Green antibacterial and bactericidal breathable diaper

Abstract

The invention relates to a green antibacterial and bactericidal breathable diaper. The diaper comprises a diaper body and an improved coating; the improved coating is formed by spraying a modified spray on the outer surface of the diaper body, sterilizing and drying, and the outer surface is a non-close-fitting surface; and the modified spray is composed of the following ingredients (by weight): 95-98 parts of an organosilicon waterproofing agent and 2-5 parts of negative oxygen ion powder, wherein the negative oxygen ion powder comprises the following components (by weight): 15-28 parts of chlorophyll, 19-25 parts of catechinic acid, 10-15 parts of tea polyphenol, 20-50 parts of nano zinc oxide powder, 0.6-2.5 parts of selenium dioxide, 3-10 parts of potassium octatitanate, 0.5-4 parts ofgallium arsenide, 1-6 parts of vermiculite powder and 5-20 parts of nano aerogel powder. The diaper has the antibacterial and bactericidal functions and can release negative oxygen ions for a long time, and the practical performance is improved.

Description

technical field

[0001] The invention relates to the technical field of daily necessities, in particular to a green antibacterial and sterilizing breathable diaper. Background technique

[0002] Negative oxygen ions are also known as air vitamins, vitamins, and longevity. Generally, the air negative ion concentration in the airtight room is 50-100 / cm 3 ;The general content is 700 pieces / cm 3 The above (such as fields or parks) can make people feel that the air is fresh and good for health. Therefore, negative ions are known as "air vitamins". Medical experts at home and abroad have passed clinical verification that the air contains an appropriate amount of natural negative ions that have the following functions:

[0003] (1) Improve the oxygen conversion ability of the human body, accelerate metabolism, make people feel comfortable and produce physical therapy and healing effects. Negative ions can activate a variety of enzymes in the body; increase oxygen uptake by 20%,...

Examples

Embodiment 1

[0048]S1: Put 28 parts of nano zinc oxide powder, 1 part of selenium dioxide, 4 parts of potassium octatitanate, 0.6 parts of gallium arsenide, and 1.5 parts of vermiculite powder in a stainless steel mixing tank for the first stage of stirring to obtain the first intermediate product ; The time control of the first stage stirring is 30 minutes;

[0049] S2: placing the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcination time is controlled to 8 hours;

[0050] S3: After the second intermediate product is cooled, put the second intermediate product in a stainless steel stirring tank, then add 19 parts of chlorophyll, 20 parts of catechin, and 10 parts of tea polyphenols into the stainless steel stirring tank for the second stage of stirring ; The time of the second stage stirring is controlled at 35 minutes;

[0051] S4: Add 8 parts of nano-airgel powder to the stainless steel stirring tank for the t...

Embodiment 2

[0056] S1: Put 30 parts of nano zinc oxide powder, 1 part of selenium dioxide, 5 parts of potassium octatitanate, 1 part of gallium arsenide, and 3 parts of vermiculite powder in a stainless steel stirring tank for the first stage of stirring to obtain the first intermediate product ; The time control of the first stage stirring is 30 minutes;

[0057] S2: placing the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcination time is controlled to 8 hours;

[0058] S3: After the second intermediate product is cooled, put the second intermediate product in a stainless steel stirring tank, then add 20 parts of chlorophyll, 20 parts of catechin, and 10 parts of tea polyphenols into the stainless steel stirring tank for the second stage of stirring ; The time of the second stage stirring is controlled at 30 minutes;

[0059] S4: Add 10 parts of nano-airgel powder to a stainless steel stirring tank for the thir...

Embodiment 3

[0064] S1: Put 35 parts of nano zinc oxide powder, 1.3 parts of selenium dioxide, 5.5 parts of potassium octatitanate, 1.5 parts of gallium arsenide, and 3.5 parts of vermiculite powder in a stainless steel stirring tank for the first stage of stirring to obtain the first intermediate product ; The time control of the first stage stirring is 40 minutes;

[0065] S2: placing the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcination time is controlled to 9 hours;

[0066] S3: After the second intermediate product is cooled, put the second intermediate product in a stainless steel stirring tank, then add 21 parts of chlorophyll, 22 parts of catechin, and 11 parts of tea polyphenols into the stainless steel stirring tank for the second stage of stirring ; The time of the second stage stirring is controlled at 35 minutes;

[0067] S4: Add 13 parts of nano-airgel powder to the stainless steel stirring tank ...

technical field

[0001] The invention relates to the technical field of daily necessities, in particular to a green antibacterial and sterilizing breathable diaper. Background technique

[0002] Negative oxygen ions are also known as air vitamins, vitamins, and longevity. Generally, the air negative ion concentration in the airtight room is 50-100 / cm 3 ;The general content is 700 pieces / cm 3 The above (such as fields or parks) can make people feel that the air is fresh and good for health. Therefore, negative ions are known as "air vitamins". Medical experts at home and abroad have passed clinical verification that the air contains an appropriate amount of natural negative ions that have the following functions:

[0003] (1) Improve the oxygen conversion ability of the human body, accelerate metabolism, make people feel comfortable and produce physical therapy and healing effects. Negative ions can activate a variety of enzymes in the body; increase oxygen uptake by 20%,...

Examples

Embodiment 1

[0048]S1: Put 28 parts of nano zinc oxide powder, 1 part of selenium dioxide, 4 parts of potassium octatitanate, 0.6 parts of gallium arsenide, and 1.5 parts of vermiculite powder in a stainless steel mixing tank for the first stage of stirring to obtain the first intermediate product ; The time control of the first stage stirring is 30 minutes;

[0049] S2: placing the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcination time is controlled to 8 hours;

[0050] S3: After the second intermediate product is cooled, put the second intermediate product in a stainless steel stirring tank, then add 19 parts of chlorophyll, 20 parts of catechin, and 10 parts of tea polyphenols into the stainless steel stirring tank for the second stage of stirring ; The time of the second stage stirring is controlled at 35 minutes;

[0051] S4: Add 8 parts of nano-airgel powder to the stainless steel stirring tank for the t...

Embodiment 2

[0056] S1: Put 30 parts of nano zinc oxide powder, 1 part of selenium dioxide, 5 parts of potassium octatitanate, 1 part of gallium arsenide, and 3 parts of vermiculite powder in a stainless steel stirring tank for the first stage of stirring to obtain the first intermediate product ; The time control of the first stage stirring is 30 minutes;

[0057] S2: placing the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcination time is controlled to 8 hours;

[0058] S3: After the second intermediate product is cooled, put the second intermediate product in a stainless steel stirring tank, then add 20 parts of chlorophyll, 20 parts of catechin, and 10 parts of tea polyphenols into the stainless steel stirring tank for the second stage of stirring ; The time of the second stage stirring is controlled at 30 minutes;

[0059] S4: Add 10 parts of nano-airgel powder to a stainless steel stirring tank for the thir...

Embodiment 3

[0064] S1: Put 35 parts of nano zinc oxide powder, 1.3 parts of selenium dioxide, 5.5 parts of potassium octatitanate, 1.5 parts of gallium arsenide, and 3.5 parts of vermiculite powder in a stainless steel stirring tank for the first stage of stirring to obtain the first intermediate product ; The time control of the first stage stirring is 40 minutes;

[0065] S2: placing the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcination time is controlled to 9 hours;

[0066] S3: After the second intermediate product is cooled, put the second intermediate product in a stainless steel stirring tank, then add 21 parts of chlorophyll, 22 parts of catechin, and 11 parts of tea polyphenols into the stainless steel stirring tank for the second stage of stirring ; The time of the second stage stirring is controlled at 35 minutes;

[0067] S4: Add 13 parts of nano-airgel powder to the stainless steel stirring tank ...