Preparation method of natural antibacterial latex liner for underwear

A natural antibacterial and natural latex technology, applied in the field of natural rubber materials, can solve the problems of poor rubber mechanical properties and high protein content of natural latex, and achieve the effects of good anti-oxidation performance, improved curing performance and simple operation.

Inactive Publication Date: 2019-10-15
唐卫兵
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the natural latex has a high protein content and the prepared rubber has poor mechanical properties. There is still a long way to go to develop a high-performance natural antibacterial latex liner.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of preparation method of natural antibacterial latex pad for underwear, it is characterized in that, comprises the following steps:

[0020] (1) Mix natural rubber and water at a volume ratio of 1:1, add a total volume of 4% dedecyltrimethylammonium bromide-tetrahydrofuran supramolecular solvent to the mixture, ultrasonicate for 8 min, filter, and The filtrate is freeze-dried to obtain natural latex;

[0021] (2) Dissolve chitosan in 1.5% acetic acid-water mixture, add 30 parts of natural latex, 8 parts of nano-cellulose, 4 parts of nano-silicon dioxide, 4 parts of glutaraldehyde, After 3 parts of tetraalkyltriethoxysilane, react at 600 rpm, 50 °C for 1.5 h, filter, freeze-dry and pulverize to obtain natural latex masterbatch;

[0022] (3) Mix 77 parts of natural latex masterbatch, 1 part of Coptidis alcohol extract, 2 parts of garlic alcohol extract, 1 part of aloe alcohol extract, 3 parts of aloe water extract, 8 parts of nano-silica, and 8 parts of water at h...

Embodiment 2

[0024] A kind of preparation method of natural antibacterial latex pad for underwear, it is characterized in that, comprises the following steps:

[0025] (1) Mix natural rubber and water at a volume ratio of 1:1, add a total volume of 3.5% dedecyltriethylammonium bromide-tetrahydrofuran supramolecular solvent to the mixed solution, and ultrasonically filter for 10 min. The filtrate is freeze-dried to obtain natural latex;

[0026] (2) Dissolve chitosan in 2% acetic acid-water mixture, add 25 parts of natural latex, 5 parts of nanocellulose, 3 parts of nano-silicon dioxide, 2 parts of glutaraldehyde, After 3 parts of hexaalkyltriethoxysilane, react at 650 rpm, 60 °C for 2 h, filter, freeze-dry and pulverize to obtain natural latex masterbatch;

[0027] (3) Mix 83 parts of natural latex masterbatch, 1 part of coptis alcohol extract, 1 part of garlic alcohol extract, 1 part of aloe alcohol extract, 4 parts of grape seed alcohol extract, 5 parts of nano silicon dioxide, 5 parts ...

Embodiment 3

[0029] A kind of preparation method of natural antibacterial latex pad for underwear, it is characterized in that, comprises the following steps:

[0030] (1) Mix natural rubber and water at a volume ratio of 1:1, add a total volume of 4% dodecyltrimethylammonium bromide-tetrahydrofuran supramolecular solvent to the mixture, and filter it after ultrasonication for 10 min. The filtrate is freeze-dried to obtain natural latex;

[0031] (2) Dissolve chitosan in 2.5% acetic acid-water mixture, add 25 parts of natural latex, 8 parts of nanocellulose, 4 parts of nano calcium carbonate, 3 parts of glutaraldehyde, 4 parts of After parting of hexaalkyltrimethoxysilane, react at 700 rpm, 65°C for 3 h, filter, freeze-dry and pulverize to obtain natural latex masterbatch;

[0032] (3) Mix 78 parts of natural latex masterbatch, 1 part of Coptidis alcohol extract, 1 part of garlic alcohol extract, 1 part of aloe alcohol extract, 4 parts of tea alcohol extract, 10 parts of nano silicon diox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of natural rubber materials, and concretely relates to a preparation method of a natural antibacterial latex liner for underwear. The preparation method comprises the following steps: mixing natural rubber with water, adding a supramolecular solvent to the mixed solution, removing proteins, and performing freeze drying to obtain a natural latex; dissolving chitosan in an acetic acid-water mixed solution, adding natural latex, nano-cellulose, an inorganic filler, glutaraldehyde and a silane modifier, carrying out a reaction, filtering the obtained solution, and performing freeze drying to obtain a natural latex master batch; and performing high-speed stirring and mixing on the natural latex master batch, a natural antibacterial agent, an oxidant,nano-silica and a punching agent, heating and melting the obtained mixture at 100-150 DEG C, injecting the melted mixture into a grinding tool, carrying out curing molding, keeping the temperature at60-75 DEG C for 2-4 h, and cooling, washing and drying the cured mixture to obtain the natural antibacterial latex liner for underwear. The method of the invention is simple to operate, and the prepared latex liner has the advantages of soft texture, excellent mechanical properties, good air permeability and good antibacterial and anti-oxidation properties.

Description

technical field [0001] The invention relates to the technical field of natural rubber materials, in particular to a preparation method of a natural antibacterial latex pad for underwear. Background technique [0002] Natural latex is milky white liquid that flows out from rubber trees of a certain age when they are tapped. Fresh natural latex mainly contains rubber, protein, natural resin, sugar and so on. As a renewable polymer material, natural latex is favored by the rubber industry due to its rich sources and cheap price, anti-mite and anti-bacterial properties, good air permeability, excellent film-forming properties, elasticity and mechanical properties. At present, natural latex is mainly used to make sponge products, extruded products and impregnated products. The natural latex raw material is very soft, which makes latex an ideal material for clothing, especially underwear. But natural latex has many nutrients, although the natural components in the latex have ce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/02C08L5/08C08L1/02C08K13/02C08K5/00C08K3/36C08K5/07C08K5/5419C08J9/12C08J9/14
CPCC08J9/0014C08J9/0023C08J9/0061C08J9/0066C08J9/125C08J9/142C08J2203/10C08J2203/12C08J2307/02C08J2401/02C08J2405/08C08K3/36C08K5/0058C08K5/07C08K5/5419C08K13/02C08K2201/011
Inventor 唐卫兵
Owner 唐卫兵
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka