Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A negative electrode sheet and a stacked lithium-ion battery including the negative electrode sheet

A negative electrode sheet and negative electrode technology, which is applied in the field of stacked lithium-ion batteries, can solve the problems of not being well compatible with high energy density and fast charging.

Active Publication Date: 2021-07-06
ZHUHAI COSMX BATTERY CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current lithium-ion batteries are not well compatible with the two properties of high energy density and fast charging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A negative electrode sheet and a stacked lithium-ion battery including the negative electrode sheet
  • A negative electrode sheet and a stacked lithium-ion battery including the negative electrode sheet
  • A negative electrode sheet and a stacked lithium-ion battery including the negative electrode sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] (1) Add 0.5wt% conductive carbon black, 1.3wt% styrene-butadiene rubber, and 1.3wt% carboxymethyl cellulose to 96.9wt% graphite a, and then adjust it into negative electrode slurry A with water. Add 0.5wt% conductive carbon black, 1.3wt% styrene-butadiene rubber, and 1.3wt% carboxymethyl cellulose to 96.9wt% graphite b, and then adjust it into negative electrode slurry B with water.

[0066] Such as Figure 4 As shown, the negative electrode sheet includes a negative electrode collector, and a central area, a first edge, a second edge, a third edge, and a fourth edge are provided on the first surface of the negative electrode collector; the first edge, The second edge, the third edge and the fourth edge are arranged around the central area, and the first edge and the third edge are arranged opposite; the second edge and the fourth edge are arranged opposite;

[0067] Wherein, a first coating area is set in the central area, and a second coating area is set in the first...

Embodiment 2

[0073] Others are the same as in Example 1, only the area of ​​double-layer coating is different, that is, the area of ​​the first coating area is 1 / 2 of the sum of the areas of the first coating area and the second coating area, such as Figure 4 As shown, the areas of the first edge, the second edge, the third edge and the fourth edge are all 1 / 8.

Embodiment 3

[0075] Others are the same as in Example 1, except that the compositions of slurry A and slurry B are different.

[0076] Add 0.5wt% conductive carbon black, 1.3wt% styrene-butadiene rubber, and 1.3wt% carboxymethyl cellulose to 96.9wt% graphite a, and then adjust with water to prepare negative electrode slurry A. Add 1.0wt% conductive carbon black, 1.3wt% styrene-butadiene rubber, and 1.3wt% carboxymethyl cellulose to 96.4wt% graphite b, and then adjust with water to prepare negative electrode slurry B.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a negative electrode sheet and a laminated lithium-ion battery including the negative electrode sheet. The laminated lithium-ion battery using the negative electrode sheet can effectively increase the energy density of the laminated lithium-ion battery without loss of energy density. Fast charging capability of ion batteries. The negative electrode sheet of the present invention adopts double-layer coating technology, and the active material and surface density of the negative electrode sheet are specifically designed according to the potential and polarization distribution of the negative electrode sheet, and the edge position of the electrode sheet of the negative electrode sheet is controlled by using the double-layer coating technology. Double-layer coating is adopted; on the one hand, the accumulation mode of the negative electrode active material particles can be changed by double-layer coating, the edge polarization can be reduced, the reaction site can be increased, and the internal resistance can be reduced, so that lithium will not be precipitated at the edge; on the other hand, compared with a single Layer coating and double-layer coating can ensure a faster charging speed at the same surface density, so there will be no loss of energy density.

Description

technical field [0001] The invention belongs to the technical field of lithium ion batteries, and in particular relates to a negative electrode sheet and a laminated lithium ion battery including the negative electrode sheet. Background technique [0002] With the development of electronic products, people no longer only pursue high energy density for lithium-ion batteries, and charging speed has become one of the key evaluation criteria for consumers. However, the current lithium-ion batteries are not well compatible with the two properties of high energy density and fast charging. Contents of the invention [0003] The invention provides a negative electrode sheet and a laminated lithium ion battery including the negative electrode sheet. The laminated lithium ion battery using the negative electrode sheet can effectively improve the energy density of the laminated lithium ion battery without loss of energy density. The fast charging capability of the battery. [0004]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/133H01M4/1393H01M10/0525H01M10/0585
CPCH01M4/133H01M4/1393H01M10/0525H01M10/0585H01M2004/027Y02E60/10Y02P70/50
Inventor 石越彭冲李俊义徐延铭
Owner ZHUHAI COSMX BATTERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com