Bionic artificial temporomandibular joint disc and preparation method thereof

A temporomandibular joint and artificial technology, applied in the field of bionic artificial temporomandibular joint disc and its preparation, can solve the problems of high cost, difficult reconstruction, inability to match the physiological load of the temporomandibular joint, etc., and achieves low cost, low preparation cost, clinical The effect of high conversion value

Active Publication Date: 2020-11-24
SICHUAN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the above-mentioned problems existing in the prior art, the present invention provides a bionic artificial temporomandibular joint disc and its preparation method, in which the bio-ink is prepared from the decellularized intervertebral disc, supplemented with polymer materials, and the temporomandibular joint is reconstructed by 3D printing method Disc, which effectively solves the problems in the prior art that cannot match the physiological load of the temporomandibular joint, difficult reconstruction and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bionic artificial temporomandibular joint disc and preparation method thereof
  • Bionic artificial temporomandibular joint disc and preparation method thereof
  • Bionic artificial temporomandibular joint disc and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A bionic artificial temporomandibular joint disc, the preparation method of which comprises the following steps:

[0031] (1) The intervertebral discs of 8-month-old oxtails were harvested under sterile conditions, washed with penicillin saline to remove blood stains, then frozen and thawed for 5 cycles at a temperature range of -20 to 37°C, and extracted with ultrapure water / guanidine hydrochloride chemical reagents Glycosaminoglycan and protein, and then break the remaining tissue into floc, add 4wt% sodium dodecyl sulfate (SDS) and 4KU / ml DNase to treat at room temperature for 2 hours, wash with enzyme-free water, and obtain intervertebral disc floc sample;

[0032] (2) Freeze-dry the intervertebral disc flocculent sample obtained in step (1), then add the digestive solution, blend at room temperature and 25r / min for 60h, adjust the pH value to neutral with sodium hydroxide, and then add the step (1) The resulting glycosaminoglycan and protein are used to obtain bio...

Embodiment 2

[0036] A bionic artificial temporomandibular joint disc, the preparation method of which comprises the following steps:

[0037] (1) The intervertebral discs of 8-month-old oxtails were harvested under sterile conditions, washed with penicillin saline to remove blood stains, then frozen and thawed for 5 cycles at a temperature range of -20 to 37°C, and extracted with ultrapure water / guanidine hydrochloride chemical reagents Glycosaminoglycans and proteins, and the remaining tissues were crushed into flocculents, treated with 5wt% sodium dodecyl sulfate and 5KU / ml DNase at room temperature for 5 hours, washed with enzyme-free water, and intervertebral disc flocculent samples were obtained;

[0038](2) Freeze-dry the intervertebral disc flocculent sample obtained in step (1), then add the digestive solution, blend at room temperature and 30r / min for 72h, adjust the pH value to neutral with sodium hydroxide, and then add the step (1) The resulting glycosaminoglycan and protein ar...

Embodiment 3

[0041] A bionic artificial temporomandibular joint disc, the preparation method of which comprises the following steps:

[0042] (1) The intervertebral discs of 8-month-old oxtails were harvested under sterile conditions, washed with penicillin saline to remove blood stains, then frozen and thawed for 5 cycles at a temperature range of -20 to 37°C, and extracted with ultrapure water / guanidine hydrochloride chemical reagents Glycosaminoglycan and protein, and then crush the remaining tissue into flocculent, add 6wt% sodium lauryl sulfate and 6KU / ml DNase to treat at room temperature for 4 hours, wash with enzyme-free water, and obtain flocculent intervertebral disc samples;

[0043] (2) Freeze-dry the intervertebral disc flocculent sample obtained in step (1), then add the digestive solution, blend at room temperature and 35r / min for 84 hours, adjust the pH value to neutral with sodium hydroxide, and then add the step (1) The resulting glycosaminoglycan and protein are used to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a bionic artificial temporomandibular joint disc and a preparation method thereof. The preparation method includes the following steps that the intervertebral disc of oxtail iscollected, washed and then freeze-thawed, glycosaminoglycan and protein are extracted, then the treated intervertebral disc is broken into a flocculent shape, sodium lauryl sulfate and DNA enzyme areadded to treat at room temperature, and washing is carried out to obtain an intervertebral disc flocculent-shaped sample; the intervertebral disc flocculent-shaped sample is freeze-dried, then a digestion solution is added, blending is carried out, a pH value is adjusted to neutral, and then glycosaminoglycan and protein are added again to obtain bio-ink; and a polymer material and the bio-ink areblended at room temperature for 3D printing to obtain the bionic artificial temporomandibular joint disc. The bionic artificial temporomandibular joint disc is prepared by the preparation method. Decellularized intervertebral disc is used to prepare the bio-ink, with the help of by the polymer material, a 3D printing method is used to to reconstruct the temporomandibular joint disc, and the problems that the inability to match the physiological load, reconstruction difficulty and high cost of a temporomandibular joint in the prior art are effectively solved.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, and in particular relates to a bionic artificial temporomandibular joint disc and a preparation method thereof. Background technique [0002] Temporomandibular joint disk (Temporomandibular joint disk, TMJ disk) is a fibrocartilage-like tissue located between the mandibular condyle and the glenoid fossa of the temporal bone. Distributes loads, cushions shocks, and reduces dissonance between condyle and glenoid bony structures. Clinically, the destruction or loss of the temporomandibular joint disc is one of the main causes of temporomandibular joint diseases, which in turn will cause abnormal function of the entire stomatognathic system and seriously affect the quality of life of patients. According to relevant data, there are as many as one million patients in the world who need to reconstruct the articular disc every year, and the medical expenses required are also as high as hund...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L27/36A61L27/50A61L27/22A61L27/20A61F2/30
CPCA61F2/3099A61F2002/30985A61F2002/30993A61L27/20A61L27/22A61L27/3658A61L27/3687A61L27/3691A61L27/50A61L2430/24A61L2430/40C08L89/00C08L5/00
Inventor 祝颂松姜楠毕瑞野王旻应彬彬陈浩哲
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com