Ultrathin slurry sprinkling and glazing process

A slurry-spraying and ultra-thin technology, applied in the field of building bricks, can solve the problems of rough inkjet pattern, poor anti-fouling ability, low wear resistance, etc., and achieve the effect of smooth and delicate touch, bright color and improved processing speed.

Inactive Publication Date: 2019-02-19
FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the ceramic tiles in the prior art have low wear resistance, poor antifouling ability, and high gloss, which is easy to cause environmental pollution. At present, the inkjet patterns of domestic enterprises are relatively rough and not fine enough. Therefore, the patterns made To be more refined and to win the favor of customers has always been the direction that enterprises strive for

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The present invention claims to protect an ultra-thin glazing process, which comprises the following steps:

[0029] Step (1), prepare the porcelain tile bottom blank, and set it aside. The composition ratio of the bottom billet is as follows, loss on ignition: 5.02%; silicon dioxide: 35.45%; aluminum oxide: 35.96%; calcium oxide: 10.44%; magnesium oxide: 3.67%; Sodium: 0.29%; Zinc Oxide: 0.89%; Zirconia: 4.56%.

[0030] Step (2), preparing flour paste, for subsequent use. First prepare W glaze slurry, which is composed by weight percentage: high-temperature matt transparent wear-resistant frit A: 57-61%; sub-surface transparent glaze B: 39-43%; water: 40-42%; carboxymethyl fiber Sodium plain: 0.2-0.3%; Sodium tripolyphosphate: 0.3-0.38%; The processing fineness of W glaze slurry can be 325 mesh, and the sieve residue is 0.2-0.6%. Then use W glaze slurry to prepare ultra-thin pouring slurry L glaze, that is, composite glaze slurry. The ingredients ratio of L glaze is...

Embodiment 2

[0041] It is known in the field that the choice of abrasive tools directly affects the final matte effect, and the fineness of the abrasive in each polishing process is also crucial. If the fineness is too fine, the finish will be higher without matte effect. If it is too thick, the smoothness will be low. Although the tiles with matte effect can be produced at this time, the product has a strong graininess and is prone to serious scratches, which makes the product particularly not resistant to stains. Therefore, during polishing The abrasive tools in each process must be strictly selected, and the fineness of the abrasives should also be carefully considered to make it just right.

[0042] This embodiment is mainly aimed at further research and development of the polishing process in Example 1. In Example 2, the soft polishing in Example 1 is used as the polishing process, which specifically includes three steps. The grinding tool of the grinding tool is polished, wherein the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an ultrathin slurry sprinkling and glazing process. The ultrathin slurry sprinkling and glazing process comprises the following steps: preparing a porcelain tile bottom blankfor subsequent use; preparing a face slurry for subsequent use; first-time drying: conveying the bottom blanks in a drying kiln at the temperature of 120-220 DEG C in a period of 60-100 minutes; second-time face slurry sprinkling and applying: carrying out second-time sprinkling and applying, sprinkling 16-22 g / m<2> water on the surfaces of the dried bottom blanks to arrive at a first-time slurrysprinkling position, carrying out waterfall type face slurry sprinkling and applying according to the use amount of 320-450 g / m<2>, and arriving at a second-time slurry sprinkling position about 10-20seconds of transmitting time later; second-time drying: conveying the blanks with the face slurry into the drying kiln at the temperature of 120-220 DEG C again in a drying period of 35-45 minutes; 3D full-color high-definition printing: spraying permeation ink and a permeation aid which are used for preparing digital patterns on the surfaces of the blanks with the dried face slurry layer according to a design file by a 3D full-color high-definition printing machine; firing: firing the blanks in a kiln of which the highest temperature reaches 1160-1220 DEG C in the period of 60-80 minutes; and cooling and polishing to obtain back-to-ancients finished bricks.

Description

technical field [0001] The invention relates to the field of building bricks, in particular to an ultra-thin slurry glazing process. Background technique [0002] Retro bricks have been developed in the Chinese market for several years. Taiwanese businessmen first brought this term into mainland China, and retro brick companies sprung up like mushrooms after rain. In the context of fierce competition in the market, ceramic enterprises and technicians, in addition to innovating in product design, pay more attention to product texture, surface hardness and surface flatness, and strive to reduce production costs. The color and appearance of retro bricks emphatically reflect the style of returning to nature, with rustic, rustic, and rough characteristics. The glazed surface is mostly matte. According to the development trend of globalization, its innovative design and innovative technology endow retro tiles with higher market value and vitality, requiring certain wear-resistant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/10C04B35/14C04B35/622C03C8/02C03C8/14C04B41/86
CPCC04B35/10C03C8/02C03C8/14C04B35/14C04B35/622C04B41/5022C04B41/86C04B2235/3201C04B2235/3206C04B2235/3208C04B2235/3244C04B2235/3284
Inventor 陈贤伟范新晖廖花妹林金宏肖春燕
Owner FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products