A new type of lithium battery fire extinguishing agent and preparation method thereof

A lithium battery and fire extinguishing agent technology, applied in fire protection equipment, chemical instruments and methods, other chemical processes, etc., can solve the problems of poor cooling rate, temperature reduction, weak oxygen isolation performance, etc.

Active Publication Date: 2022-01-28
江苏阜民新材料有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] CN 110368631A discloses a lithium-ion battery foam fire extinguishing agent and its preparation method. The traditional fluorocarbon surfactant is used as the foaming agent for aqueous film formation, which has certain environmental pollution problems. Dodecafluoro-2-formazol The principle of endothermic gasification of base-3-pentanone reduces the temperature, the cooling rate is poor, the performance of isolating oxygen is weak, and the problem of environmental pollution caused by harmful gases such as HF generated by battery combustion is not solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A new type of lithium battery fire extinguishing agent and preparation method thereof
  • A new type of lithium battery fire extinguishing agent and preparation method thereof
  • A new type of lithium battery fire extinguishing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A novel lithium battery fire extinguishing agent consists of the following raw materials in parts by weight:

[0058] 6 parts by weight of flame retardant, 12 parts by weight of adsorbent, 6 parts by weight of sodium bicarbonate, 20 parts by weight of foaming agent, 12 parts by weight of foam stabilizer, and 44 parts by weight of water.

[0059] The flame retardant is a mixture of (trimethylsilyl) phosphite and zinc borate in a mass ratio of 7:1.

[0060] The adsorbent is a mixture composed of aluminum hydroxide, activated carbon and denatured vermiculite in a mass ratio of 8:4:17.

[0061] The foaming agent is a mixture of cetyl sulfobetaine and 3-sulfopropyldodecyldimethylbetaine in a mass ratio of 5:3.

[0062] The foam stabilizer is a mixture of ethylene glycol, triethylene glycol monobutyl ether and tetraethylene glycol monobutyl ether in a mass ratio of 1:3:2.

[0063] The preparation method of described novel lithium battery fire extinguishing agent is made up ...

Embodiment 2

[0072] It is basically the same as Example 1, the difference is:

[0073] The preparation method of described denatured vermiculite is:

[0074]N1 uses a planetary ball mill to mill the vermiculite with a wet milling method to obtain vermiculite powder with a particle size of 1100 mesh; in the ball milling process, two sizes of zirconia balls with diameters of 0.9mm and 1.7mm are used Mix with a mass ratio of 1:2, the ball-to-material ratio is 17:1, the rotating speed of the planetary ball mill is 800r / min, the ball milling time is 18h, and the wet grinding aid is polyoxyethylene sorbitan monooleate, water A mixture composed of a mass ratio of 1:7, the mass ratio of the wet grinding aid to the vermiculite is 1.8:1; after the ball milling is completed, the precipitate A is filtered to obtain the precipitate A, and the precipitate A is washed with water and filtered again to obtain the precipitate B, and then Dry the precipitate B at 75°C to obtain the vermiculite powder; the m...

Embodiment 3

[0078] It is basically the same as Example 1, the difference is:

[0079] The preparation method of described denatured vermiculite is:

[0080] N1 uses a planetary ball mill to mill the vermiculite with a wet milling method to obtain vermiculite powder with a particle size of 1100 mesh; in the ball milling process, two sizes of zirconia balls with diameters of 0.9mm and 1.7mm are used Mix with a mass ratio of 1:2, the ball-to-material ratio is 17:1, the rotating speed of the planetary ball mill is 800r / min, the ball milling time is 18h, and the wet grinding aid is polyoxyethylene sorbitan monooleate, water A mixture composed of a mass ratio of 1:7, the mass ratio of the wet grinding aid to the vermiculite is 1.8:1; after the ball milling is completed, the precipitate A is filtered to obtain the precipitate A, and the precipitate A is washed with water and filtered again to obtain the precipitate B, and then Dry the precipitate B at 75°C to obtain the vermiculite powder; the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
diameteraaaaaaaaaa
wavelengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel lithium battery fire extinguishing agent and a preparation method, which is composed of a flame retardant, an adsorbent, sodium bicarbonate, a foaming agent, a foam stabilizer and water; the flame retardant is (trimethylsilyl ) a mixture of phosphite and zinc borate; the adsorbent is at least one of aluminum hydroxide, activated carbon, vermiculite and denatured vermiculite. The novel lithium battery fire extinguishing agent of the invention has the advantages of long-lasting foam, strong cooling ability, and the ability to effectively absorb harmful gases such as hydrogen fluoride.

Description

technical field [0001] The invention relates to the technical field of lithium battery fire extinguishing agent, in particular to a novel lithium battery fire extinguishing agent and a preparation method. Background technique [0002] As my country pays more and more attention to environmental protection issues and the substantial reduction in the production cost of lithium batteries, the use of lithium-ion batteries as a new energy source to replace traditional energy sources has become the first step towards a low-carbon economy in my country, and is widely used in transportation, energy storage fields etc. Although the large-scale application of lithium batteries has improved the environment and achieved beneficial effects such as low carbon, energy saving, and environmental protection, the accompanying safety issues cannot be ignored. [0003] Lithium-ion battery fires are quite different from ordinary fires. As an energy aggregate, after thermal runaway occurs, the fire...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A62D1/02A62D1/06B01J20/10B01J20/30
CPCA62D1/06B01J20/10
Inventor 易川栋
Owner 江苏阜民新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap