Low temperature resistant polymer cement waterproof coating and preparation method thereof

A waterproof coating and polymer technology, applied in the direction of coating, etc., can solve the problems of poor low temperature resistance and poor use stability of the cured coating film, achieve good low temperature storage stability, improve low temperature use stability, and hydroxyl content high effect

Active Publication Date: 2022-03-25
冠翔新材料科技集团股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems of poor low-temperature storage and use stability of polymer cement waterproof coatings and poor low-temperature resistance of cured coating films, the application provides a low-temperature resistant polymer cement waterproof coating and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low temperature resistant polymer cement waterproof coating and preparation method thereof
  • Low temperature resistant polymer cement waterproof coating and preparation method thereof
  • Low temperature resistant polymer cement waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example

[0044] A modified polyacrylate emulsion is prepared according to the following preparation method:

[0045]S1. Weigh 0.2kg of emulsifier OP-10 and dissolve it in 9.8kg of deionized water, stir and mix at a speed of 600rpm, and prepare an emulsion;

[0046] Weigh 3.3kg hydroxyethyl methacrylate, 3.3kg methacrylate, 1.1kg methacrylic acid and 1.1kg3-glycidyloxypropyltrimethoxysilane;

[0047] Take 0.3kg of hydroxyethyl methacrylate, 0.3kg of methacrylate, 0.1kg of methacrylic acid and 0.1kg of 3-glycidyloxypropyltrimethoxysilane into the emulsion, stir and mix at a speed of 600rpm Carry out emulsification to obtain a pre-emulsion; add 0.1kg of potassium persulfate solution with a concentration of 0.01wt% to the pre-emulsion, stir at a speed of 600rpm and heat up to 75°C, then keep warm for 0.3h to obtain a seed emulsion;

[0048] S2. Raise the temperature of the seed emulsion to 80°C, then put the remaining hydroxyethyl methacrylate, methacrylate, methacrylic acid and 3-glycidy...

preparation example 2-10

[0050] A modified polyacrylate emulsion, the difference from Preparation Example 1 is that hydroxyethyl methacrylate, methacrylate, methacrylic acid, 3-glycidyloxypropyltrimethoxysilane and emulsifier The dosing amount is different, and the specific dosing amount is shown in Table 2 below.

[0051] Table 2. The dosage of each component of the modified polyacrylate emulsion in each step

[0052]

[0053]

preparation example 11

[0055] A modified polyacrylate emulsion, the difference from Preparation Example 9 is that 1,3-diglycidyl etheroxypropyl-1,1,3,3 tetramethyldisiloxane is used to replace 3 - glycidyloxypropyltrimethoxysilane.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-temperature-resistant polymer cement waterproof coating, which includes a liquid material and a powder material, and the liquid material and the powder material are compounded according to a weight ratio (0.8-1.5): 1; the liquid material includes the following Components by weight: 70-90 parts of modified polyacrylate emulsion, 0-5 parts of water, 3-6 parts of triethanolamine, 1-5 parts of defoamer; the powder includes the following components by weight : 40-60 parts of cement, 10-15 parts of quartz powder, 10-15 parts of heavy calcium powder, 1-5 parts of diisocyanate; the modified polyacrylate emulsion is composed of acrylate monomers containing hydroxyl groups, epoxy group-containing The siloxane and methacrylic acid were prepared by using seeded emulsion polymerization. The polymer cement waterproof coating prepared by the present application has good stability in low-temperature storage and use, and at the same time, the coating film formed after curing has good low-temperature resistance.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a low-temperature-resistant polymer cement waterproof coating and a preparation method thereof. Background technique [0002] Polymer cement waterproof coating, also known as JS waterproof coating, is a two-component waterproof coating compounded by a reasonable ratio of liquid and powder. Among them, the liquid material generally chooses polymer emulsion such as polypropionate emulsion or ethylene-vinyl acetate copolymer emulsion, and the powder material generally uses cement as the main component. Polymer cement waterproof coating has the characteristics of high elasticity of synthetic polymer materials and good durability of inorganic materials. [0003] The polymer cement waterproof coating is constructed after mixing and mixing on site. It solidifies into a film through the mechanism of cement hydration or water volatilization. Therefore, the liquid material contains a lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/14C09D7/63C09D7/61
CPCC09D133/14C09D7/63C09D7/61C08K2003/265C08K5/29C08K5/17C08K3/36C08K3/26
Inventor 景肖波
Owner 冠翔新材料科技集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap