A graphene-based wallpaper

An alkenyl-based wallpaper, graphene technology, applied in the direction of home wall, other home appliances, chemical instruments and methods, etc., to reduce power consumption, reduce the demand for current, and improve the safety of use

Active Publication Date: 2021-04-06
浙江捷信纺织科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems in the prior art, the present invention provides a graphene-based wallpaper, which solves the blank of the existing wallpaper in terms of environmental protection and heating. The combination of the graphene resistance layer and the heat-conducting purification layer forms a micro-current heating effect and has negative ions. Purifying wallpapers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A graphene-based wallpaper
  • A graphene-based wallpaper
  • A graphene-based wallpaper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A graphene-based wallpaper, comprising a graphene resistance layer and a thermally conductive purification layer,

[0036] The formula of described graphene resistance layer is as follows:

[0037] 30 parts of graphene, 10 parts of PVC material, 5 parts of ethyl cellulose, 30 parts of absolute ethanol;

[0038] The formula of the heat conduction purification layer is as follows:

[0039] 10 parts of tourmaline powder, 20 parts of thermal silica gel, 10 parts of nano-alumina, 5 parts of methyl cellulose, 20 parts of distilled water.

[0040] The preparation method of described graphene resistance layer is as follows:

[0041] Step 1, adding ethyl cellulose to absolute ethanol and ultrasonically reacting for 20 minutes to obtain a dispersed ethanol liquid;

[0042] Step 2, adding graphene and PVC to the dispersed ethanol solution for 20 minutes of ultrasonication and microwave reaction for 2 hours to obtain a suspension;

[0043] Step 3, spray the suspension evenly on...

Embodiment 2

[0056] A graphene-based wallpaper, comprising a graphene resistance layer and a thermally conductive purification layer,

[0057] The formula of described graphene resistance layer is as follows:

[0058] 50 parts of graphene, 15 parts of PVC material, 8 parts of ethyl cellulose, 50 parts of absolute ethanol;

[0059] The formula of the heat conduction purification layer is as follows:

[0060] 20 parts of tourmaline powder, 30 parts of thermal silica gel, 15 parts of nano-alumina, 8 parts of methyl cellulose, 40 parts of distilled water.

[0061] The preparation method of described graphene resistance layer is as follows:

[0062] Step 1, adding ethyl cellulose to absolute ethanol and ultrasonically reacting for 50 minutes to obtain a dispersed ethanol liquid;

[0063] Step 2, adding graphene and PVC to the dispersed ethanol solution for 50 minutes of ultrasonication and microwave reaction for 4 hours to obtain a suspension;

[0064] Step 3: Spray the suspension evenly on t...

Embodiment 3

[0077] A graphene-based wallpaper, comprising a graphene resistance layer and a thermally conductive purification layer,

[0078] The formula of described graphene resistance layer is as follows:

[0079] 40 parts of graphene, 13 parts of PVC material, 7 parts of ethyl cellulose, 40 parts of absolute ethanol;

[0080] The formula of the heat conduction purification layer is as follows:

[0081] 15 parts of tourmaline powder, 25 parts of thermal silica gel, 13 parts of nano-alumina, 7 parts of methyl cellulose, 30 parts of distilled water.

[0082] The preparation method of described graphene resistance layer is as follows:

[0083] Step 1, adding ethyl cellulose to absolute ethanol and ultrasonically reacting for 40 minutes to obtain a dispersed ethanol liquid;

[0084] Step 2, adding graphene and PVC to the dispersed ethanol solution for 40 minutes of ultrasonication and microwave reaction for 3 hours to obtain a suspension;

[0085] Step 3: Spray the suspension evenly on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of wallpaper, and specifically relates to a graphene-based wallpaper, comprising a graphene resistance layer and a heat-conducting purification layer. The formula of the graphene resistance layer is as follows: 30-50 parts of graphene, 10-15 parts of PVC material, B 5-8 parts of base cellulose, 30-50 parts of absolute ethanol; the formula of the heat-conducting purification layer is as follows: 10-20 parts of tourmaline powder, 20-30 parts of heat-conducting silica gel, 10-15 parts of nano-alumina, methyl cellulose 5-8 parts of vegetarian food, 20-40 parts of distilled water. The invention solves the blank of the existing wallpaper in terms of environmental protection and heating, and forms a wallpaper with a micro-current heating effect and an anion purification function through the combination of a graphene resistance layer and a heat conduction purification layer.

Description

technical field [0001] The invention belongs to the field of wallpaper, in particular to a graphene-based wallpaper. Background technique [0002] Wallpaper, English is Wallpaper or Wallpaper, it is a kind of widely used interior decoration material. Because wallpaper has the characteristics of various colors, rich patterns, luxurious style, safety and environmental protection, convenient construction, and reasonable price, which are incomparable to many other interior decoration materials, it has been widely popularized in developed countries and regions such as Europe, America, Southeast Asia, and Japan. . Wallpaper is divided into many categories, such as coated wallpaper, laminated wallpaper, embossed wallpaper and so on. Usually bleached chemical wood pulp is used to produce base paper, and then processed by different processes, such as coating, printing, embossing or surface coating, and finally cut and packaged before leaving the factory. Because have certain stren...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B9/00B32B9/04B32B5/16B32B7/08B32B33/00B32B37/10B32B37/06C08L27/06C08L1/28C08K3/04C08J5/18C04B26/28
CPCB32B7/08B32B9/007B32B9/048B32B33/00B32B37/06B32B37/10B32B2264/10B32B2307/302B32B2307/7145B32B2607/02C04B26/285C08J5/18C08J2327/06C08J2401/28C08K3/042C04B14/303C04B22/002C04B14/04C04B14/06
Inventor 祁云永
Owner 浙江捷信纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap