A kind of gradation method of heavy oil hydrotreating catalyst

A heavy oil hydrogenation and catalyst technology, applied in chemical instruments and methods, hydrocarbon oil treatment, petroleum industry, etc., can solve the problem of poor hydrogenation saturation ability of polycyclic aromatic hydrocarbons, low catalyst utilization rate, weak hydrogenation conversion ability, etc. question

Active Publication Date: 2022-02-01
PETROCHINA CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The large-pore diameter catalyst for residual oil hydrogenation disclosed in the invention is more suitable for the hydrogenation demetallization process of residual oil. Its hydrogenation active component content is low, the hydrogenation saturation ability of polycyclic aromatic hydrocarbons is poor, the acidity is weak, and the hydrogenation conversion ability is not good. powerful
[0009] In general, the main disadvantage of the existing technology is that the utilization rate of the catalyst in the grading system is not high, and the existing catalyst grading combination system needs to be further optimized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of gradation method of heavy oil hydrotreating catalyst
  • A kind of gradation method of heavy oil hydrotreating catalyst
  • A kind of gradation method of heavy oil hydrotreating catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] This example shows the preparation process of a graded combination of catalysts.

[0060] The following catalyst gradation assembly scheme is adopted, and several catalysts are loaded in the reactor, and the bed is filled with hydrodemetallization catalyst HDM-1, hydrodesulfurization catalyst HDS-1 and hydrodenitrogenation catalyst HDN-1 from top to bottom , the mass proportions added are respectively 45%, 20%, and 35%.

[0061] Hydrodemetallization catalyst HDM-1 has an average pore size of 24.35nm and a particle size of 3.5mm; hydrodesulfurization catalyst HDS-1 has an average pore size of 11.64nm and a particle size of 1.5mm; The average pore diameter is 9.04nm, and the particle diameter is 1.0mm. When the catalyst is loaded along the flow direction, the catalyst activity gradually increases, the pore size gradually decreases, the particle size gradually decreases, and the porosity gradually decreases.

[0062] Then, wet vulcanization is adopted, and the vulcanizin...

Embodiment 2

[0070] This example shows the preparation process of a graded combination of catalysts.

[0071] The following catalyst grading assembly scheme is adopted, and several catalysts are loaded in the reactor, and the bed is filled with hydrodemetallization catalyst HDM-2, hydrodesulfurization catalyst HDS-2 and hydrodenitrogenation catalyst HDN-1 respectively from top to bottom , the mass proportions added are respectively 35%, 20%, and 45%.

[0072] Hydrodemetallization catalyst HDM-2 has an average pore size of 21.67nm and a particle size of 2.2mm; hydrodesulfurization catalyst HDS-2 has an average pore size of 10.10nm and a particle size of 1.2mm; The average pore diameter is 9.04nm, and the particle diameter is 1.0mm. When the catalyst is loaded along the flow direction, the catalyst activity gradually increases, the pore size gradually decreases, the particle size gradually decreases, and the porosity gradually decreases.

[0073] Then, wet vulcanization is adopted, the vul...

Embodiment 3

[0082] This example shows the preparation process of a graded combination of catalysts.

[0083] The following catalyst grading assembly scheme is adopted. Several catalysts are loaded in the reactor, and the bed is filled with hydrodemetallization catalysts (HDM-1, HDM-2, the mass ratio is 1:1) and hydrogenation catalysts from top to bottom. Desulfurization catalyst (HDS-1, HDS-2, the mass ratio is 1:1) and hydrodenitrogenation catalyst HDN-1P, the mass proportions added are 30%, 45%, and 25%, respectively.

[0084] The average pore diameter of the hydrodemetallization catalyst HDM-1 is 24.35nm, and the particle size is 3.5mm; the average pore diameter of the hydrodemetallization catalyst HDM-2 is 21.67nm, and the particle size is 2.2mm; The average pore size is 11.64nm and the particle size is 1.5mm; the average pore size of the hydrodesulfurization catalyst HDS-2 is 10.10nm and the particle size is 1.2mm; the average pore size of the hydrodenitrogenation catalyst HDN-1 is 9...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a gradation method for heavy oil hydrotreating catalysts. The reactor is sequentially filled with hydrodemetallization catalyst, hydrodesulfurization catalyst and hydrodenitrogenation catalyst from top to bottom. direction, the catalyst activity gradually increases, the pore size gradually decreases, the particle size gradually decreases, and the porosity gradually decreases; the hydrodemetallization catalyst, the hydrodesulfurization catalyst and the hydrodenitrogenation catalyst are independently composed of Composition of one or more catalysts, active metal MoS in hydrodemetallization catalyst, hydrodesulfurization catalyst and hydrodenitrogenation catalyst after sulfidation 2 Highly dispersed distribution, MoS in the sulfided hydrodemetallization catalyst 2 Mainly single-layer and double-layer dispersion, MoS in the hydrodesulfurization catalyst after sulfidation 2 Mainly double-layer dispersion. The catalyst gradation combination obtained by the method has high activity and stability of demetallization, residual carbon removal, desulfurization and denitrogenation, and long service life.

Description

technical field [0001] The invention relates to a grading method of a heavy oil hydrogenation treatment catalyst, in particular to a gradation method of a hydrogenation catalyst used for the hydrorefining and hydrotreating of heavy distillate oil and residual oil. Background technique [0002] The shortage and inferior quality of global oil resources have led to the continuous increase in the proportion of heavy crude oil and high-sulfur crude oil in the crude oil market; at the same time, with the rapid development of my country's economy and increasingly stringent environmental protection regulations, the market demand for clean oil products is also rapidly increasing. The hydrogenation process is becoming more and more important in the refinery. Research and development of new hydrogenation catalysts to achieve deep hydroprocessing of oil products has become an urgent need in hydroprocessing. [0003] In the process of hydrotreating heavy distillate oil, especially residu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10G45/04C10G45/08B01J8/02B01J8/00
CPCC10G45/04C10G45/08B01J8/02B01J8/008C10G2300/202C10G2300/4012C10G2300/4006C10G2300/4018
Inventor 赵愉生赵元生张天琪张志国宋俊男李井泉于双林张春光程涛由慧玲崔瑞利王小丹
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com