Green polymer concrete recycled brick and preparation method thereof
A concrete regeneration and polymer technology, applied in the field of building materials, can solve the problems of large land occupation, low utilization rate and added value of residual mud and slag, and achieve the effect of solving large land occupation and reducing production costs.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0029] Such as figure 1 Shown is the preparation method of the above-mentioned green polymer concrete regenerated brick provided by the embodiment of the present invention, comprising the following steps:
[0030] Step S11: Mix the residual sludge, water, water glass and sodium hydroxide, and stir in a stirrer with a rotating speed of 200r / min-300r / min to form a slurry of sludge. In this step, 200-400 parts of residual sludge (mass parts, the same below), 50-150 parts of water, 200-280 parts of water glass and 100-140 parts of sodium hydroxide.
[0031] Specifically, the sand content of the residue sludge in this embodiment is 25%-60%, which can be obtained from new construction, reconstruction, expansion and demolition of various buildings, structures, roads, pipe networks, etc., and the process of residential decoration and house decoration. Spoils, waste materials and other wastes generated. Moreover, the above-mentioned residual sludge can be obtained by blending spoils,...
Embodiment 1
[0040] Prepare the green polymer concrete regenerated brick raw material (×10kg) according to the following proportions by weight: 300 parts of residual sludge, 100 parts of slag powder, 100 parts of cement, 200 parts of water glass, 100 parts of sodium hydroxide, recycled fine aggregate 350 parts, 500 parts of recycled coarse aggregate, 200 parts of water, 20 parts of admixture.
[0041]Mix 300 parts of residual sludge, 100 parts of water, 200 parts of water glass, and 100 parts of sodium hydroxide, and stir in a stirrer with a rotating speed of 240 r / min to form a slurry of sludge. Add 500 parts of recycled coarse aggregate, 350 parts of recycled fine aggregate, 100 parts of cement, 100 parts of slag powder, 700 parts of dregs slurry, and 100 parts of water into the concrete mixer and mix evenly. The mud can be cleaned with water and poured into the mixer. The stirring speed of the mixer is 60r / min, and the stirring time is 60s. Lay a silicone film with a specific pattern ...
Embodiment 2
[0043] Prepare the green polymer concrete regenerated brick raw material (×10kg) according to the following proportions by weight: 250 parts of residual sludge, 130 parts of slag powder, 80 parts of cement, 200 parts of water glass, 100 parts of sodium hydroxide, recycled fine aggregate 380 parts, 540 parts of recycled coarse aggregate, 185 parts of water, and 17 parts of admixture.
[0044] Mix 250 parts of residual sludge, 90 parts of water, 200 parts of water glass, and 100 parts of sodium hydroxide, and stir in a stirrer with a rotational speed of 240 r / min to form a slurry of sludge. Add 540 parts of recycled coarse aggregate, 380 parts of recycled fine aggregate, 130 parts of cement, 130 parts of slag powder, 640 parts of dregs slurry, and 95 parts of water into the concrete mixer and mix evenly. The mud is cleaned with water and poured into the mixer. The stirring speed of the mixer is 60r / min, and the stirring time is 80s. Lay a silicone film with a specific pattern ...
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap