Secondary amide cyclamine quaternary ammonium salt amphoteric asphalt emulsifier and preparation method thereof

A technology of asphalt emulsifier and secondary amide cyclic amine, which is applied in the field of fine chemical industry, can solve the problems of high requirements for production experimental equipment, high cost of emulsifier raw materials, complicated preparation steps, etc., and achieves excellent performance indicators and good aggregate adhesion. and storage stability, the effect of improving stability

Active Publication Date: 2020-06-23
SHANDONG UNIV
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The inventor found that the disadvantage of this method is that the preparation steps are cumbersome, the cost is high, and high temperature reaction is required
[0005] The general disadvantages of the above cationic asphalt emulsifiers and their preparation methods are: the cost of raw materials for the preparation of emulsifiers is high, the sources are limited, high temperature reactions are required during preparation, and the requirements for production and experimental equipment are relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Secondary amide cyclamine quaternary ammonium salt amphoteric asphalt emulsifier and preparation method thereof
  • Secondary amide cyclamine quaternary ammonium salt amphoteric asphalt emulsifier and preparation method thereof
  • Secondary amide cyclamine quaternary ammonium salt amphoteric asphalt emulsifier and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] For above asphalt emulsifier, the present invention also provides its preparation method, comprises the following steps:

[0037] (1) Aminoethylpiperazine, alcoholic solvent and acrylic acid are mixed and reacted to obtain reaction intermediate I, and the structural formula of said reaction intermediate I is:

[0038]

[0039] (2) Add epichlorohydrin gradually again in reaction intermediate I, mixed reaction, obtain reaction intermediate II, the structural formula of described reaction intermediate II is:

[0040]

[0041](3) Gradually add cocoyl propyl dimethyl tertiary amine to the reaction intermediate II, mix and react, then add water, mix and react, and obtain the secondary amide cyclic amine quaternary ammonium salt amphoteric asphalt emulsifier.

[0042] In some preferred technical schemes of the present invention, the mol ratio of cocoyl propyl dimethyl tertiary amine, alcoholic solvent, water, epichlorohydrin, aminoethylpiperazine, acrylic acid is 1mol: (...

Embodiment 1

[0063] (1) Preparation of secondary amide cyclic amine quaternary ammonium salt amphoteric asphalt emulsifier:

[0064] 1) Add 141.9g aminoethylpiperazine, 300g isopropanol in the reactor, heat and stir to mix. Then gradually added 79.3g of acrylic acid, and stirred at 75°C for 2h to obtain reaction intermediate I.

[0065] 2) Gradually add 97.07 g of epichlorohydrin to the reaction intermediate I. After the addition is complete, react at 75° C. for 2 hours to obtain the reaction intermediate II.

[0066] 3) Gradually add 284.5g cocoyl propyl dimethyl tertiary amine to the reaction intermediate II. After the addition is complete, react at 75°C for 0.5h, then add 300g of water. After adding water, react at 75°C for 3h. That is, the amphoteric asphalt emulsifier of secondary amide cyclic amine quaternary ammonium salt was obtained, which was reserved for the emulsified asphalt test.

[0067] The synthesized product was separated and purified by recrystallization and then detec...

Embodiment 2

[0076] (1) Preparation of secondary amide cyclic amine quaternary ammonium salt amphoteric asphalt emulsifier:

[0077] 1) Add 141.9g aminoethylpiperazine and 300g dehydrated ethanol in the reactor, heat and stir to mix. Then gradually added 79.3g of acrylic acid, and stirred at 65°C for 3h to obtain reaction intermediate I.

[0078] 2) Gradually add 97.07 g of epichlorohydrin to the reaction intermediate I. After the addition is complete, react at 75° C. for 2 hours to obtain the reaction intermediate II.

[0079] 3) Gradually add 284.5g cocoyl propyl dimethyl tertiary amine to the reaction intermediate II. After the addition is complete, react at 75°C for 0.5h, then add 300g of water. After adding water, react at 75°C for 3h. That is, the amphoteric asphalt emulsifier of secondary amide cyclic amine quaternary ammonium salt was obtained, which was reserved for the emulsified asphalt test.

[0080] (2) Preparation of emulsified asphalt:

[0081] Take 300g of AH-70# asphalt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a secondary amide cyclamine quaternary ammonium salt amphoteric asphalt emulsifier and a preparation method thereof. The asphalt emulsifier is prepared from the following raw materials according to a molar ratio of cocoyl propyl dimethyl tertiary amine: an alcohol solvent: water: epoxy chloropropane: aminoethyl piperazine: acrylic acid of 1 mol to (4.50 to 10.00) mol to (14.00 to 18.00) mol to (1.00 to 1.15) mol to (1.00 to 1.20) mol to (1.00 to 1.20) mol, wherein the alcohol solvent is ethanol, methanol or isopropanol. The asphalt emulsifier has the advantages of easily available synthesis raw materials, low production cost and simple technique, and does not need high-temperature reaction. The emulsifier can emulsify various types of asphalt, the prepared emulsified asphalt is fine and uniform, the storage stability is good, and cationic or anionic emulsified asphalt can be prepared.

Description

technical field [0001] The invention relates to a secondary amide cyclic amine quaternary ammonium salt amphoteric asphalt emulsifier and a preparation method thereof, belonging to the technical field of fine chemicals. Background technique [0002] Emulsified asphalt is an oil-in-water liquid asphalt emulsion formed by asphalt and water under the action of an emulsifier. Emulsified asphalt is mainly divided into cationic emulsified asphalt, anionic emulsified asphalt and nonionic emulsified asphalt. Among them, cationic emulsified asphalt is widely used in road construction and road maintenance due to its energy-saving and environmental protection, can improve construction conditions, has strong adhesion to stone materials, and can effectively reduce over-aging of asphalt and many other excellent application characteristics. [0003] The emulsified asphalt used for micro-surface is required to be slow-cracking and fast-setting type, which not only requires sufficient mixin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07D295/15C08J3/03E01C7/26C08L95/00
CPCC07D295/15C08J3/03C08J2395/00E01C7/265
Inventor 施来顺陈雅雯顾晨阳巩雪笛王天曜于小梦
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com