High sensitivity mobile phone protection screen full lamination adhesive and preparation method thereof

A mobile phone protection and high-sensitivity technology, applied in the direction of modified epoxy resin adhesives, adhesives, adhesive types, etc., can solve the problem of 100% bonding of curved screens, high difficulty of bonding protective films, and constraints on development And other problems, to achieve the effect of shortening the sizing time, good peeling characteristics, and convenient transmission of ultrasound

Inactive Publication Date: 2019-11-08
河源然生新材料有限公司
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional pressure-sensitive adhesives are gradually eliminated by the market due to their strong smell, not being environmentally friendly, not easy to store, and difficult to attach protective films
However, liquid silicone is unable to achieve 100% fit on curved screens, which hinders its development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High sensitivity mobile phone protection screen full lamination adhesive and preparation method thereof
  • High sensitivity mobile phone protection screen full lamination adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] like figure 1 As shown, the preparation method of the high-sensitivity mobile phone protective screen full-fit adhesive of the present invention comprises the following steps:

[0024] S1, acrylate active monomer and photoinitiator are heated and mixed;

[0025] S2, add oligomer, polymerization inhibitor and leveling agent again, stir and mix;

[0026] S3, add wetting agent again;

[0027] S4, filter the mixture to obtain the finished product.

[0028] In step S1, the heating and mixing temperature is 40-50°C, and stirring is carried out at 1200-2000r / min for 40-45min; the stirring time in step S2 is 30-45min, and the stirring time in step S3 is 10-15min; In step S4, a 300-mesh filter is used to filter the mixture, and the filtrate is packaged to obtain the full bonding adhesive for the mobile phone screen protective film.

[0029] In addition, in the preparation method of the high-sensitivity mobile phone protective screen full-fit adhesive of the present invention...

Embodiment 1

[0040] A method for preparing a high-sensitivity mobile phone protective screen full-fit adhesive. Calculated by mass fraction, first weigh 8% acryloylmorpholine, 8% isobornyl acrylate, 32% ethoxyethoxyethyl acrylate, Mix 32% 2-phenoxyethyl acrylate, 2% acyl phosphine oxide and 2% benzoin, heat to 40-50°C, and stir at 1200-2000r / min for 40-45min. Then add 7% urethane acrylate oligomer, 3% polyether acrylate oligomer, 4% epoxy acrylate oligomer and 0.8% polymerization inhibitor in turn, after stirring for 20-30min, add 0.1% moistening The aerosol and 0.1% leveling agent are stirred for 10-15 minutes, filtered through a 300-mesh filter, and the filtrate is packaged to obtain a full-fit adhesive for the mobile phone protective screen. The properties of the obtained mobile phone protective screen full-fit glue are as follows:

[0041]

[0042] Compared with the prior art, the present invention has the following beneficial effects: the proportion of oligomer is low, so that the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high sensitivity mobile phone protection screen full lamination adhesive and a preparation method thereof. The high sensitivity mobile phone protection screen full laminationadhesive comprises, by mass fraction, 10-20% of an oligomer, 70-90% of an acrylate active monomer, 2-6% of a photoinitiator and 1-3% of assistants. The high sensitivity mobile phone protection screenfull lamination adhesive provided by the invention not only has the characteristics of high sensitivity, high transparency, low odor, high lamination degree, environmental protection, etc., also is not added with any solvent, has heavy metal, toluene, formaldehyde, methanol meeting the EU ROSH and REACH standards, and has good peeling performance.

Description

technical field [0001] The invention belongs to the technical field of chemical products, and relates to a mobile phone protective screen fully laminating glue, in particular to a high-sensitivity mobile phone protective screen fully laminating glue and a preparation method thereof. Background technique [0002] Mobile phone screen protective film, also known as mobile phone beauty film and mobile phone protective film, is a cold lamination film used for mounting mobile phone screens. From the initial simple anti-scratch protective film to the introduction of functional protective film series, it can be divided into: anti-peeping film, AR film, frosted film, high-definition film, anti-scratch protective film, 3D film, tempered film, etc. Zhengdao mobile phone film can protect Eyesight, no damage to eyes, multi-layer protection, effectively block ultraviolet rays, short-wave blue rays, soft glare light source stimulation, attached with AF coating, so that the phone's film fee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/14C09J171/00C09J163/10C09J7/30
CPCC09J175/14C09J7/30C08L71/00C08L63/10
Inventor 欧龙生李超邹名超
Owner 河源然生新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap