A kind of mold lapping paper and mold lapping method

A mold and pulp technology, which is applied in special paper, synthetic cellulose/non-cellulose material pulp/paper, papermaking, etc., can solve the problems of high operator operation level and high research and development costs, and reduce research and development costs , to reduce the effect of using

Active Publication Date: 2022-04-12
BAIC MOTOR CORP LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this disclosure is to solve the problem that the use of metal stamping parts in the existing mold research and integration method leads to high research and synthesis costs, and the application of red lead powder or blue lead powder requires a high level of operator operation, and provides a mold research and development method. Combined paper and mold grinding method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The preparation method of the mold grinding paper of the present disclosure may be a conventional method in the art, and will not be repeated here.

[0033] The second aspect of the present disclosure provides a method for mold grinding using the mold grinding paper described in any one of the first aspect, the method includes the following steps: (1) placing the mold grinding paper under the mold (2) After the mold is closed, remove the mold lapping paper, and lap the high point of the mold gap.

[0034] The above-mentioned mold grinding method provided by the present disclosure uses paper for mold grinding instead of metal stamping parts, reduces the use of metal stamping parts, and reduces grinding costs; moreover, there is no need to paint red lead on the surface of the mold grinding paper during the grinding process Powder or blue lead powder, to avoid uneven application of red lead powder or blue lead powder and affect the effect of mold grinding.

[0035] Prefer...

Embodiment 1

[0039] According to the needs of mold grinding, cut the paper for mold grinding into rectangles, squares, and trapezoids of any size within the range of 4m, and then lay it flat on the lower mold of the mold, so that the upper mold and the lower mold of the mold can be closed. After the end, remove the mold grinding paper, and grind the high point of the mold gap.

[0040] In the present embodiment, the mold grinding paper contains 40% by weight of toughening fiber (polyester fiber), 40% by weight of pulp (wood pulp), 18% by weight of tackifier (made of polypropylene, vegetable oil , polyvinyl acetate and wax are mixed according to the weight ratio of 5:5:3:5) and 2% by weight of pigment (red lead powder).

Embodiment 2

[0042]Utilize the method for embodiment 1 to carry out mold grinding, the difference is: in the present embodiment, the toughening fiber of 35% by weight is contained in the mold grinding and combining paper, the paper pulp of 40% by weight, the viscosifier of 20% by weight agent and 5% by weight of the pigment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The present disclosure relates to a paper for mold grinding, which is characterized in that the paper for mold grinding contains toughening fiber, pulp, tackifier and pigment, wherein, based on the weight of the paper for mold grinding, the toughening fiber The weight percentage of the tough fiber is 20-40%, the weight percentage of the pulp is 20-40%, the weight percentage of the tackifier is 10-20%, and the weight percentage of the pigment is 1-10%. The mold grinding paper of the present disclosure can replace metal stamping parts, reduce the use of metal stamping parts, and reduce the cost of research and development; moreover, the mold grinding paper of the present disclosure does not need to be painted with red lead powder or blue lead powder to avoid redness. Tan powder or blue lead powder is not evenly applied, which affects the effect of mold grinding.

Description

technical field [0001] The disclosure relates to the technical field of mold production, in particular to a paper for mold grinding and combining and a mold grinding and combining method. Background technique [0002] Automobile cover parts refer to thin steel parts covering the engine, chassis, cab and body. This kind of parts generally meet the design requirements by allowing the thin steel plates to deform plastically under the action of high pressure and molds. shape, size. The production of an automobile panel is generally realized by molds with 3-6 processes. Among all the molds, the drawing die is the most critical process for the forming of the cover. The grinding quality of the drawing die is directly related to the final part. pass rate and surface quality. [0003] In the existing drawing die grinding and combining method, metal stamping parts are used for drawing die grinding and combining. Between the upper and lower molds, apply pressure to the mold to make ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/00D21H13/24D21H21/28D21H21/06D21H17/35D21H17/53D21H17/60D21H17/48D21H17/21D21H17/00B24B19/20B24D11/02
CPCD21H27/00D21H13/24D21H21/28D21H21/06D21H17/35D21H17/53D21H17/60D21H17/48D21H17/21D21H17/00B24B19/20B24D11/02
Inventor 林春雷
Owner BAIC MOTOR CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap