Preparation method of ammonium nitrogen adsorption bag in natural water and isotope detection method thereof
A detection method, ammonium nitrogen technology, applied in the field of materials science, can solve problems such as low work efficiency, cross-contamination, and high requirements for operators, and achieve avoidance of organic nitrogen decomposition and isotope fractionation, high accuracy and precision, and experimental conditionally reliable effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023]Example 1
[0024]This example gives a method of preparing a ammonium nitrogen suction package in natural water, including:
[0025]The polytetrafluoride film was taken, and the Seporadion 24 h was added to the mixed gel filter, and the mixed gel filter was dried in a dry box at 100 ° C for 2 h under a nitrogen condition. After the dry mixed gel filter is stored in a vacuum drying case of 20 to 40 ° C to obtain a hydrophobic film; a glass fiber filter having a substantially hydrophobic film is placed on a hydrophobic film. 25 μl of 2 mol / L of sulfuric acid was added to the glass fiber filter, and then the surface of the acidified glass fiber filter was covered from the new hydrophobic film, and the hydrophobic film on both sides was sealed.
[0026]The adsorption package prepared by the present embodiment is a method of detecting an ammonium nitrogen azoa: a natural water sample of 100 mL is added to the culture flask, and the stirrer is added to the culture bottle, and the adsorptio...
Example Embodiment
[0028]Example 2:
[0029]The method of preparing ambient nitrogen suction package in natural water given in this example, the difference from Embodiment 1 is to replace the polytetrafluoroethylene filter in step one as a polypropylene filter, TEOA-PAM -Gel gel concentration of 35%, an amount of sulfuric acid was 30 μL, and the application of the obtained adsorbed package was added to a mass of 300 mg of the Wipple alloy, and the volume of the glass fiber filter was a hydrophobic film. First, the other conditions were the same as in Example 1, and the calculated ammonity nitrogen recovery is 93%, recorded in Table 1, and detects ammonium nitrogen isotope is detected by elemental analyzer - hostelapers. The isotope value is 3.5 ‰ record in Table 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap