI PRODS PROCESSING RES INST CHINESE ACAD OF TROPICAL AGRI SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap