A modified composite reinforcing material and antibacterial wear-resistant lightweight pallet

A composite reinforcement and modification technology, which is applied in antifouling/underwater coatings, biocide-containing paints, coatings, etc., can solve problems such as foam falling off, foam materials are easy to get dirty, and foam materials have weak load-bearing capacity, and achieve improved Smoothness, excellent wear resistance, effect of improving adhesion

Active Publication Date: 2021-11-30
北京帅阔达新材料科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after a period of use, the foam material on the surface is easy to get dirty on the one hand, and on the other hand, it is easy to cause the foam to fall off during use; the other is the disadvantage of the weak load-bearing capacity of the foam material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A modified composite reinforcing material and antibacterial wear-resistant lightweight pallet
  • A modified composite reinforcing material and antibacterial wear-resistant lightweight pallet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of antibacterial wear-resisting polyurea elastomer coating of the present embodiment is polyurea resin, and the mass fraction of each component of described polyurea resin is as follows:

[0043] A component

[0044] 40 parts of diphenylmethane diisocyanate (MDI-100);

[0045] 50 parts of polytetrahydrofuran glycol;

[0046] 10 parts of dibutylbenzyl phthalate.

[0047] B component

[0048] Polyether diamine (D-400) 50 parts;

[0049] 30 parts of 4,4'-bis-secondary aminodiphenylmethane;

[0050] 15 parts of methyl hydroxy silicone oil;

[0051] 3.75 parts of nano zinc oxide powder;

[0052] 1.25 parts of chitosan micropowder.

[0053]Modification of nano-zinc oxide: Add absolute ethanol to 2 parts of nano-zinc oxide at a ratio of 1:15, ultrasonically treat for 20 minutes to obtain zinc oxide-ethanol dispersion; then add 0.1 part of coupling agent (KH570 ), mechanically stirred for 10 minutes, then ultrasonically treated at 40-50°C for 1h, heated to 75-85°...

Embodiment 2

[0058] A kind of antibacterial wear-resisting polyurea elastomer coating of the present embodiment is polyurea resin, and the mass fraction of each component of described polyurea resin is as follows:

[0059] A component

[0060] Toluene diisocyanate (TDI) 40 parts;

[0061] 55 parts of polytetrahydrofuran glycol;

[0062] 5 parts of dibutylbenzyl phthalate.

[0063] B component

[0064] 55 parts of polyether diamine (T-403);

[0065] 30 parts of diaminodimethylthiotoluene;

[0066] 10 parts of methyl hydroxy silicone oil;

[0067] 3.85 parts of nano zinc oxide powder;

[0068] 1.15 parts of chitosan micropowder.

[0069] Modification of nano-zinc oxide: Add absolute ethanol to 2 parts of nano-zinc oxide at a ratio of 1:15, and ultrasonically treat for 20 minutes to obtain a zinc oxide-ethanol dispersion; the coupling agent is KH570. Then add 0.1 part of coupling agent to the zinc oxide-ethanol dispersion, stir mechanically for 10 minutes to mix, then ultrasonically t...

Embodiment 3

[0074] A kind of antibacterial wear-resisting polyurea elastomer coating of the present embodiment is polyurea resin, and the mass fraction of each component of described polyurea resin is as follows:

[0075] A component

[0076] 55 parts of diphenylmethane diisocyanate (MDI-100);

[0077] 40 parts of tetrahydroxypropyl ethylenediamine;

[0078] 5 parts of dibutylbenzyl phthalate.

[0079] B component

[0080] 45 parts of polyether diamine (D-230);

[0081] 35 parts of diaminodimethylthiotoluene;

[0082] 15 parts of methyl hydroxy silicone oil;

[0083] 4.5 parts of nano zinc oxide powder;

[0084] Chitosan micropowder 0.5 part.

[0085] Modification of nano-zinc oxide: Add absolute ethanol to 2 parts of nano-zinc oxide at a ratio of 1:15, and ultrasonically treat for 20 minutes to obtain a zinc oxide-ethanol dispersion; the coupling agent is KH570. Then add 0.1 part of coupling agent to the zinc oxide-ethanol dispersion, stir mechanically for 10 minutes to mix, then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of packaging and transportation, and in particular relates to a modified composite reinforcing material and an antibacterial and wear-resistant light pallet. Wherein, the modified composite reinforcing material includes the following components by weight fraction: 50-75 parts of methyl hydroxy silicone oil, 10-35 parts of nano-zinc oxide powder, 1-10 parts of chitosan micropowder; the antibacterial and wear-resistant The lightweight pallet includes: a foam inner core and a polyurea coating, and the polyurea coating is coated on the outer surface of the foam inner core; the foam inner core includes a pallet and feet positioned below the pallet; The coating material is the antibacterial and wear-resistant polyurea elastomer coating. The invention adopts the modified composite reinforcing material, optimizes the pallet coating material component system, and combines the spraying process to obtain a lightweight pallet with impact resistance, antibacterial and wear resistance.

Description

technical field [0001] The invention belongs to the technical field of packaging and transportation, and in particular relates to a modified composite reinforcing material and an antibacterial and wear-resistant light pallet. Background technique [0002] Pallets are load-carrying devices for cargo assembly, stacking and transportation. It is convenient for loading and unloading, handling unit materials and small quantities of material pallets. It plays a considerable role in protecting products and facilitating storage and transportation. It can be said that pallets are the development of modern logistics industry. essential tool. At first, most pallets used wood as the main material, but with the reduction of wood resources, the stringent requirements of international trade on wooden pallets, the standardization of pallets and the acceleration of the development of pallet sharing systems, iron pallets, plastic pallets and paper pallets began to be used. been used on a lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D161/24C09D7/62C09D7/65C09D5/14C08J9/36
CPCC08J9/365C08J2461/24C08K2003/2296C08K2201/011C08L2205/03C09D5/14C09D161/24C09D7/62C09D7/65C08L83/04C08L5/08C08K9/06C08K3/22
Inventor 郭瑞
Owner 北京帅阔达新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap