Method for preparing ultra-fine denier skin-affinity polyester filaments

A technology of polyester filament and production method is applied in the field of producing ultra-fine denier skin-friendly polyester filament, which can solve problems such as inability to meet the needs of consumers, and achieve the effects of strong product stability, easy operation and flattening.

Inactive Publication Date: 2018-12-18
JIANGSU DELI CHEM FIBER CO LTD
View PDF8 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The so-called polyester filament is a filament with a length of more than one kilometer, and the filament is wound into a ball. At present, the polyester filament on the market is mainly coarse denier fiber, and there are few fine denier fibers. Fiber is even rarer. With the improvement of living standards, the existing coarse denier fiber is difficult to meet the needs of consumers. In view of the above situation, the company successfully researched a super-soft and ultra-fine denier fiber on November 02, 2017. The preparation method of polyester filament is used to prepare ultra-soft and ultra-fine polyester filament, and an application for an invention patent was filed on November 02, 2017. After a long period of use, it was found that the ultra-soft and ultra-fine polyester filament prepared by this method The comfort, hand feel and visual or tactile effects of the fabrics processed from silk still have certain deficiencies, which cannot meet the needs of consumers. silk preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing ultra-fine denier skin-affinity polyester filaments
  • Method for preparing ultra-fine denier skin-affinity polyester filaments
  • Method for preparing ultra-fine denier skin-affinity polyester filaments

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Such as figure 1 As shown, the present invention discloses a production method for producing ultra-fine denier skin-friendly polyester filaments, which includes the following steps: (1) selecting POY precursors; (2) making the POY precursors in step (1) Carry out pre-grid; (3) Send the POY precursor treated in step (2) to the first wire feeding roller; (4) Send the POY precursor treated in step (3) into the first deformation heating box for deformation; (5) Put the POY raw silk treated in step (4) into the cooling plate to cool; (6) Send the POY raw silk treated in step (5) into the false twister for twisting; (7) Put the step (6) ) The treated POY precursors are sent to the second feeding roller; (8) The POY precursors treated in step (7) are networked; (9) The POY precursors treated in step (8) are sent to the second feeding roller; The second heat box for shaping; (10) Send the POY raw silk treated in step (9) to the third wire feeding roller; (11) Oil the POY raw s...

Embodiment 2

[0023] Such as figure 1As shown, the present invention discloses a production method for producing ultra-fine denier skin-friendly polyester filaments, which includes the following steps: (1) selecting POY precursors; (2) making the POY precursors in step (1) Carry out pre-grid; (3) Send the POY precursor treated in step (2) to the first wire feeding roller; (4) Send the POY precursor treated in step (3) into the first deformation heating box for deformation; (5) Put the POY raw silk treated in step (4) into the cooling plate to cool; (6) Send the POY raw silk treated in step (5) into the false twister for twisting; (7) Put the step (6) ) The treated POY precursors are sent to the second feeding roller; (8) The POY precursors treated in step (7) are networked; (9) The POY precursors treated in step (8) are sent to the second feeding roller; The second heat box for shaping; (10) Send the POY raw silk treated in step (9) to the third wire feeding roller; (11) Oil the POY raw si...

Embodiment 3

[0025] Such as figure 1 As shown, the present invention discloses a production method for producing ultra-fine denier skin-friendly polyester filaments, which includes the following steps: (1) selecting POY precursors; (2) making the POY precursors in step (1) Carry out pre-grid; (3) Send the POY precursor treated in step (2) to the first wire feeding roller; (4) Send the POY precursor treated in step (3) into the first deformation heating box for deformation; (5) Put the POY raw silk treated in step (4) into the cooling plate to cool; (6) Send the POY raw silk treated in step (5) into the false twister for twisting; (7) Put the step (6) ) The treated POY precursors are sent to the second feeding roller; (8) The POY precursors treated in step (7) are networked; (9) The POY precursors treated in step (8) are sent to the second feeding roller; The second heat box for shaping; (10) Send the POY raw silk treated in step (9) to the third wire feeding roller; (11) Oil the POY raw s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing ultra-fine denier skin-affinity polyester filaments. The method comprises the steps of POY precursors, pre-interlace, first feeding roller, first deformation heat box, cooling plate, false twister, second feeding roller, intermediate interlace, second heat box, third feeding roller, oiling roller, DTY winding shaping and spinning cake inspection, wherein the intermediate interlace procedure can be removed, the temperature of the first deformation heat box is 165 DEG C-175 DEG C, the temperature of the second heat box is 130 DEG C-140 DEG C, the draft ratio is 1.58-1.68, the false twist ratio is 1.66-1.80, and the interlace air pressure is 0.03-0.15 MPA. The method has the advantages of being simple and easy to operate, fabric prepared by polyester filaments prepared by means of the method has the advantages of being more flexible, good in comfort performance and strong in visual and tactile feeling.

Description

technical field [0001] The invention specifically relates to a preparation method for producing polyester filaments, in particular to a preparation method for producing superfine denier skin-friendly polyester filaments. Background technique [0002] Polyester filament is made of polyester filament. Polyester is an important variety of synthetic fibers and is the trade name of polyester fibers in my country. It is a fiber-forming high polymer prepared from purified terephthalic acid (PTA) or dimethyl terephthalate (DMT) and ethylene glycol (MEG) through esterification or transesterification and polycondensation. - Polyethylene terephthalate (PET), fibers made by spinning and post-processing. The so-called polyester filament is a filament with a length of more than one kilometer, and the filament is wound into a ball. At present, the polyester filament on the market is mainly coarse denier fiber, and there are few fine denier fibers. Fiber is even rarer. With the improveme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/02D02G3/34D02G1/02D02J13/00
CPCD02G3/02D02G1/0206D02G3/346D02J13/00D10B2331/04
Inventor 赵金广颜明郭皎范芹芹刘小雨张秉怀
Owner JIANGSU DELI CHEM FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap