A kind of synthetic method of lubricating oil base oil

A technology of lubricating base oil and synthesis method, which is applied in the field of lubricating oil, can solve the problems of single raw material, poor viscosity-temperature performance, low-temperature performance, low utilization rate of highly branched olefins, etc., so as to improve the degree of polymerization and regularity, improve The effect of isomerization

Active Publication Date: 2022-03-29
PETROCHINA CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention mainly aims to solve the problem of poor viscosity-temperature performance and low-temperature performance in polyα-olefin lubricating oil base oil synthesized from complex raw materials and high-carbon olefins in the prior art, and solve the problem of single raw material and highly branched polyα-olefin lubricating oil base oil. Olefin utilization rate is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The above-mentioned two kinds of olefin raw materials and two-step polymerization process were used to carry out the polymerization reaction. First, the reactor was cleaned with cyclohexane for half an hour, and then the reactor was purged with nitrogen three times to remove the air and traces of water in the polymerization reactor. Carry out the first step of polymerization reaction: add 100 g of wax cracking olefin raw materials, 50 g of cyclohexane solvent, TiCl 4 The amount of addition is 1g, and triethylaluminum Al(Et) is added according to the ratio of Al / Ti molar ratio of 5:1 3 , feed 20g of ethylene raw material, start heating and stirring, control the reaction temperature at 80°C to 100°C, and stop stirring after 10min of reaction. When the temperature in the reactor drops to room temperature, carry out the second step reaction: add AlCl to the reactor 3 Catalyst 0.5g, start stirring, control the reaction temperature 150°C by taking heat from the external circ...

Embodiment 2

[0054] Using the same polymerization process as in Example 1: in the polymerization reactor, 100 g of wax cracking olefin raw materials, 50 g of cyclohexane solvent, TiCl 4 The amount of addition is 7.5g, and Al(Et) is added according to the ratio of Al / Ti molar ratio of 10:1 3 , feed 50 g of ethylene raw material, start heating and stirring, control the reaction temperature to 80°C, and stop stirring after 40 minutes of reaction. When the temperature in the reactor drops to room temperature, carry out the second step reaction: add AlCl to the reactor 3 Catalyst 15g, start stirring, control the reaction temperature 80°C by taking heat from the external circulation, stop stirring after 30 minutes of reaction, empty the reactor, flush with nitrogen for replacement 4 times, pass the tail gas into the alkali solution for absorption, and put the reaction materials into a container equipped with alkaline earth The three-necked flask was placed in an oil bath to heat up the reaction...

Embodiment 3

[0056] Using the same polymerization process as in Example 1: in the polymerization reactor, 150 g of wax cracking olefin raw materials, 100 g of cyclohexane solvent, TiCl 4 The amount of addition is 7.5g, and the ratio of Al / Ti molar ratio is 15:1, and diethylaluminum chloride Al(Et) is added 2 Cl, feed 50 g of ethylene raw material, start heating and stirring, control the reaction temperature to 90°C, and stop stirring after 60 minutes of reaction. When the temperature in the reactor drops to room temperature, carry out the second step reaction: add AlCl to the reactor 3 Catalyst 20g, start stirring, control the reaction temperature 180°C by taking heat from the external circulation, stop stirring after 60 minutes of reaction, empty the reactor, flush with nitrogen for replacement 4 times, pass the tail gas into alkali solution for absorption, and put the reaction materials into a container equipped with alkaline earth The three-necked flask was placed in an oil bath to hea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
dew pointaaaaaaaaaa
pour pointaaaaaaaaaa
pour pointaaaaaaaaaa
Login to View More

Abstract

A method for synthesizing lubricating oil base oil, comprising the following steps: adding high-carbon olefin and ethylene into a high-pressure white steel polymerization reactor at the same time, adding a Ziegler-Natta catalyst, starting the reaction, controlling conditions in the polymerization process, and adding the The material is pressed into the second reactor by nitrogen (or cooled to room temperature in the same reactor), and AlCl is added to the material at the same time 3 Catalyst, the amount of catalyst added and the polymerization reaction conditions are controlled. After the reaction is completed, the reactor is vented and depressurized, and the obtained crude product is subjected to an alkali washing process to remove the residual catalyst, and then the unreacted high-carbon olefin is removed by depressurization and distillation. The product obtained after hydrogenation is subjected to structural characterization to determine the degree of branching and performance testing to determine the viscosity, viscosity index, pour point and other indicators of the product. The present invention adopts complex raw material high-carbon olefin as raw material, and the synthesized polyα-olefin lubricating base oil has excellent viscosity-temperature performance and low-temperature performance.

Description

technical field [0001] The invention relates to a synthesis method of lubricating oil base oil, the main purpose is to improve the viscosity-temperature performance and low-temperature performance of the lubricating oil base oil, and belongs to the field of lubricating oil. Background technique [0002] Poly-α-olefin lubricating base oil (PAO) is a kind of lubricating oil base oil with excellent comprehensive performance. With the advantages of wide phase range, small evaporation loss, low pour point, high viscosity index, and good thermal oxidation stability, it can meet increasingly stringent OEM specifications and meet contemporary stringent energy-saving and environmental protection requirements. [0003] PAO is generally a high-carbon α-olefin (C 8 -C 12 ) as the raw material, and the composition of the raw material, that is, the carbon number of olefins directly affects the performance of the oil. The higher the carbon number, the higher the viscosity index and the h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C10M107/02C10G50/02C10N30/02C10N30/08
CPCC10M107/02C10G50/02C10M2205/0206
Inventor王秀绘王亚丽马克存王力搏褚洪岭徐显明于部伟孙恩浩曹媛媛蒋岩刘通黄付玲高晗王玉龙霍洪亮韩云光韩雪梅林如海关伟红王凤荣陈谦马莉莉孙维徐婷婷
OwnerPETROCHINA CO LTD