A kind of PVC adhesive tape and preparation method thereof

A tape and formula technology, applied in the direction of adhesives, film/sheet adhesives, coatings, etc., can solve the problems of wasting energy and time, affecting the performance of tapes, etc., to reduce tensile deformation, reduce processing time and Waste of energy, avoid the effect of uneven expansion

Active Publication Date: 2021-10-22
陈裕旺 +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the technical problem that release agent is transferred to the surface of glue in the preparation process of PVC adhesive tape in the prior art, waste energy and time and affect the technical problem of adhesive tape performance, the purpose of the present invention is to provide a kind of PVC adhesive tape and preparation method thereof, the present invention The method can not only avoid the transfer of the release agent, but also complete one-time processing while ensuring the performance of the adhesive tape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PVC adhesive tape and preparation method thereof
  • A kind of PVC adhesive tape and preparation method thereof
  • A kind of PVC adhesive tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of preparation method of PVC adhesive tape, its technological process is as image 3 shown, including steps:

[0052] (a) Coating acrylic pressure-sensitive adhesive on one side of the PVC film.

[0053] (b) coating the other side of the PVC film with a release agent that can be hardened by ultraviolet radiation;

[0054] The release agent formula is:

[0055] Silicone oil C715: 25wt%;

[0056] Silicone oil RC722: 70wt%;

[0057] Silicone oil A18: 2wt%;

[0058] The mixture of silicone oil and photoinitiator CD9051: 3wt%.

Embodiment 2

[0062] With reference to Example 1, the difference is that the release agent formula is:

[0063] Silicone oil C715: 40wt%;

[0064] Silicone oil RC722: 50wt%;

[0065] Silicone oil A18: 5wt%;

[0066] The mixture of silicone oil and photoinitiator CD905 1:5wt%.

Embodiment 3

[0068] With reference to Example 1, the difference is that the release agent formula is:

[0069] Silicone oil C715: 29wt%;

[0070] Silicone oil RC722: 69wt%;

[0071] Silicone oil A18: 2wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a PVC adhesive tape, which comprises the steps of: (a) coating a self-adhesive on one side of a PVC film; (b) coating a release agent that can be cured by ultraviolet radiation on the other side of the PVC film; ( c) drying by ultraviolet irradiation to harden the release agent. The method is to apply the self-adhesive first, then apply the release agent, and then use ultraviolet rays to harden the release agent. It can prevent the release agent from migrating due to the plasticizer in the PVC film due to high temperature, thereby affecting the adhesion of the release agent to the PVC film, and will not lose its catalytic effect due to the chlorine poisoning in the PVC film when using a platinum catalyst. The method of the present invention can complete the coating and drying of glue and release agent after one process, which can reduce the waste of processing time and energy, and also reduce the waste of transportation costs, and can also reduce the deformation of materials due to stretching during processing. , to avoid the problem of uneven horizontal expansion.

Description

technical field [0001] The invention belongs to the technical field of films, and in particular relates to a PVC adhesive tape and a preparation method thereof. Background technique [0002] figure 1 Shown is a PVC tape, which can be used as a low-cost protective film for chip dicing. The middle layer is a PVC film 1, the outer surface of the PVC film 1 is coated with a release agent 2, and the inner surface is coated with a glue 3. The process of making the PVC tape in China is as follows: figure 2 As shown, the PVC film imported from Japan and prepared with release treatment is used as raw material, and the self-adhesive is directly coated by the glue supply equipment, and then dried in an oven and then rolled. [0003] There is following shortcoming in above-mentioned processing step: [0004] 1. Because the PVC film imported from Japan is coated with release agent, the release agent will be aged and cracked after being heated in the oven during the glue coating proce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/40C09J7/24C09D183/04
CPCC08L2205/025C08L2205/03C08L2205/035C09D183/04C09J2433/00C09J7/245C09J7/401C09J2301/302C08L83/04
Inventor 陈裕旺
Owner 陈裕旺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap