Lithium secondary cell and nonaqueous electrolytic solution for use therein

A technology of lithium secondary battery and non-aqueous electrolyte, which is applied in the field of high output lithium secondary battery and longevity, and can solve the problem of not being able to obtain output

Inactive Publication Date: 2019-07-12
MITSUBISHI CHEM CORP +1
View PDF52 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, sufficient output cannot be obtained yet, and further improvement is required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium secondary cell and nonaqueous electrolytic solution for use therein
  • Lithium secondary cell and nonaqueous electrolytic solution for use therein
  • Lithium secondary cell and nonaqueous electrolytic solution for use therein

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0798] The method for producing the above-mentioned amorphous carbonaceous material is not particularly limited as long as it does not exceed the scope of the present invention, and various methods can be mentioned. In the production of amorphous carbon, one heat treatment step is necessary, but the heat treatment may be divided into two or more times, and it is also preferable to perform various treatments before and after the heat treatment and / or in the middle of the heat treatment. The various treatments include pulverization, classification, and the above-mentioned crosslinking treatment, etc., and the pulverization and classification treatment may be performed at any one of the before, after, and intermediate stages of the heat treatment as long as it is in a solid state. The crosslinking treatment is preferably performed before or during the heat treatment. By performing these treatments, the specific surface area of ​​the negative electrode active material can be contr...

Embodiment

[1989] Hereinafter, although an Example and a comparative example are given and this invention is demonstrated more concretely, this invention is not limited to these Examples unless the summary of this invention is exceeded.

[1990] Positive electrode[1][Positive electrode active material]

[1991] The types and physical properties of positive electrode active materials used in the following Examples and Comparative Examples are as follows.

[1992] Positive electrode [1] Table 1

[1993] [Table 1]

[1994]

[1995] Positive electrode [1] In Table 1, as the physical properties of the positive electrode active material, BET specific surface area, average primary particle size (measured by SEM), median particle size d 50 , Determination of tap density.

[1996] [Positive electrode active material A]

[1997] The positive electrode active material A is a lithium transition metal composite oxide synthesized by the method shown below, with the composition formula LiMn 0.3...

Embodiment 2

[2025] It carried out similarly to positive electrode [1] Example 1 except having made electrolytic solution contain 0.3 mass % of trimethylsilyl methanesulfonate instead of hexamethylcyclotrisiloxane. The results of the battery evaluation are shown in Table 2 of the positive electrode [1].

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

A lithium secondary battery comprises: a positive electrode and a negative electrode which each has a specific composition and specific properties; and a nonaqueous electrolyte which contains a cyclicsiloxane compound represented by general formula (1), fluorosilane compound represented by general formula (2), compound represented by general formula (3), compound having an S-F bond in the molecule, nitric acid salt, nitrous acid salt, monofluorophosphoric acid salt, difluorophosphoric acid salt, acetic acid salt, or propionic acid salt in an amount of 10 ppm or more of the whole nonaqueous electrolyte. This lithium secondary battery has a high capacity, long life, and high output. In general formula (1), R 1 and R 2 are an organic group having 1-12 carbon atoms and n is an integer of 3-10. In general formula (2), R 3 to R 5 are an organic group having 1-12 carbon atoms; x is an integer of 1-3; and p, q, and r each are an integer of 0-3, provided that 1 p+q+r 3. In general formula (3),R 6 to R 8 are an organic group having 1-12 carbon atoms and symbol A is a group constituted of H, C, N, O, F, S, Si, and / or P.

Description

[0001] This application is a divisional application of the application with the filing date of October 19, 2006, the application number of 201410514981.1, and the title of the invention "lithium secondary battery and non-aqueous electrolyte used therein". technical field [0002] The present invention relates to a lithium secondary battery and a non-aqueous electrolytic solution used therein, more specifically, to a non-aqueous electrolytic solution for a lithium secondary battery containing specific components, and a non-aqueous electrolytic solution having a specific composition and physical properties capable of occluding and releasing lithium. positive and negative electrodes, and particularly lithium secondary batteries excellent in low-temperature discharge characteristics and high in capacity, long life, and high output, and nonaqueous electrolytic solutions used therein. Background technique [0003] In recent years, along with the miniaturization of electronic equipm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/131H01M4/133H01M4/587H01M10/0525H01M10/0567H01M10/0568H01M10/0569H01M4/02H01M4/134H01M4/36H01M10/0587H01M4/485H01M4/505H01M4/525H01M10/052H01M50/102H01M50/46
CPCH01M10/0525H01M10/0567H01M10/0569H01M4/131H01M4/134H01M4/133H01M4/364H01M4/587H01M10/0568H01M10/0587H01M2004/021H01M2300/0025H01M2300/004H01M2220/20Y02E60/10Y02P70/50
Inventor 宫城秀和加藤竜一横沟正和宇尾野宏之松本一志佐藤智洋古田土稔中岛孝之铃木仁大岛裕之
Owner MITSUBISHI CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com