A functional and glaze technology, applied in the field of ceramic basic glaze, can solve problems such as hindering the application of negative ion material technology, and achieve the effects of improving wine quality, good process applicability, and accelerating aging speed.
Inactive Publication Date: 2019-03-19
吴鹃
View PDF5 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Nowadays, the tea sets, wine sets, and artistic porcelain that people use most in daily life are all ceramic products that are fired at medium and high temperatures and require high appearance quality. Therefore, the lack of this technology greatly hinders the application and development of negative ion material technology.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] Implementation column one:
[0016] The composition of the functional glaze materials is as follows: unit: wt%
[0017]
[0018] First, mix materials, ball mill, and pass through a 325-mesh sieve according to the composition in the above table to obtain a basic glaze with a moisture content of 50%;
[0019] Then apply the prepared glaze to the interior and surface of the ceramic body, the thickness of the glaze layer is 0.3mm, and after drying, it is fired in a kiln at 1180°C to obtain the health-preserving and environmental-friendly functional glaze of the present invention. The amount of negative ions emitted is 1500 / cm3.
[0020] Implementation column two:
[0021] The composition of the functional glaze materials is as follows: unit: wt%
[0022]
[0023] First, mix materials, ball mill, and pass through a 325-mesh sieve according to the composition in the above table to obtain a basic glaze with a moisture content of 50%;
[0024] Then apply the prepared ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a ceramic basic glaze with health regimen and environmental protection functions and a using method of the ceramic basic glaze. Natural mineral raw materials and industrial pure raw materials are adopted. The ceramic basic glaze with health regimen and environmental protection functions comprises the following components in percentages by weight: feldspar 30-55%, quartz 15-30%, calcite 10-25%, talcum 1-8%, barium carbonate 3-8%, strontium carbonate 1-3%, lithium carbonate 1-3%, zinc oxide 1-8%, rutile 1-8%, kaolin 3-8% and a negative ion generating agent 3-10%. The components are mixed, ball-milled and sieved to obtain the glaze. The glaze preparation process is the same as a common ceramic glaze process basically, the cost is low, by addition of different ceramicpigments, monochrome glaze, fancy glaze or transmutation glaze can be made, functionality and attractiveness of the made ceramic product are integrated, compared with products which have similar technical schemes in markets, the ceramic basic glaze is higher in practicality, higher in technical content and better in process applicability, and therefore, the application prospect is wide.
Description
technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a basic ceramic glaze with functions of health preservation and environmental protection and a use method thereof. Background technique [0002] Negative ion is a kind of far-infrared radiation material that is very beneficial to human health. The optimal wavelength of far-infrared rays suitable for human body absorption is 9.6 μm, while the wavelength of far-infrared rays radiated by negative ion mineral crystals is in the range of 2-18 μm, and the radiation power emission density is 0.04w / cm2 is slightly higher. The above data can fully prove that the far infrared rays radiated by negative ion mineral crystals are well coordinated with the human body and can be completely absorbed by the human body. Generally speaking, people need about 13 billion negative ions every day, but our living room, office, entertainment place and other environmen...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & AuthorityApplications(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86
Inventor吴鹃
Owner吴鹃