A kind of preparation method of seawater desalination material based on polyurethane foam

A polyurethane foam, polyaniline technology, applied in chemical instruments and methods, seawater treatment, general water supply conservation, etc., can solve the problems of low desalination efficiency of seawater desalination materials, etc. The effect of tangential resistance

Active Publication Date: 2021-12-31
HARBIN INST OF TECH AT WEIHAI +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem of low desalination efficiency of the seawater desalination material prepared by the existing method using photothermal conversion, and to provide a preparation method of the seawater desalination material based on polyurethane foam

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of seawater desalination material based on polyurethane foam

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0014] Embodiment 1: This embodiment is a preparation method of a polyurethane foam-based seawater desalination material, which is specifically prepared according to the following steps:

[0015] 1. Preparation of ammonium persulfate (A) and aniline (B) solutions: First, dissolve 10-15 g of ammonium persulfate in 300-500 ml of deionized water, and record it as solution A. Then, add 5-10 ml of aniline into 600-1000 ml of deionized water, and ultrasonically treat it for 90-120 min to completely dissolve it, which is recorded as solution B;

[0016] 2. Preparation of polyaniline powder: Add solution A and solution B in (1) into a beaker containing 3 L of 1.0-2.0 M HCl in turn under stirring, react for 5 minutes and then filter. Then, wash with deionized water and filter 3 times to obtain polyaniline powder. Finally, put the obtained polyaniline powder into an oven at 50-70°C and dry for 48-96 h to obtain polyaniline powder;

[0017] 3. Preparation of polyaniline solution: Add 0...

specific Embodiment approach 2

[0025] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the polyaniline in step 3 has a mass of 0.5-1.5 g. . Others are the same as the first embodiment.

specific Embodiment approach 3

[0026] Embodiment 3: This embodiment differs from Embodiment 1 or Embodiment 2 in that: the quality of the polyvinyl alcohol powder described in Step 4 is 25-35 g. Others are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a polyurethane foam-based seawater desalination material, which relates to a preparation method of the material. The purpose of the invention is to solve the problem of low desalination efficiency of the seawater desalination material prepared by the existing method using photothermal conversion. Method: 1. Preparation of ammonium persulfate and aniline solution; 2. Preparation of polyaniline powder; 3. Preparation of polyaniline solution; 4. Preparation of polyvinyl alcohol solution; 5. Preparation of crude seawater desalination material based on polyurethane foam; 6. Optimizing treatment , that is, a polyurethane foam-based seawater desalination material is obtained. The nano-channels capable of sufficient pore structure of the polyurethane foam material and the polyvinyl alcohol gel prepared by the invention can effectively reduce the latent heat of evaporation of water and greatly improve the efficiency of seawater desalination. The seawater desalination material has a high seawater evaporation rate (2.0kg m ‑2 h ‑1 ) and desalination efficiency (99.9%), compared with traditional photothermal conversion seawater desalination materials, increased by 25%.

Description

technical field [0001] The invention relates to a preparation method of seawater desalination material. Background technique [0002] Demand for freshwater resources is increasing due to rising population growth rates and improved living standards, as well as expansion of industrial and agricultural activities. Existing fresh water resources such as rivers and groundwater are limited. Facing the ever-increasing demand for fresh water, many cities are facing a water shortage crisis. However, the earth is rich in water resources, but the seawater has a high salt content, which is not suitable for human use, nor is it suitable for industrial and agricultural use. In order to realize the desalination of seawater to produce fresh water, over the years, a variety of desalination technologies have been developed on the basis of technologies such as multi-effect evaporation, membrane separation, freezing, and electrodialysis, among which the two most important technologies are base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/04C08L29/04C08L79/02C08J9/28C02F1/14C02F103/08
CPCC08J9/28C02F1/048C02F1/14C08J2375/04C08J2429/04C08J2479/02C02F2103/08Y02A20/142Y02A20/212Y02A20/124
Inventor 程喜全黄军辉王凯张瑛洁
Owner HARBIN INST OF TECH AT WEIHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap