Diamond rope saw bead added with cubic boron nitride and preparation process of diamond rope saw

A cubic boron nitride and diamond wire saw technology, which is applied in the manufacture of tools, metal processing, stone processing equipment, etc., can solve the problems affecting sharpness, cutting effect and service life, loss of diamond cutting ability, and fast wear of wire saws, etc. , to achieve the effects of reducing the difficulty of coating, enhancing wear resistance and improving performance

Active Publication Date: 2019-10-18
石家庄海川工具有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the beads are mainly made of diamond materials. Diamond is mainly used in the processing of hard and brittle materials such as cemented carbide, glass, ceramics, stone, concrete, and building materials. Because diamond has an obvious affinity for iron and carbon at high temperatures, it can be used in diamond When the wire saw cuts iron materials at high speed, the high temperature generated will easily graphitize the diamond and form iron carbides, causing the diamond to lose its cutting ability, which will cause the wire saw to wear quickly, affecting the sharpness, cutting effect and service life. , so the diamond wire saw is not suitable for cutting metal materials such as steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diamond rope saw bead added with cubic boron nitride and preparation process of diamond rope saw
  • Diamond rope saw bead added with cubic boron nitride and preparation process of diamond rope saw
  • Diamond rope saw bead added with cubic boron nitride and preparation process of diamond rope saw

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This embodiment relates to a diamond wire saw bead added with cubic boron nitride and a preparation process of the diamond wire saw.

[0037] A diamond wire saw bead, comprising the following raw material components in parts by mass:

[0038] 91-95 parts of metal powder, 0.5-2.5 parts of diamond, 1.5-5.3 parts of cubic boron nitride; the particle size of the metal powder is 200-400 mesh, the particle size of the diamond is 25-60 mesh, and the cubic boron nitride The particle size of boron is 25-60 mesh;

[0039] Among them, every hundred parts of metal powder includes the following mass powder raw material components: 25-45 parts of FeCu30 pre-alloyed powder, 5-10 parts of FeCu20 pre-alloyed powder, 30-45 parts of CuSn15 pre-alloyed powder, 5-10 parts of am1 alloyed powder , 10-15 parts of cobalt powder, 10-15 parts of tungsten carbide powder; the particle size of the FeCu30 pre-alloy powder, FeCu20 pre-alloy powder, CuSn15 pre-alloy powder, am1 alloy powder, cobalt po...

Embodiment 2

[0056] This embodiment relates to the use effect of the diamond wire saw.

[0057] The performance of the diamond wire saw prepared in Examples 1.1 to 1.4 is tested, and its use effect is tested as follows:

[0058] The diamond wire saw obtained in Example 1.1 has a cutting power of 22kw, and the sample specification is: φ11.5mm beads, 50m, 40 beads per meter. Test the diamond wire saw obtained by using a test block (c40 cement, containing 8 18mm steel bars per square meter), and its cutting speed can reach 25min / m 2 , service life up to 230m 2 .

[0059] The diamond wire saw obtained in Example 1.2 has a cutting power of 22kw, and the sample specification is: φ11.5mm beads, 50m, 40 beads per meter. Test the diamond wire saw obtained by using a test block (c40 cement, containing 8 18mm steel bars per square meter), and its cutting speed can reach 22min / m 2 , service life up to 235m 2 .

[0060] The diamond wire saw obtained in Example 1.3 has a cutter power of 22kw, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a diamond rope saw bead added with cubic boron nitride. The diamond rope saw bead is prepared from metal powder, diamond, cubic boron nitride and the like, wherein the metal powder comprises FeCu30 pre-alloyed powder, FeCu20 pre-alloyed powder, CuSn15 pre-alloyed powder, am1 alloy powder, cobalt powder and tungsten carbide powder. The mode of coating diamond and cubic boronnitride with a covering agent and then blending the coated body with the metal powder is adopted for adding of the cubic boron nitride. The obtained diamond rope saw bead not only has the property advantages of being good in abrasive resistance, high in toughness, high in heat stability and the like, the service life of a diamond rope saw is greatly prolonged, the cutting hardness of the diamondrope saw is greatly improved, and the cutting speed of the diamond rope saw is greatly increased. In addition, according to a preparation process of the diamond rope saw, the special coating process is adopted for coating the diamond and cubic boron nitride to form a composite, and then the composite is blended with the metal powder and treatment conditions are limited, so that the high quality and high performance of the diamond rope saw are guaranteed. The preparation process is convenient, safe, high in production efficiency and low, and the products are excellent and stable in quality.

Description

technical field [0001] The invention relates to the technical field of diamond wire saws, in particular to a diamond wire saw bead added with cubic boron nitride and a preparation process of the diamond wire saw. Background technique [0002] Diamond wire saw is a tool for cutting various hard materials, mainly used in stone mining, block shaping, concrete, plate cutting and forming cutting processing; and beading is an important part of diamond wire saw. The component is a cutting body with a steel wire rope as a carrier. [0003] At present, most of the beads are mainly made of diamond materials. Diamond is mainly used in the processing of hard and brittle materials such as cemented carbide, glass, ceramics, stone, concrete, and building materials. Because diamond has an obvious affinity for iron and carbon at high temperatures, it can be used in diamond When the wire saw cuts iron materials at high speed, the high temperature generated will easily graphitize the diamond ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00B22F3/02B22F3/10B22F5/00C22C26/00C22C32/00B28D1/08B24D99/00B24D18/00
CPCB22F3/02B22F3/10B22F5/00C22C26/00C22C32/0047B28D1/08B24D99/00B24D18/0009B24D18/00C22C2026/007C22C2026/006B22F2005/001B22F1/052B22F1/10
Inventor 栾会生刘冰马永德
Owner 石家庄海川工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap