A metal cleaning agent and defoamer technology, applied in the field of cleaning, can solve the problems of shortened cleaning agent life, reduced cleaning efficiency, easy foaming, etc., and achieve the effects of overcoming the long induction period, increasing the reaction rate, and increasing the electrophilicity

Active Publication Date: 2019-01-08
WUHAN SPACEFLIGHT SCI & TECH PETROCHEM CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, water-based metal cleaning agents are prone to foaming and residues. In severe cases, the foam overflows and takes away a large amount of surfactant, which shortens the life of the cleaning agent, and the foam will reduce the cleaning efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of low-foam metal cleaning agent
  • Preparation method of low-foam metal cleaning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The invention provides a kind of preparation method of low-foam metal cleaning agent, comprises the following steps:

[0029] Among them, the formula of low-foaming metal cleaning agent is: LAS10%-20%, oleic acid 8%-16%, triethanolamine 10%-18%, OP-102%-5%, benzotriazole 0.1%-0.3% , sodium carboxymethyl cellulose 0.1%-0.5%, STPP 0.5%-1.0%, sodium p-toluenesulfonate 0.5%-1.0%, polyether modified silicone type defoamer 5%-8%, antifoam Agent 2%-4%, water balance;

[0030] Wherein the preparation method of polyether modified silicone type defoamer is:

[0031] S1: Preparation of hydrogen-containing silicone oil: use 0.15g solid superacid to catalyze 10kg of hexamethyldisiloxane, 6kg of octamethylcyclotetrasiloxane, and 8kg of tetramethylcyclotetrasiloxane, and heat in a water bath for 35 ℃, reacted for 6 hours, and filtered to obtain hydrogen-containing silicone oil;

[0032] S2: Put 10 μg of platinum catalyst, 100 μg of polyethylene glycol 600, 20 g of ethyl acetate and...

Embodiment 2

[0036] The invention provides a kind of preparation method of low-foam metal cleaning agent, comprises the following steps:

[0037] Among them, the formula of low-foaming metal cleaning agent is: LAS10%-20%, oleic acid 8%-16%, triethanolamine 10%-18%, OP-102%-5%, benzotriazole 0.1%-0.3% , sodium carboxymethyl cellulose 0.1%-0.5%, STPP 0.5%-1.0%, sodium p-toluenesulfonate 0.5%-1.0%, polyether modified silicone type defoamer 5%-8%, antifoam Agent 2%-4%, water balance;

[0038] Wherein the preparation method of polyether modified silicone type defoamer is:

[0039] S1: Preparation of hydrogen-containing silicone oil: use 0.2g solid superacid to catalyze 10kg of hexamethyldisiloxane, 6kg of octamethylcyclotetrasiloxane, and 8kg of tetramethylcyclotetrasiloxane, and heat in a water bath for 35 ℃, reacted for 6 hours, and filtered to obtain hydrogen-containing silicone oil;

[0040] S2: Put 20 μg of platinum catalyst, 150 μg of polyethylene glycol 600, 35 g of ethyl acetate and ...

Embodiment 3

[0044] The invention provides a kind of preparation method of low-foam metal cleaning agent, comprises the following steps:

[0045] Among them, the formula of low-foaming metal cleaning agent is: LAS10%-20%, oleic acid 8%-16%, triethanolamine 10%-18%, OP-102%-5%, benzotriazole 0.1%-0.3% , sodium carboxymethyl cellulose 0.1%-0.5%, STPP 0.5%-1.0%, sodium p-toluenesulfonate 0.5%-1.0%, polyether modified silicone type defoamer 5%-8%, antifoam Agent 2%-4%, water balance;

[0046] Wherein the preparation method of polyether modified silicone type defoamer is:

[0047] S1: Preparation of hydrogen-containing silicone oil: use 0.25g solid superacid to catalyze 10kg of hexamethyldisiloxane, 6kg of octamethylcyclotetrasiloxane, and 8kg of tetramethylcyclotetrasiloxane, and heat in a water bath for 35 ℃, reacted for 6 hours, and filtered to obtain hydrogen-containing silicone oil;

[0048] S2: Put 30 μg of platinum catalyst, 200 μg of polyethylene glycol 600, 50 g of ethyl acetate and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a low-foam metal cleaning agent. The formula of the low-foam metal cleaning agent comprises 10 to 20 percent of LAS, 8 to 16 percent of oleic acid, 10 to18 percent of triethanolamine, 2 to 5 percent of OP-10, 0.1 to 0.3 percent of benzotriazole, 0.1 to 0.5 percent of sodium carboxymethylcellulose, 0.5 to 1.0 percent of STPP, 0.5 TO 1.0 percent of paratoluenesulfonic acid sodium salt, 5 to 8 percent of polyether modified organosilicone type defoaming agent, 2 to 4 percent of a foam inhibitor and the balance of water, wherein the preparation methodof the polyether modified organosilicone type defoaming agent comprises the steps of preparing hydrogen-containing silicone oil, preparing mixed liquid A and performing synthetic reaction to obtain viscous solid B, namely the polyether modified organosilicone type defoaming agent. The invention aims to provide the preparation method of the low-foam metal cleaning agent with small foam height andgood cleaning effect.

Description

technical field [0001] The invention relates to the technical field of cleaning, in particular to a preparation method of a low-foaming metal cleaning agent. Background technique [0002] After the metal workpiece is processed, the surface will carry dirt, such as various cutting fluids, guide rail oil, etc. If it is not cleaned, it will not only affect the smooth progress of the processing process, but also cause and accelerate the corrosion of the metal surface, affecting the processing quality and use of the product life. In addition, before finishing such as electroplating, phosphating (silanization), glaze coating, spray painting, etc., as well as in the repair and maintenance of mechanical equipment, the cleaning process is inseparable. The choice of cleaning process and the quality of the cleaning effect not only involve major issues such as safety, energy and environmental protection, but also directly affect the performance and quality of the product. Therefore, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(China)
IPC IPC(8): C23G1/24
CPCC23G1/24
Inventor倪维力喻翔彭钰珩袁婷婷沈东晓李松
OwnerWUHAN SPACEFLIGHT SCI & TECH PETROCHEM CO LTD