A kind of high-entropy ceramics with high hardness and high conductivity and its preparation method and application

A high-conductivity, high-hardness technology, applied in the field of ceramic materials, can solve problems such as insufficient electrical conductivity, and achieve the effects of low cost, large application potential, and wide application range

Active Publication Date: 2021-12-21
DONGHUA UNIV +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a high-entropy ceramic with high hardness and high conductivity and its preparation method and application, so as to overcome the shortcomings of insufficient electrical conductivity of traditional ceramics and existing boride high-entropy ceramics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-entropy ceramics with high hardness and high conductivity and its preparation method and application
  • A kind of high-entropy ceramics with high hardness and high conductivity and its preparation method and application
  • A kind of high-entropy ceramics with high hardness and high conductivity and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation composition is (Dy, Ho, Er, Tm, Lu) B 12 According to the molar mass percentage of the high-entropy ceramics, Dy, Ho, Er, Tm, and Lu each account for 20%, and the balance is B and unavoidable impurities, and the impurity content is less than 0.05%. The preparation of high-entropy ceramics proceeds as follows:

[0028] (1) Dosing is carried out according to the molar mass of the high-entropy ceramic, and the amorphous boron powder is added according to the theoretically calculated 110%.

[0029] (2) the rare earth oxide (Dy 2 o 3 Powder, Ho 2 o 3 Powder, Er 2 o 3 Powder, Tm 2 o 3 Powder, Lu 2 o 3 powder) and the raw materials of amorphous boron powder are placed in the ball mill tank, and ZrO 2 The balls are grinding beads, which are mixed on a ball tank mill at a speed of 120 rpm for 24 hours to obtain a uniform mixed powder; the mass ratio of raw materials to ball milling beads is 1:0.2.

[0030] (3) Place the powder obtained in step (2) in ...

Embodiment 2

[0034] The preparation composition is (Dy, Ho, Er, Tm, Lu) B 12 The high-entropy ceramics, Dy, Ho, Er, Tm, and Lu each account for 20% according to the molar mass percentage, and the balance is B and unavoidable impurities, and the impurity content is less than 0.05. The preparation of high-entropy ceramics proceeds as follows:

[0035] (1) Dosing is carried out according to the molar mass of the high-entropy ceramic, and the amorphous boron powder is added according to the theoretically calculated 110%.

[0036] (2) the rare earth oxide (Dy 2 o 3 Powder, Ho 2 o 3 Powder, Er 2 o 3 Powder, Tm 2 o 3 Powder, Lu 2 o 3 powder) and the raw materials of amorphous boron powder are placed in the ball mill tank, and ZrO 2 The balls are grinding beads, which are mixed on a ball tank mill at a speed of 120 rpm for 24 hours to obtain a uniform mixed powder; the mass ratio of raw materials to ball milling beads is 1:0.2.

[0037] (3) Place the powder obtained in step (2) in a grap...

Embodiment 3

[0041] The preparation composition is (Dy, Ho, Er, Tm, Lu) B 12 The high-entropy ceramics, according to the molar mass percentage a=30%, b=30%, c=20%, d=10% and e=10%, the balance is B and unavoidable impurities, and the impurity content is less than 0.05. The preparation of high-entropy ceramics proceeds as follows:

[0042] (1) Dosing is carried out according to the molar mass of the high-entropy ceramic, and the amorphous boron powder is added according to the theoretically calculated 110%.

[0043] (2) Rare earth oxides (Dy 2 o 3 Powder, Ho 2 o 3 Powder, Er 2 o 3 Powder, Tm 2 o 3 Powder, Lu 2 o 3 powder) and the raw materials of amorphous boron powder are placed in the ball mill tank, and ZrO 2 The balls are grinding beads, which are mixed on a ball tank mill at a speed of 120 rpm for 24 hours to obtain a uniform mixed powder; the mass ratio of raw materials to ball milling beads is 1:0.2.

[0044] (3) Place the powder obtained in step (2) in a graphite mold, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a kind of high-entropy ceramics with high hardness and high conductivity and its preparation method and application. The chemical formula of the high-entropy ceramics is (A a B b C c D. d E. e )B 12 . The dodecaboride high-entropy ceramic provided by the present invention has high hardness and high electrical conductivity at the same time, enriches the boride high-entropy ceramic material system, has the advantages of low cost, simple operation, wide application range, etc., and can withstand high stress and high Electrical conductivity has great application potential in the field of electrical equipment.

Description

technical field [0001] The invention belongs to the field of ceramic materials, in particular to a high-entropy ceramic with high hardness and high electrical conductivity, a preparation method and application thereof. Background technique [0002] The currently studied high-entropy ceramics mainly include high-entropy oxides, carbides, nitrides, and borides. Among them, high-entropy boride ceramics have broad development potential in the fields of ultra-high temperature, biomedicine, aerospace and energy due to their high hardness and melting point, good corrosion resistance, biocompatibility, and electrochemical performance. Has been successfully developed (V 0.2 Cr 0.2 Nb 0.2 Ta 0.2 W 0.2 ) B-boride high-entropy ceramics (Mingde Qin, et al.Scripta Materiala 189 (2020) 101-105), (Hf 0.2 Mo 0.2 Nb 0.2 Ta 0.2 Ti 0.2 )B 2 Diboride high-entropy ceramics (Giovanna Tallarita, et al. Scripta Materiala 189 (2020) 100-104), (Hf 0.2 Mo 0.2 Nb 0.2 Ta 0.2 Ti 0.2 )B 6 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/50C04B35/58
CPCC04B35/50C04B35/5805C04B2235/666C04B2235/6562C04B2235/6567C04B2235/96
Inventor 郑兴伟崔建梁拥成张国军刘吉轩韩志林蔡小芝杜小琪
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com