A glass wool and surface treatment technology, applied in the field of glass wool for construction and separators containing the glass wool, can solve the problems of limited doping amount and limited research and development of composite materials, so as to improve anti-aging and increase load capacity. , Improve the effect of aging resistance

Pending Publication Date: 2021-08-31
HUBEI JIA FU DA ENERGY SAVING TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the research and development of glass wool-nanocomposites, due to the current direct impregnation method, the amount of doping is limited, resulting in restrictions on the research and development of composite materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass wool for building and partition plate containing glass wool
  • Glass wool for building and partition plate containing glass wool
  • Glass wool for building and partition plate containing glass wool

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～ Embodiment 5

[0036] Embodiment 1~embodiment 5 provides a kind of glass wool surface treatment method, concrete operation is as follows:

[0037] Step S1: The ultra-fine glass wool raw material is impregnated with acid first, and then cleaned to obtain acid-impregnated glass wool. The acid used is 40%wt HF.

[0038] Step S2: Nano-TiO 2 Dispersed in ethanol solution, nano-TiO 2 Ultrasonic dispersion in ethanol solution to obtain 15%wt nano-TiO 2 Dispersions.

[0039] Step S3: impregnating acid-leached glass wool in nano-TiO 2 After drying in the dispersion, repeat the operation to obtain pretreated glass wool;

[0040] Step S4: impregnating the pretreated glass wool with 2%wt silane coupling agent solvent, and drying to obtain modified glass wool.

[0041] The specific reaction parameters of steps S1 to S4 are shown in Table 1.

[0042] Table 1 embodiment 1~embodiment 6 specific reaction conditions

[0043]

[0044]

Embodiment 7

[0046] The present embodiment provides a kind of glass wool surface treatment method, concrete operation is as follows:

[0047] Step S1: the ultrafine glass wool raw material is impregnated with acid first, and then cleaned to obtain acid-impregnated glass wool. The acid used is 40%wt HF, and the impregnation time is 10 minutes.

[0048] Step S2: Nano-TiO 2 Dispersed in ethanol solution, nano-TiO 2 Ultrasonic dispersion in ethanol solution to obtain 15%wt nano-TiO 2 Dispersions.

[0049] Step S3: impregnating acid-leached glass wool in nano-TiO 2 After the dispersion was dried for 20 minutes, pretreated glass wool was obtained;

[0050] Step S4: impregnating the pretreated glass wool with 2%wt silane coupling agent solvent for 40min, and drying to obtain the modified glass wool.

Embodiment 8～ Embodiment 14

[0052] This embodiment provides a noise reduction panel for buildings, including:

[0053] The surface-treated glass wool and ordinary glass wool are bonded with epoxy resin adhesive. Among them, the selected surface-modified glass wool types and the thickness of ordinary glass wool are shown in Table 2.

[0054] The surface modification glass wool type of table 2 embodiment 8~embodiment 14, the thickness ratio of surface modification glass wool and common glass wool

[0055]

[0056]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides glass wool for buildings and a partition plate containing the glass wool. The glass wool is prepared through the following steps: step S1, dipping a glass wool raw material with acid, and then conducting cleaning to obtain acid-leached glass wool; S2, dispersing nano-TiO2 in a solvent so as to obtain a nano-TiO2 dispersion liquid; S3, dipping the acid-leached glass wool in the nano-TiO2 dispersion liquid, and conducting drying to obtain pretreated glass wool; and S4, impregnating the pretreated glass wool with a silane coupling agent solvent, and conducting drying to obtain the modified glass wool. Compared with the prior art, the invention has the beneficial effects that the glass wool is subjected to acid corrosion to increase the hydrophilicity of the glass wool; then the glass wool is soaked in the titanium dioxide dispersion liquid, so the loading capacity of titanium dioxide is increased, and the ageing resistance of the superfine glass wool is improved; and after the nano-TiO2 is deposited, the silane coupling agent is finally used for sealing layer modification, so moisture resistance is prevented from being reduced after the glass wool is corroded in an early stage.

Description

technical field [0001] The invention belongs to the field of glass wool preparation, and in particular relates to glass wool for construction and a separator containing the glass wool. Background technique [0002] Glass wool is a commonly used sound insulation and thermal insulation material in the construction field, and the improvement of its anti-aging property is an important improvement direction. Nano-titanium dioxide is widely used to improve the anti-aging properties of materials due to its photocatalytic properties. [0003] However, in the research and development of glass wool-nanocomposites, due to the current direct impregnation method, the amount of doping is limited, resulting in restrictions on the research and development of composite materials. Contents of the invention [0004] In order to solve the above-mentioned technical solution, the present invention provides glass wool for construction and a separator containing the glass wool. [0005] The spe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B20/10C04B20/02C04B14/42
CPCC04B20/1066C04B20/1018C04B20/023C04B14/42
Inventor 杨辉张洋
Owner HUBEI JIA FU DA ENERGY SAVING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap