A gasket material suitable for laser printing

A technology of laser printing and spacers, which is applied in the direction of film/sheet without carrier, pressure-sensitive film/sheet, film/sheet-shaped adhesive, etc., which can solve poor contrast, poor elasticity and strength, and poor laser energy absorption and other problems, to achieve the effect of enhancing contrast, preventing the decline of tensile strength, and increasing the pressure-sensitive adhesive strength

Active Publication Date: 2021-10-01
FOSHAN TONGJUN ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The absorption of laser energy is poor, after laser development, the contrast is poor, the development effect is not good, and the recognition degree is not high;
[0004] 2. The elasticity and strength are not as good as PVC gaskets, especially the adhesion between the gasket and the iron cover is poor, resulting in problems such as side leakage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A gasket material suitable for laser printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The gasket material suitable for laser printing in this embodiment is prepared from raw materials with the following weight fractions:

[0022] 50 parts of styrene-butadiene-styrene block copolymer (SBS), 40 parts of polyethylene, 15 parts of rosin soap, 10 parts of stearic acid amide, 10 parts of laser powder, 10 parts of silicon-titanium compound, of which , the silicon-titanium composite is composed of nano-silicon dioxide, nano-titanium dioxide and EPDM rubber at a mass ratio of 1:1:7, and before mixing with other components, silicon dioxide and nano-titanium dioxide are preferentially mixed with The rubber mixes to form a sol.

[0023] Among them, the number average molecular weight of styrene-butadiene-styrene block copolymer (SBS) is 5.25.2×10 5 , the mass content of polystyrene and polybutadiene blocks is 15% and 45% respectively;

[0024] Described polyethylene is linear low-density polyethylene (LLDPE) and low-density polyethylene (LDPE) and mixture, and whe...

Embodiment 2

[0028] 60 parts of styrene-butadiene-styrene block copolymer (SBS), 25 parts of polyethylene, 10 parts of rosin modified phenolic resin, 8 parts of stearic acid amide, 8 parts of laser powder, 15 parts of silicon-titanium compound Parts, wherein, the silicon-titanium composite is composed of nano-silica, nano-titanium dioxide and isoprene rubber in a mass ratio of 1:1:8, and before mixing with other components, the silicon dioxide, nano-titanium dioxide It is preferentially mixed with rubber to form a sol.

[0029] Among them, the number average molecular weight of styrene-butadiene-styrene block copolymer (SBS) is 3.8×10 5 , the mass content of polystyrene and polybutadiene blocks is 20% and 35% respectively;

[0030] Described polyethylene is linear low-density polyethylene (LLDPE) and low-density polyethylene (LDPE) and mixture, and wherein LLDPE content is 50%, and LDPE content is 50%, and the melting index MFI of LLDPE and LDPE is respectively 4.4 / 10min ( 230°C, 2.16kg)...

Embodiment 3

[0034] 80 parts of styrene-isoprene-styrene block copolymer (SIS), 15 parts of polyethylene, 5 parts of disproportionated rosin, 5 parts of stearic acid amide, 5 parts of laser powder, 10 parts of silicon-titanium compound, Among them, the silicon-titanium composite is composed of nano-silicon dioxide, nano-titanium dioxide and isoprene rubber in a mass ratio of 1:1:9, and before mixing with other components, silicon dioxide and nano-titanium dioxide are preferred Mixed with rubber to form a sol.

[0035] Among them, the number average molecular weight of styrene-isoprene-styrene block copolymer (SIS) is 1.8×10 5 , the mass content of polystyrene and polyisoprene blocks is 15% and 45% respectively;

[0036] Described polyethylene is linear low-density polyethylene (LLDPE) and low-density polyethylene (LDPE) and mixture, and wherein LLDPE content is 40%, and LDPE content is 60%, and the melting index MFI of LLDPE and LDPE is respectively 5.2 / 10min ( 230°C, 2.16kg) and 0.8 / 10m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a gasket material suitable for laser printing, which comprises the following raw materials in parts by weight: 50-80 parts of thermoplastic elastomer, 15-40 parts of polyethylene, 5-15 parts of modified rosin resin, stearin 5-10 parts of acid amide, 5-10 parts of laser powder, 10-20 parts of silicon-titanium compound, wherein, the silicon-titanium compound is composed of nano-silicon dioxide, nano-titanium dioxide and rubber in a mass ratio of 1:1 : Composite of 7‑9. The gasket material of the present invention is copolymerized by thermoplastic elastomer, polyethylene, modified rosin resin, and stearic acid amide, so that the pressure-sensitive bonding strength of the gasket and the bottle cap is high, and no additional adhesive is needed, and the Adding laser powder and silicon-titanium compound is beneficial to synergistically enhance the contrast of laser marking, and using rubber as a medium can toughen the system.

Description

technical field [0001] The invention relates to the field of laser printing materials, in particular to a gasket material suitable for laser printing. Background technique [0002] At present, the gasket material that can be developed by laser for iron bottle caps is generally PVC gasket, which is composed of directly or indirectly adding lead-based laser powder to PVC to ensure the developability of the gasket material. However, since the gasket material is bonded to the bottle cap and is in direct contact with the bottled product, plasticizers need to be added in PVC processing. The plasticizer will migrate into the product if it is in contact with the product for a long time. Products that migrate plasticizers will pose a threat to the health of consumers, so more and more research has been transferred to non-PVC materials, but the current non-PVC gasket materials generally use blended modified materials, and there are the following shortcoming: [0003] 1. The absorpti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J153/02C09J123/06C09J123/08C09J11/04C09J11/06C09J11/08C09J7/38C09J7/10
CPCC08K2003/0812C08K2003/2241C08K2201/011C08L2205/02C08L2205/035C08L2207/04C08L2207/066C09J11/04C09J11/06C09J11/08C09J153/02C09J153/025C09J2409/00C09J2423/04C09J2453/00C09J7/10C09J7/387C08L23/06C08L23/0815C08L23/16C08L93/04C08K13/02C08K5/20C08K3/36C08K3/22C08K3/08C08L9/00C08L61/14C08K5/40
Inventor 车俊峥车皓橦
Owner FOSHAN TONGJUN ENVIRONMENTAL PROTECTION TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More